To improve the environmental benefits and solve the problems of large shrinkage and high brittleness, the partial replacement of calcined kaolin by fly ash as a raw material for geopolymer synthesis and the influences...To improve the environmental benefits and solve the problems of large shrinkage and high brittleness, the partial replacement of calcined kaolin by fly ash as a raw material for geopolymer synthesis and the influences of polypropylene (PP) fiber on the mechanical properties and volume stability were investigated. The results show that compressive strength of the geopolymer containing 33.3%(mass fraction) fly ash by steam curing at 80 ℃ for 6 d is improved by 35.5%. The 3-day compressive strength, flexural strength and impacting energy of geopolymers containing 0.05%PP fiber increase by 67.8%, 36.1% and 6.25%, while the shrinkage and modulus of compressibility decrease by 38.6% and 31.3%, respectively. The results of scanning electron microscopy (SEM) and the appearances of crack growths confirm that PP fiber can offer a bridging effect over the harmful pores and defects and change the expanding ways of cracks, resulting in a great improvement of strength and toughness.展开更多
Fly ash is a fine and dispersed powder discharged from power station after the coal being burned. With the deepening of people’s recognition about the pollution problem of fly ash, the ways of utilizing fly ash are g...Fly ash is a fine and dispersed powder discharged from power station after the coal being burned. With the deepening of people’s recognition about the pollution problem of fly ash, the ways of utilizing fly ash are gradually increasing. Utilizing value of fly ash is closely related to the unburned carbon content.On the basis of analysis of modern testing method,a fundamental thinking is theoretically posed for decreasing unburned carbon content from fly ash by a dry removing carbon technology. The triboelectric separation method shown that the above mentioned thinking of dry removing carbon from fly ash is practical.展开更多
Physical-chemical properties of phosphorous gypsum, proportion and cemented mechanism of slurry with gypsum as aggregate were studied to remove the harms of gypsum pile, combining with difficult problems of excessive ...Physical-chemical properties of phosphorous gypsum, proportion and cemented mechanism of slurry with gypsum as aggregate were studied to remove the harms of gypsum pile, combining with difficult problems of excessive mined-out gobs, enormous ore body under roadway and low recovery ratio of Yongshaba Mine, Kaiyang Phosphor Mine Group, Guizhou Province, China. An appropriate backfill system and craflwork were designed, using shattering milling method to crush gypsum, double-axles mixing and strong activation mixing way to mix slurry, cemented slurry and mullock backfill alternately process. The results show that gypsum is fit for backfilling afterwards by adding fly ash, though it is not an ideal aggregate for fine granule and coagulate retardation. The suggested dosage （the mass ratio of cement to fly ash to gypsum） is 1：1：6-1：1：8 with mass fraction of solid materials 60%-63%. Slurry is transported in suspend state with non-plastic strength, and then in concretion state after backfilling. The application to mine shows the technology is feasible, and gypsum utilization ratio is up to 100%. Transportation and backfill effect is very good for paste-like slurry and drenching cemented slurry into mullock, and the compressive strength and recovery ratio are 2.0 MPa and 82.6%, respectively, with the maximum subsidence of surface only 1.307 mm. Furthermore, the investment of system is about 7 × 10^6 yuan （RMB）, only 1/10 of that of traditional paste backfill system.展开更多
基金Project(2006AA06Z225) supported by the National High-Tech Research and Development Program of China
文摘To improve the environmental benefits and solve the problems of large shrinkage and high brittleness, the partial replacement of calcined kaolin by fly ash as a raw material for geopolymer synthesis and the influences of polypropylene (PP) fiber on the mechanical properties and volume stability were investigated. The results show that compressive strength of the geopolymer containing 33.3%(mass fraction) fly ash by steam curing at 80 ℃ for 6 d is improved by 35.5%. The 3-day compressive strength, flexural strength and impacting energy of geopolymers containing 0.05%PP fiber increase by 67.8%, 36.1% and 6.25%, while the shrinkage and modulus of compressibility decrease by 38.6% and 31.3%, respectively. The results of scanning electron microscopy (SEM) and the appearances of crack growths confirm that PP fiber can offer a bridging effect over the harmful pores and defects and change the expanding ways of cracks, resulting in a great improvement of strength and toughness.
文摘Fly ash is a fine and dispersed powder discharged from power station after the coal being burned. With the deepening of people’s recognition about the pollution problem of fly ash, the ways of utilizing fly ash are gradually increasing. Utilizing value of fly ash is closely related to the unburned carbon content.On the basis of analysis of modern testing method,a fundamental thinking is theoretically posed for decreasing unburned carbon content from fly ash by a dry removing carbon technology. The triboelectric separation method shown that the above mentioned thinking of dry removing carbon from fly ash is practical.
基金Project(2006BAB02A03)supported by the National Key Technology Research and Development ProgramProject(08MX16)supported by Mittal Scientific and Technological Innovation Projects of Central South University during 2008
文摘Physical-chemical properties of phosphorous gypsum, proportion and cemented mechanism of slurry with gypsum as aggregate were studied to remove the harms of gypsum pile, combining with difficult problems of excessive mined-out gobs, enormous ore body under roadway and low recovery ratio of Yongshaba Mine, Kaiyang Phosphor Mine Group, Guizhou Province, China. An appropriate backfill system and craflwork were designed, using shattering milling method to crush gypsum, double-axles mixing and strong activation mixing way to mix slurry, cemented slurry and mullock backfill alternately process. The results show that gypsum is fit for backfilling afterwards by adding fly ash, though it is not an ideal aggregate for fine granule and coagulate retardation. The suggested dosage （the mass ratio of cement to fly ash to gypsum） is 1：1：6-1：1：8 with mass fraction of solid materials 60%-63%. Slurry is transported in suspend state with non-plastic strength, and then in concretion state after backfilling. The application to mine shows the technology is feasible, and gypsum utilization ratio is up to 100%. Transportation and backfill effect is very good for paste-like slurry and drenching cemented slurry into mullock, and the compressive strength and recovery ratio are 2.0 MPa and 82.6%, respectively, with the maximum subsidence of surface only 1.307 mm. Furthermore, the investment of system is about 7 × 10^6 yuan （RMB）, only 1/10 of that of traditional paste backfill system.