Dry sliding wear tests on as-cast and cast＋T6 Mg-11Y-5Gd-2Zn magnesium alloys were performed using a ball-on-plate configuration. The wear rates were measured within a load range of 3-15 N, sliding speed range of 0.0...Dry sliding wear tests on as-cast and cast＋T6 Mg-11Y-5Gd-2Zn magnesium alloys were performed using a ball-on-plate configuration. The wear rates were measured within a load range of 3-15 N, sliding speed range of 0.03-0.24 m/s, test temperature range of 25-200 °C and at a constant sliding distance of 400 m. The wear tracks, worn surfaces and wear debris of the alloys were analyzed using scanning electron microscope （SEM）. The results show that the wear rate of the alloys increases almost linearly with increasing applied load and decreases with increasing sliding speed. The wear rate of the as-cast alloy is higher than that of the cast＋T6 alloy. The amount of Mg12Y1Zn1 phase, surface oxidation and retained wear debris affect the wear rate. The dominant wear mechanisms under the test condition are abrasion and plastic deformation.展开更多
In order to study the effect of element Nb on the microstructure and properties of the biomedical β-type Ti-Mo based alloys,Ti-15Mo-xNb（x=5,10,15 and 20 in %） alloys were investigated.The dry wear resistance of β-...In order to study the effect of element Nb on the microstructure and properties of the biomedical β-type Ti-Mo based alloys,Ti-15Mo-xNb（x=5,10,15 and 20 in %） alloys were investigated.The dry wear resistance of β-type Ti-15Mo-xNb alloys against Gr15 ball was investigated on CJS111A ball-disk wear instrument.Experimental results indicate that crystal structure and morphology of the Ti-15Mo-xNb alloys are sensitive to their Nb contents.Ti-15Mo-xNb alloys match those for β phase peaks and no any phases are found.The Vickers hardness values of all the Ti-15Mo-xNb alloys are higher than HV200.The compression yield strength of the Ti-15Mo-5Nb alloy is the lowest and that of the Ti-15Mo-10Nb alloy is the highest.For all the Ti-15Mo-xNb alloys,the friction coefficient is not constant but takes a higher value.In dry condition,SEM study reveals deep parallel scars on the wear surfaces of all the Ti-15Mo-xNb alloys under different loads.The friction coefficient of the Ti-15Mo-5Nb alloy under 1 N is the lowest.The wear principal mechanism for Ti-15Mo-xNb alloys is adhesive wear.展开更多
基金Project (51074106) supported by the National Natural Science Foundation of ChinaProject (2009AA033501) supported by the Hi-Tech Research and Development Program of China+1 种基金Project (09JC1408200) supported by the Science and Technology Commission of Shanghai Municipality, ChinaProject (20100480586) supported by Postdoctoral Science Foundation of China
文摘Dry sliding wear tests on as-cast and cast＋T6 Mg-11Y-5Gd-2Zn magnesium alloys were performed using a ball-on-plate configuration. The wear rates were measured within a load range of 3-15 N, sliding speed range of 0.03-0.24 m/s, test temperature range of 25-200 °C and at a constant sliding distance of 400 m. The wear tracks, worn surfaces and wear debris of the alloys were analyzed using scanning electron microscope （SEM）. The results show that the wear rate of the alloys increases almost linearly with increasing applied load and decreases with increasing sliding speed. The wear rate of the as-cast alloy is higher than that of the cast＋T6 alloy. The amount of Mg12Y1Zn1 phase, surface oxidation and retained wear debris affect the wear rate. The dominant wear mechanisms under the test condition are abrasion and plastic deformation.
基金Project(20080440850) supported by China Postdoctoral Science FoundationProject(ZJY0605-02) supported by the Natural Science Foundation of Heilongjiang Province,ChinaProject(HIT.NSRIF.2012002) supported by the Fundamental Research Funds for the Central Universities,China
文摘In order to study the effect of element Nb on the microstructure and properties of the biomedical β-type Ti-Mo based alloys,Ti-15Mo-xNb（x=5,10,15 and 20 in %） alloys were investigated.The dry wear resistance of β-type Ti-15Mo-xNb alloys against Gr15 ball was investigated on CJS111A ball-disk wear instrument.Experimental results indicate that crystal structure and morphology of the Ti-15Mo-xNb alloys are sensitive to their Nb contents.Ti-15Mo-xNb alloys match those for β phase peaks and no any phases are found.The Vickers hardness values of all the Ti-15Mo-xNb alloys are higher than HV200.The compression yield strength of the Ti-15Mo-5Nb alloy is the lowest and that of the Ti-15Mo-10Nb alloy is the highest.For all the Ti-15Mo-xNb alloys,the friction coefficient is not constant but takes a higher value.In dry condition,SEM study reveals deep parallel scars on the wear surfaces of all the Ti-15Mo-xNb alloys under different loads.The friction coefficient of the Ti-15Mo-5Nb alloy under 1 N is the lowest.The wear principal mechanism for Ti-15Mo-xNb alloys is adhesive wear.