Large area diamond films were fabricated on copper substrates by a multi-step process comprised of electroplating Cu-diamond composite layer on Cu substrate, plating a Cu layer to fix the protruding diamond particles,...Large area diamond films were fabricated on copper substrates by a multi-step process comprised of electroplating Cu-diamond composite layer on Cu substrate, plating a Cu layer to fix the protruding diamond particles, and depositing continuous diamond film on composite interlayer by hot-filament chemical vapor deposition （HFCVD）. The interface characteristics, internal stress and adhesion strength were investigated by scanning electron microscopy, Raman analysis and indentation test. The results show that the continuous film without cracks is successfully obtained. The microstructure of the film is a mixture of large cubo-octahedron grains grown from homo-epitaxial growth and small grains with （111） apparent facets grown from lateral second nuclei. The improved adhesion between diamond film and substrate results from the deep anchoring of the diamond particles in the Cu matrix and the low residual stress in the film.展开更多
A high performance composite membrane was prepared under the inspiration of bioadhesion principles for pervaporative dehydration of ethanol.Chitosan(CS)and polyacrylonitrile(PAN)ultrafiltration membranes were used as ...A high performance composite membrane was prepared under the inspiration of bioadhesion principles for pervaporative dehydration of ethanol.Chitosan(CS)and polyacrylonitrile(PAN)ultrafiltration membranes were used as the active layer and the support layer,respectively.Guar gum(GG),a natural bioadhesive,was introduced as the intermediate bonding layer to improve the separation performance and stability of the fabricated CS/GG/PAN composite membranes.The contact angle of the GG layer was just between those of the CS layer and the PAN layer,minimizing the difference of hydrophilicity between the active layer and the support layer.The peeling strength of the composite membrane was significantly enhanced after the introduction of the GG layer.The effects of preparation conditions and operation conditions including GG concentration,operating temperature and ethanol concentration in feed on the pervaporation performance were investigated.The as-fabricated CS/GG/PAN composite membrane showed the optimum performance with a permeation flux of up to804 g·m-2·h-1and a separation factor higher than 1900.Besides,the composite membranes exhibited a desirable long-term operational stability.展开更多
基金Projects(51071070,51271079)supported by the National Natural Science Foundation of ChinaProject(NCET-11-0156)supported by New Century Excellent Talents in University,China
文摘Large area diamond films were fabricated on copper substrates by a multi-step process comprised of electroplating Cu-diamond composite layer on Cu substrate, plating a Cu layer to fix the protruding diamond particles, and depositing continuous diamond film on composite interlayer by hot-filament chemical vapor deposition （HFCVD）. The interface characteristics, internal stress and adhesion strength were investigated by scanning electron microscopy, Raman analysis and indentation test. The results show that the continuous film without cracks is successfully obtained. The microstructure of the film is a mixture of large cubo-octahedron grains grown from homo-epitaxial growth and small grains with （111） apparent facets grown from lateral second nuclei. The improved adhesion between diamond film and substrate results from the deep anchoring of the diamond particles in the Cu matrix and the low residual stress in the film.
基金Supported by the New Century Excellent Talents in University(NCET-10-0623)the National Natural Science Foundation for Distinguished Young Scholars(21125627)+1 种基金the National Basic Research Program of China(2009CB623404)State Key Laboratory for Modification of Chemical Fibers and Polymer Materials(Dong Hua University)
文摘A high performance composite membrane was prepared under the inspiration of bioadhesion principles for pervaporative dehydration of ethanol.Chitosan(CS)and polyacrylonitrile(PAN)ultrafiltration membranes were used as the active layer and the support layer,respectively.Guar gum(GG),a natural bioadhesive,was introduced as the intermediate bonding layer to improve the separation performance and stability of the fabricated CS/GG/PAN composite membranes.The contact angle of the GG layer was just between those of the CS layer and the PAN layer,minimizing the difference of hydrophilicity between the active layer and the support layer.The peeling strength of the composite membrane was significantly enhanced after the introduction of the GG layer.The effects of preparation conditions and operation conditions including GG concentration,operating temperature and ethanol concentration in feed on the pervaporation performance were investigated.The as-fabricated CS/GG/PAN composite membrane showed the optimum performance with a permeation flux of up to804 g·m-2·h-1and a separation factor higher than 1900.Besides,the composite membranes exhibited a desirable long-term operational stability.