Kinetics of SiO2 leaching from Al2O3 extracted slag of fly ash with sodium hydroxide solution was studied.The effect of leaching temperature,mass ratio of NaOH to SiO2 and stirring speed on SiO2 leaching rate was inve...Kinetics of SiO2 leaching from Al2O3 extracted slag of fly ash with sodium hydroxide solution was studied.The effect of leaching temperature,mass ratio of NaOH to SiO2 and stirring speed on SiO2 leaching rate was investigated.The results show that increasing leaching temperature,mass ratio of NaOH to SiO2 and stirring speed increases SiO2 leaching rate.The SiO2 leaching rate is 95.66%under the optimized conditions.There are two stages for the SiO2 leaching process,and the leaching reaction is very rapid in the first stage but quite slow in the second stage.The whole leaching process follows the shrinking core model,and the outer diffusion of no product layer is the rate-controlling step.The activation energies of the first and second stages are calculated to be8.492 kJ/mol and 8.668 kJ/mol,respectively.The kinetic equations of the first and the second stages were obtained,respectively.展开更多
In order to examine the leaching rate of potassium chloride from the sintering dust by water,surface morphology and inner structure of the dust,especially the existing state of potassium chloride,were observed by scan...In order to examine the leaching rate of potassium chloride from the sintering dust by water,surface morphology and inner structure of the dust,especially the existing state of potassium chloride,were observed by scanning electron microscopy（SEM） and linear scanning technique via energy dispersive spectroscopy（EDS）.The characterization shows that the sintering dusts are mostly porous composites or agglomerates of the fine dust particles with size less than 10 μm,and the potassium chloride and sodium chloride particles are partly covered by other water insoluble matters in the dust which consist of elements iron,calcium and etc.Exposure of potassium chloride in the agglomerated dust matrix of this kind suggests that the leaching can be simply perceived as the dissolution of water soluble matters in the dust.On-line monitor of specific electrical conductivity of the leaching system verifies the prediction that leaching kinetics of potassium chloride from the sintering dust fits dissolution model well.Leaching equilibrium can be reached within 5 min with potassium leaching ratio more than 95%.展开更多
基金Project (2007CB613603) supported by the National Basic Research Program of ChinaProject (2013M530934) supported by the Postdoctoral Science Foundation of China
文摘Kinetics of SiO2 leaching from Al2O3 extracted slag of fly ash with sodium hydroxide solution was studied.The effect of leaching temperature,mass ratio of NaOH to SiO2 and stirring speed on SiO2 leaching rate was investigated.The results show that increasing leaching temperature,mass ratio of NaOH to SiO2 and stirring speed increases SiO2 leaching rate.The SiO2 leaching rate is 95.66%under the optimized conditions.There are two stages for the SiO2 leaching process,and the leaching reaction is very rapid in the first stage but quite slow in the second stage.The whole leaching process follows the shrinking core model,and the outer diffusion of no product layer is the rate-controlling step.The activation energies of the first and second stages are calculated to be8.492 kJ/mol and 8.668 kJ/mol,respectively.The kinetic equations of the first and the second stages were obtained,respectively.
基金Project (50974018) supported by the National Natural Science Foundation of China Project (108007) supported by the ScienceFoundation of Ministry of Education of China
文摘In order to examine the leaching rate of potassium chloride from the sintering dust by water,surface morphology and inner structure of the dust,especially the existing state of potassium chloride,were observed by scanning electron microscopy（SEM） and linear scanning technique via energy dispersive spectroscopy（EDS）.The characterization shows that the sintering dusts are mostly porous composites or agglomerates of the fine dust particles with size less than 10 μm,and the potassium chloride and sodium chloride particles are partly covered by other water insoluble matters in the dust which consist of elements iron,calcium and etc.Exposure of potassium chloride in the agglomerated dust matrix of this kind suggests that the leaching can be simply perceived as the dissolution of water soluble matters in the dust.On-line monitor of specific electrical conductivity of the leaching system verifies the prediction that leaching kinetics of potassium chloride from the sintering dust fits dissolution model well.Leaching equilibrium can be reached within 5 min with potassium leaching ratio more than 95%.