Na_(2)S,Na_(2)CO_(3),FeO,FeS and carbon were used to regulate the properties of slag or metal fractions,and their effects on metal growth and metal–slag separation behavior were investigated.The growth of ferronickel...Na_(2)S,Na_(2)CO_(3),FeO,FeS and carbon were used to regulate the properties of slag or metal fractions,and their effects on metal growth and metal–slag separation behavior were investigated.The growth of ferronickel grains can be enhanced by adding these additives,and Na_(2)S was the most effective.Na_(2)S,Na_(2)CO_(3) and FeO mainly affected the properties of slag,while carbon and FeS affected the metal fraction.The onset temperature of metal–slag separation was 1297℃ for the sample without additive,which was decreased to 1123 and 1101℃ after adding 3.30 wt.%Na_(2)S and 4.47 wt.%Na_(2)CO_(3),respectively.The onset temperature of metal–slag separation was mainly controlled by the slag fraction.The average apparent activation energy of metal grain growth was 125.32 kJ/mol without additive,and it decreased obviously after adding different additives.Na_(2)S also had the most remarkable effect on the decrease in activation energy.展开更多
基金support from the National Natural Science Foundation of China(No.51904047)the Fundamental and Frontier Research Project of Chongqing,China(No.cstc2020jcyj-msxmX0515)the State Key Laboratory of Complex Nonferrous Metal Resources Clean Utilization,China.
文摘Na_(2)S,Na_(2)CO_(3),FeO,FeS and carbon were used to regulate the properties of slag or metal fractions,and their effects on metal growth and metal–slag separation behavior were investigated.The growth of ferronickel grains can be enhanced by adding these additives,and Na_(2)S was the most effective.Na_(2)S,Na_(2)CO_(3) and FeO mainly affected the properties of slag,while carbon and FeS affected the metal fraction.The onset temperature of metal–slag separation was 1297℃ for the sample without additive,which was decreased to 1123 and 1101℃ after adding 3.30 wt.%Na_(2)S and 4.47 wt.%Na_(2)CO_(3),respectively.The onset temperature of metal–slag separation was mainly controlled by the slag fraction.The average apparent activation energy of metal grain growth was 125.32 kJ/mol without additive,and it decreased obviously after adding different additives.Na_(2)S also had the most remarkable effect on the decrease in activation energy.