目的研究TC4合金在等离子-MIG复合焊(Plasma–MIG Hybrid Welding)过程中的温度场特性,探究不同电弧功率对熔池形貌的影响。方法进行了2组4 mm TC4合金板堆焊试验,根据实验结果提出了一种改进的复合热源模型并进行了相应的仿真分析。结...目的研究TC4合金在等离子-MIG复合焊(Plasma–MIG Hybrid Welding)过程中的温度场特性,探究不同电弧功率对熔池形貌的影响。方法进行了2组4 mm TC4合金板堆焊试验,根据实验结果提出了一种改进的复合热源模型并进行了相应的仿真分析。结果仿真与实验获得的焊缝截面相吻合;等离子电流的增大使熔池尺寸增大且余高减小,等离子电弧功率的变化对熔池宽度的影响相对较小。结论等离子–MIG复合电弧对工件的热作用非常集中,更易实现深熔焊、焊接效率更高;所提出的热源模型适用于TC4合金等离子–MIG复合焊温度场模拟。展开更多
The plasma-MIG welding torch was developed.5A06 aluminum alloys with V-grooves were welded in a single pass in the plasma-MIG welding process and the joints were examined by X-ray diffractometry analysis and mechanica...The plasma-MIG welding torch was developed.5A06 aluminum alloys with V-grooves were welded in a single pass in the plasma-MIG welding process and the joints were examined by X-ray diffractometry analysis and mechanical tests.The orthogonal experimental design was used to study the influence of plasma-MIG welding parameters on the aluminum weld porosity.The mixed orthogonal matrix L16(4 4×2 3) and analysis of variance (ANOVA)technique were employed to optimize the welding parameters.The experimental results indicate that the effect of plasma gas flow rate is dominant,the secondary factors are MIG welding voltage,welding speed,wire feed rate and plasma current in turn.Confirmation experiments were conducted under optimum conditions and there was almost no porosity in the welded joints,thus good mechanical performance joints were obtained.展开更多
文摘目的研究TC4合金在等离子-MIG复合焊(Plasma–MIG Hybrid Welding)过程中的温度场特性,探究不同电弧功率对熔池形貌的影响。方法进行了2组4 mm TC4合金板堆焊试验,根据实验结果提出了一种改进的复合热源模型并进行了相应的仿真分析。结果仿真与实验获得的焊缝截面相吻合;等离子电流的增大使熔池尺寸增大且余高减小,等离子电弧功率的变化对熔池宽度的影响相对较小。结论等离子–MIG复合电弧对工件的热作用非常集中,更易实现深熔焊、焊接效率更高;所提出的热源模型适用于TC4合金等离子–MIG复合焊温度场模拟。
文摘The plasma-MIG welding torch was developed.5A06 aluminum alloys with V-grooves were welded in a single pass in the plasma-MIG welding process and the joints were examined by X-ray diffractometry analysis and mechanical tests.The orthogonal experimental design was used to study the influence of plasma-MIG welding parameters on the aluminum weld porosity.The mixed orthogonal matrix L16(4 4×2 3) and analysis of variance (ANOVA)technique were employed to optimize the welding parameters.The experimental results indicate that the effect of plasma gas flow rate is dominant,the secondary factors are MIG welding voltage,welding speed,wire feed rate and plasma current in turn.Confirmation experiments were conducted under optimum conditions and there was almost no porosity in the welded joints,thus good mechanical performance joints were obtained.