Face centred cubic（FCC） TiB ceramic powder synthesized by Ti-boronizing method was used as conductive filler to make ceramic electrically conductive adhesives（ECAs） with the polymer matrix.Electrically conductive ...Face centred cubic（FCC） TiB ceramic powder synthesized by Ti-boronizing method was used as conductive filler to make ceramic electrically conductive adhesives（ECAs） with the polymer matrix.Electrically conductive properties of the ceramic ECAs were studied.The bulk electrical resistivity varied with the powder content of the FCC-TiB in ECAs.The FCC-TiB filled ECAs also showed the percolation behavior that usually occurred for the metal-filled ECAs,the percolation threshold was located at the content of 60%FCC-TiB.A minimum value of 0.1 Ω·cm was obtained at a content of 75%FCC-TiB.In order to check the reliability of mechanical property,tensile test was done to measure the shear strength,and the shear strength dropped with increasing the content of FCC-TiB powders.It is about 12.26 MPa at the content of 70%TiB powders.The Cu filled ECAs were also prepared for comparison.The properties of the oxidation resistance of the two ECAs were evaluated.The results show that the ceramic ECAs have excellent oxidation resistance and better stability compared with the Cu filled ECAs.展开更多
基金Project (51172088) supported by the National Natural Science Foundation of China
文摘Face centred cubic（FCC） TiB ceramic powder synthesized by Ti-boronizing method was used as conductive filler to make ceramic electrically conductive adhesives（ECAs） with the polymer matrix.Electrically conductive properties of the ceramic ECAs were studied.The bulk electrical resistivity varied with the powder content of the FCC-TiB in ECAs.The FCC-TiB filled ECAs also showed the percolation behavior that usually occurred for the metal-filled ECAs,the percolation threshold was located at the content of 60%FCC-TiB.A minimum value of 0.1 Ω·cm was obtained at a content of 75%FCC-TiB.In order to check the reliability of mechanical property,tensile test was done to measure the shear strength,and the shear strength dropped with increasing the content of FCC-TiB powders.It is about 12.26 MPa at the content of 70%TiB powders.The Cu filled ECAs were also prepared for comparison.The properties of the oxidation resistance of the two ECAs were evaluated.The results show that the ceramic ECAs have excellent oxidation resistance and better stability compared with the Cu filled ECAs.