As clean energy,the microwave is commonly used to pretreat various ores.In this work,the microwave dielectric properties of limonitic laterite ore were measured by resonant cavity perturbation technique and the effect...As clean energy,the microwave is commonly used to pretreat various ores.In this work,the microwave dielectric properties of limonitic laterite ore were measured by resonant cavity perturbation technique and the effects from microwave were systematically investigated.Results indicated that limonitic laterite had high microwave absorbance.After microwave pretreatment,the microstructure of the laterite became less aggregated and more porous and the main phase transformed from goethite to hematite that improved leaching in nitric acid(1.2 kg HNO3/kg ore);Ni,Co,Fe,and Mg extraction ratios were 95.2%,98.1%,1.8%and 15%,respectively,after leaching for 60 min at 200°C and 500 r/min.Furthermore,in the process of goethite to hematite by microwave pretreatment,the nickel-containing mineral is activated,which makes nickel be leached easily.The leaching process has high Ni extraction ratio compared to that without microwave(82%)and conventional pretreatment(90.4%).Therefore,microwave pretreatment of limonitic laterite before nitric acid pressure leaching is an effective way to improve the selectivity and extraction of the leach.展开更多
基金Project(51974025)supported by the National Natural Science Foundation of ChinaProject(2018IA055)supported by the International Cooperation Project of Key Research and Development Plan of Yunan Province,ChinaProject(JKY2019-09)supported by State Key Laboratory of Nickel and Cobalt Resources Comprehensive Utilization,China。
文摘As clean energy,the microwave is commonly used to pretreat various ores.In this work,the microwave dielectric properties of limonitic laterite ore were measured by resonant cavity perturbation technique and the effects from microwave were systematically investigated.Results indicated that limonitic laterite had high microwave absorbance.After microwave pretreatment,the microstructure of the laterite became less aggregated and more porous and the main phase transformed from goethite to hematite that improved leaching in nitric acid(1.2 kg HNO3/kg ore);Ni,Co,Fe,and Mg extraction ratios were 95.2%,98.1%,1.8%and 15%,respectively,after leaching for 60 min at 200°C and 500 r/min.Furthermore,in the process of goethite to hematite by microwave pretreatment,the nickel-containing mineral is activated,which makes nickel be leached easily.The leaching process has high Ni extraction ratio compared to that without microwave(82%)and conventional pretreatment(90.4%).Therefore,microwave pretreatment of limonitic laterite before nitric acid pressure leaching is an effective way to improve the selectivity and extraction of the leach.