Vertically orientated TiO2 nanotube array with diameters ranging from 60 up to 80 nm and length of 4 μm was grown on titanium by anodization.Crack initiation,propagation and saturation were studied using the substrat...Vertically orientated TiO2 nanotube array with diameters ranging from 60 up to 80 nm and length of 4 μm was grown on titanium by anodization.Crack initiation,propagation and saturation were studied using the substrate straining test.The results show that annealing obviously modifies the interfaces.With the increase of tensile strain,cracks in TiO2 nanotube films propagate rapidly and reach the saturation within a narrow strain gap.Interfacial shear strengths of TiO2 nanotube films without annealing,with 250 ℃ annealing and with 400 ℃ annealing can be estimated as 163.3,370.2 and 684.5 MPa,respectively.The critical energy release rates of TiO2 nanotube films are calculated as 49.6,102.6 and 392.7 J/m2,respectively.The fracture toughnesses of TiO2 nanotube films are estimated as 0.996,1.433 and 2.803 MPa-m1/2,respectively.The interfacial bonding mechanism of TiO2 nanotube film is chemical bonding.展开更多
Curvature method was used to measure the residual stress and substrate straining tensile test was carried out to study the debonding behavior of TiO2 nanotube film. The results indicate that the internal residual stre...Curvature method was used to measure the residual stress and substrate straining tensile test was carried out to study the debonding behavior of TiO2 nanotube film. The results indicate that the internal residual stress is -54 MPa. The strains of debonding initiation of TiO2 nanotube films without annealing, with 250 °C annealing and with 400 °C annealing are 2.6%, 5.1% and 8.6%, respectively, and the average radii of the debonding patches with debonding initiation are 27.5, 17.1 and 19.4 μm, respectively. The true critical debonding stresses of TiO2 nanotube films without annealing, with 250 °C annealing and with 400 °C annealing can be estimated as 220.4, 394.5 and 627.9 MPa, respectively. Interfacial shear lag model is modified and polynomial fitting equation of the interfacial shear strength of TiO2 nanotube film is demonstrated under debonding conditions. The modification and polynomial fitting are reliable since good agreement of the interfacial shear strengths after fitting is obtained compared with those results from the crack density analysis.展开更多
基金Project(50604017) supported by the National Natural Science Foundation of ChinaProject(20110946Z) supported by the State Key Laboratory of Powder Metallurgy,China
文摘Vertically orientated TiO2 nanotube array with diameters ranging from 60 up to 80 nm and length of 4 μm was grown on titanium by anodization.Crack initiation,propagation and saturation were studied using the substrate straining test.The results show that annealing obviously modifies the interfaces.With the increase of tensile strain,cracks in TiO2 nanotube films propagate rapidly and reach the saturation within a narrow strain gap.Interfacial shear strengths of TiO2 nanotube films without annealing,with 250 ℃ annealing and with 400 ℃ annealing can be estimated as 163.3,370.2 and 684.5 MPa,respectively.The critical energy release rates of TiO2 nanotube films are calculated as 49.6,102.6 and 392.7 J/m2,respectively.The fracture toughnesses of TiO2 nanotube films are estimated as 0.996,1.433 and 2.803 MPa-m1/2,respectively.The interfacial bonding mechanism of TiO2 nanotube film is chemical bonding.
基金Project (51274248) supported by the National Natural Science Foundation of ChinaProject (20110946Z) supported by the State Key Laboratory of Powder Metallurgy, China
文摘Curvature method was used to measure the residual stress and substrate straining tensile test was carried out to study the debonding behavior of TiO2 nanotube film. The results indicate that the internal residual stress is -54 MPa. The strains of debonding initiation of TiO2 nanotube films without annealing, with 250 °C annealing and with 400 °C annealing are 2.6%, 5.1% and 8.6%, respectively, and the average radii of the debonding patches with debonding initiation are 27.5, 17.1 and 19.4 μm, respectively. The true critical debonding stresses of TiO2 nanotube films without annealing, with 250 °C annealing and with 400 °C annealing can be estimated as 220.4, 394.5 and 627.9 MPa, respectively. Interfacial shear lag model is modified and polynomial fitting equation of the interfacial shear strength of TiO2 nanotube film is demonstrated under debonding conditions. The modification and polynomial fitting are reliable since good agreement of the interfacial shear strengths after fitting is obtained compared with those results from the crack density analysis.