Zirconia-mullite-corundum composites were successfully prepared from fly ash,zircon and alumina powder by a reaction sintering process.The phase and microstructure evolutions of the composite synthesized at desired te...Zirconia-mullite-corundum composites were successfully prepared from fly ash,zircon and alumina powder by a reaction sintering process.The phase and microstructure evolutions of the composite synthesized at desired temperatures of 1 400,1 500 and 1 600°C for 4 h were characterized by X-ray diffractometry and scanning electronic microscopy,respectively.The influences of sintering temperature on shrinkage ratio,apparent porosity and bulk density of the synthesized composite were investigated.The formation process of the composites was discussed in detail.The results show that the zirconia-mullite-corundum composites with good sintering properties can be prepared at 1 600°C for 4 h.Zirconia particles can be homogeneously distributed in mullite matrix,and the zirconia particles are around 5μm.The formation process of zirconia-mullite-corundum composites consists of decomposition of zircon and mullitization process.展开更多
Porous ceramics was made from coal fly ash, and the microstructure and other properties were characterized as a function of the amount of the pore-forming agent and firing temperature. The results indicated that the p...Porous ceramics was made from coal fly ash, and the microstructure and other properties were characterized as a function of the amount of the pore-forming agent and firing temperature. The results indicated that the proper sintering temperature for the useful ceramic materials is 1 250℃, and a liquid-phase was involved in the densification process.展开更多
Novel AZ91D Mg alloy/fly-ash cenospheres(AZ91D/FACs)composites were fabricated by melt stir technique.Fly-ash cenosphere particles with 4%,6%,8%,10%in mass fraction and 100μm in size were used.Hardness and compressiv...Novel AZ91D Mg alloy/fly-ash cenospheres(AZ91D/FACs)composites were fabricated by melt stir technique.Fly-ash cenosphere particles with 4%,6%,8%,10%in mass fraction and 100μm in size were used.Hardness and compressive strength of the composites were measured.The effects of mass fraction of cenospheres on the microstructure and compressive properties were characterized.The results show that the cenospheres are uniformly distributed in the matrix and there is no sign of cenosphere cluster or residual pore.The densities of the composites are 1.85-1.92 g/cm 3 .By comparing with matrix,the compressive yield strength of the composites is improved,and the cenospheres is filled with Mg matrix alloy.SEM,XRD and EDX results of the composites show clear evidence of reaction product at cenosphere/matrix interface.On the basis of XRD and EDX,composition, structure and thermodynamic analysis,the main interfacial phase between the cenosphere and AZ91D Mg alloy was identified to be MgAl2O4.展开更多
基金Project(N100302002)supported by the Fundamental Research Funds for the Central Universities,ChinaProject(20100471467)supported by the China Postdoctoral Science Foundation
文摘Zirconia-mullite-corundum composites were successfully prepared from fly ash,zircon and alumina powder by a reaction sintering process.The phase and microstructure evolutions of the composite synthesized at desired temperatures of 1 400,1 500 and 1 600°C for 4 h were characterized by X-ray diffractometry and scanning electronic microscopy,respectively.The influences of sintering temperature on shrinkage ratio,apparent porosity and bulk density of the synthesized composite were investigated.The formation process of the composites was discussed in detail.The results show that the zirconia-mullite-corundum composites with good sintering properties can be prepared at 1 600°C for 4 h.Zirconia particles can be homogeneously distributed in mullite matrix,and the zirconia particles are around 5μm.The formation process of zirconia-mullite-corundum composites consists of decomposition of zircon and mullitization process.
文摘Porous ceramics was made from coal fly ash, and the microstructure and other properties were characterized as a function of the amount of the pore-forming agent and firing temperature. The results indicated that the proper sintering temperature for the useful ceramic materials is 1 250℃, and a liquid-phase was involved in the densification process.
基金Project(2007KZ07)supported by Plans for Science and Technology of Changchun City,ChinaProject supported by the Program for New Century Excellent Talents in University,ChinaProject supported by the 985 Project of Jilin University,China
文摘Novel AZ91D Mg alloy/fly-ash cenospheres(AZ91D/FACs)composites were fabricated by melt stir technique.Fly-ash cenosphere particles with 4%,6%,8%,10%in mass fraction and 100μm in size were used.Hardness and compressive strength of the composites were measured.The effects of mass fraction of cenospheres on the microstructure and compressive properties were characterized.The results show that the cenospheres are uniformly distributed in the matrix and there is no sign of cenosphere cluster or residual pore.The densities of the composites are 1.85-1.92 g/cm 3 .By comparing with matrix,the compressive yield strength of the composites is improved,and the cenospheres is filled with Mg matrix alloy.SEM,XRD and EDX results of the composites show clear evidence of reaction product at cenosphere/matrix interface.On the basis of XRD and EDX,composition, structure and thermodynamic analysis,the main interfacial phase between the cenosphere and AZ91D Mg alloy was identified to be MgAl2O4.