The green and sintered densities,and tensile strength of sintered P/M steels produced by cold compaction,warm compaction,warm compaction combined with die wall lubrication(DWL)were measured under various compaction pr...The green and sintered densities,and tensile strength of sintered P/M steels produced by cold compaction,warm compaction,warm compaction combined with die wall lubrication(DWL)were measured under various compaction pressures using polytetrafluoroethylene(PTFE)emulsion as the die wall lubricant.The effects of warm compaction on the mechanical properties were studied.The tensile fracture behaviors of cold compaction and warm compaction were studied using scanning electron microscope(SEM).The results show that the density of sintered P/M steel prepared by warm compaction or warm compaction with DWL is higher than that by cold compaction under all compaction pressures.Meanwhile,the highest tensile strength is obtained by combination of warm compaction and die wall lubrication under all compaction pressures.The SEM results show that the fracture modes of the sintered samples prepared by cold compaction and warm compaction at 700 MPa are the mixed mode of ductile fracture and brittle fracture,and obvious dimples can be found in some regions.The fracture of sample prepared by cold compaction is uneven and has irregular and big pores,but that by warm compaction is relatively even and the pores are round mostly,and the samples have many obvious dimples on the whole fracture surface.展开更多
The phenomena of die wall lubricated warm compaction of non-lubricant admixed iron powders were researched, and its mechanism of densification was discussed. Water atomized powder obtained from the Wuhan Iron and Stee...The phenomena of die wall lubricated warm compaction of non-lubricant admixed iron powders were researched, and its mechanism of densification was discussed. Water atomized powder obtained from the Wuhan Iron and Steel Corporation was used. With compacting and sintering, compared with cold compaction, the density of warm compacted samples increases by 0.07 - 0. 22 g/cm^3 at the same pressed pressure. The maximum achievable green density of warm compacted samples is 7.12 g/cm^3 at 120℃, and the maximum sintered density is 7.18 g/cm^3 at 80℃. Compared with cold compaction, the ejection force of warm compaction is smaller; the maximum discrep- ancy is about 7 kN. The warm compacted mechanism of densification of iron powders can be obtained： heating the powder contributes to improving plastic deformation of powder particles, and accelerating the mutual filling and rearrangement of powder particles.展开更多
FVS1212/FVS0812 material was prepared by adding FVS1212 powder into FVS0812 powder. The structure and mechanical properties of materials were studied by means of X-Ray, tensile measurement, OM and SEM. The results sho...FVS1212/FVS0812 material was prepared by adding FVS1212 powder into FVS0812 powder. The structure and mechanical properties of materials were studied by means of X-Ray, tensile measurement, OM and SEM. The results show that adding proper content FVS1212 powders can improve the tensile strength of FVS0812 aluminum at room temperature and elevated temperature, and that the elongation of FVS1212/FVS0812 material is better than that of FVS1212 aluminum.展开更多
基金Project (MKPT-2004-09ZD) supported by the National Key Technological Research and Development Program of ChinaProject (040117) supported by the Innovative Engineering Program of Central South University
文摘The green and sintered densities,and tensile strength of sintered P/M steels produced by cold compaction,warm compaction,warm compaction combined with die wall lubrication(DWL)were measured under various compaction pressures using polytetrafluoroethylene(PTFE)emulsion as the die wall lubricant.The effects of warm compaction on the mechanical properties were studied.The tensile fracture behaviors of cold compaction and warm compaction were studied using scanning electron microscope(SEM).The results show that the density of sintered P/M steel prepared by warm compaction or warm compaction with DWL is higher than that by cold compaction under all compaction pressures.Meanwhile,the highest tensile strength is obtained by combination of warm compaction and die wall lubrication under all compaction pressures.The SEM results show that the fracture modes of the sintered samples prepared by cold compaction and warm compaction at 700 MPa are the mixed mode of ductile fracture and brittle fracture,and obvious dimples can be found in some regions.The fracture of sample prepared by cold compaction is uneven and has irregular and big pores,but that by warm compaction is relatively even and the pores are round mostly,and the samples have many obvious dimples on the whole fracture surface.
文摘The phenomena of die wall lubricated warm compaction of non-lubricant admixed iron powders were researched, and its mechanism of densification was discussed. Water atomized powder obtained from the Wuhan Iron and Steel Corporation was used. With compacting and sintering, compared with cold compaction, the density of warm compacted samples increases by 0.07 - 0. 22 g/cm^3 at the same pressed pressure. The maximum achievable green density of warm compacted samples is 7.12 g/cm^3 at 120℃, and the maximum sintered density is 7.18 g/cm^3 at 80℃. Compared with cold compaction, the ejection force of warm compaction is smaller; the maximum discrep- ancy is about 7 kN. The warm compacted mechanism of densification of iron powders can be obtained： heating the powder contributes to improving plastic deformation of powder particles, and accelerating the mutual filling and rearrangement of powder particles.
文摘FVS1212/FVS0812 material was prepared by adding FVS1212 powder into FVS0812 powder. The structure and mechanical properties of materials were studied by means of X-Ray, tensile measurement, OM and SEM. The results show that adding proper content FVS1212 powders can improve the tensile strength of FVS0812 aluminum at room temperature and elevated temperature, and that the elongation of FVS1212/FVS0812 material is better than that of FVS1212 aluminum.