In order to improve the bonding strength between piston alloys and cast iron ring of aluminum piston with reinforced cast iron ring,the different methods of the surface treatments(shot blasting and sand blasting) to t...In order to improve the bonding strength between piston alloys and cast iron ring of aluminum piston with reinforced cast iron ring,the different methods of the surface treatments(shot blasting and sand blasting) to the cast iron ring are experimented.The optical micrograph shows that an intermetallic layer and a ligulate shaped structure are formed between piston alloys and cast iron base ring.After sand blasting treatment,the ring surface is non-metal shiny,matte-like and has no obvious pits.The intermetallic layer thickness formed between piston alloys and cast iron is thinner and more equally distributed after sand blasting to the ring.The content of the graphite distributed the interfacial zone after the shot blasting treatment is little.With the increase of time by sand blasting,the hardness starts to slightly descend.The bonding strength of the sample by sand blasting is obviously higher than that by shot blasting and increases from 9.32 MPa to 19.53 MPa.展开更多
In order to improve the mechanical properties and corrosion resistance of Mg alloys,the equal channel angular extrusion (ECAE)was employed to fabricate the Mg-5Gd-5Y/Mg-2Zn-1Gd(GW55/ZG21)laminated composites.After fab...In order to improve the mechanical properties and corrosion resistance of Mg alloys,the equal channel angular extrusion (ECAE)was employed to fabricate the Mg-5Gd-5Y/Mg-2Zn-1Gd(GW55/ZG21)laminated composites.After fabrication and annealing treatment,the microstructural evolution,phase constitution,microhardness,and bonding strength were investigated on the bonding interface zone of GW55/ZG21 laminated composites.The bonding interface zone of GW55/ZG21 laminated composites comprises a lot of Mg3(Y,Gd)2Zn3 particles along the bonding interface,some rod Mg24(Y,Gd)5 phases on GW55 side,and a precipitation free zone(PFZ)on ZG21 side.After annealing treatment,Mg3(Y,Gd)2Zn3 particles along the bonding interface increase, rod Mg24(Y,Gd)5 phases on GW55 side decrease,and PFZ is broadened.Meanwhile,the hardness on the bonding interface zone decreases and the bonding strength increases from 126 MPa to 162 MPa.展开更多
基金Project(51101109)supported by the National Natural Science Foundation of China
文摘In order to improve the bonding strength between piston alloys and cast iron ring of aluminum piston with reinforced cast iron ring,the different methods of the surface treatments(shot blasting and sand blasting) to the cast iron ring are experimented.The optical micrograph shows that an intermetallic layer and a ligulate shaped structure are formed between piston alloys and cast iron base ring.After sand blasting treatment,the ring surface is non-metal shiny,matte-like and has no obvious pits.The intermetallic layer thickness formed between piston alloys and cast iron is thinner and more equally distributed after sand blasting to the ring.The content of the graphite distributed the interfacial zone after the shot blasting treatment is little.With the increase of time by sand blasting,the hardness starts to slightly descend.The bonding strength of the sample by sand blasting is obviously higher than that by shot blasting and increases from 9.32 MPa to 19.53 MPa.
基金Project(2007CB613704)supported by the National Basic Research Program of ChinaProject(50874100)supported by the National Natural Science Foundation of China
文摘In order to improve the mechanical properties and corrosion resistance of Mg alloys,the equal channel angular extrusion (ECAE)was employed to fabricate the Mg-5Gd-5Y/Mg-2Zn-1Gd(GW55/ZG21)laminated composites.After fabrication and annealing treatment,the microstructural evolution,phase constitution,microhardness,and bonding strength were investigated on the bonding interface zone of GW55/ZG21 laminated composites.The bonding interface zone of GW55/ZG21 laminated composites comprises a lot of Mg3(Y,Gd)2Zn3 particles along the bonding interface,some rod Mg24(Y,Gd)5 phases on GW55 side,and a precipitation free zone(PFZ)on ZG21 side.After annealing treatment,Mg3(Y,Gd)2Zn3 particles along the bonding interface increase, rod Mg24(Y,Gd)5 phases on GW55 side decrease,and PFZ is broadened.Meanwhile,the hardness on the bonding interface zone decreases and the bonding strength increases from 126 MPa to 162 MPa.