The multiple cracking and deflection hardening performance of polyvinyl alcohol fiber reinforced engineered cementitious composites(PVA-ECC)under four-point flexural loading have been investigated.Matrices with differ...The multiple cracking and deflection hardening performance of polyvinyl alcohol fiber reinforced engineered cementitious composites(PVA-ECC)under four-point flexural loading have been investigated.Matrices with different binder combinations and W/B ratios(from 0.44 to 0.78)providing satisfactory PVA fiber dispersion were specially designed.Effect of pre-existing flaw size distribution modification on deflection hardening behavior was comparatively studied by adding 3 mm diameter polyethylene beads into the mixtures(6%by total volume).Natural flaw size distributions of composites without beads were determined by cross sectional analysis.The crack number and crack width distributions of specimens after flexural loading were characterized and the possible causes of changes in multiple cracking and deflection hardening behavior by flaw size distribution modification were discussed.Promising results from the view point of deflection hardening behavior were obtained from metakaolin incorporated and flaw size distribution modified PVA-ECCs prepared with W/B=0.53.The dual roles of W/B ratio and superplasticizer content on flaw size distribution,cracking potential and fiber-matrix bond behavior were evaluated.Flaw size distribution modification is found beneficial in terms of ductility improvement at an optimized W/B ratio.展开更多
Strengthening of RC structures with externally bonded FRP （fiber reinforced polymers） has become an important challenge in civil engineering. Epoxy is the main bonding agent used so far, but in the case of a fire, i...Strengthening of RC structures with externally bonded FRP （fiber reinforced polymers） has become an important challenge in civil engineering. Epoxy is the main bonding agent used so far, but in the case of a fire, it is subjected to complete loss of his bonding capabilities. Mineral based composites strengthening systems consist of FRPs and a cementitious bonding agent which form a repair or strengthening system that is more compatible with the concrete substrata, and roved its efficiency. The current research introduces the use of a special cementitious material ＂Grancrete＂ as a bonding agent. Test results of 32 T-section RC beams strengthened with various FRG （fiber reinforced Grancrete） strengthening systems are presented. The results demonstrated that most of the specimens were likely to fail by debonding of the FRP from the concrete either at the ends or at intermediate flexural cracks. This paper presents an in-depth study aimed at the development of a better understanding of debonding failures in RC beams strengthened with externally bonded FRP systems. Different analytical models, published in the literature for plate end debonding, are reviewed and compared to test results. The results also demonstrated that when using U-wraps, the specimens were likely to fail by FRP sheet rupture.展开更多
基金Project(114M246)supported by the Scientific and Technological Research Council of Turkey
文摘The multiple cracking and deflection hardening performance of polyvinyl alcohol fiber reinforced engineered cementitious composites(PVA-ECC)under four-point flexural loading have been investigated.Matrices with different binder combinations and W/B ratios(from 0.44 to 0.78)providing satisfactory PVA fiber dispersion were specially designed.Effect of pre-existing flaw size distribution modification on deflection hardening behavior was comparatively studied by adding 3 mm diameter polyethylene beads into the mixtures(6%by total volume).Natural flaw size distributions of composites without beads were determined by cross sectional analysis.The crack number and crack width distributions of specimens after flexural loading were characterized and the possible causes of changes in multiple cracking and deflection hardening behavior by flaw size distribution modification were discussed.Promising results from the view point of deflection hardening behavior were obtained from metakaolin incorporated and flaw size distribution modified PVA-ECCs prepared with W/B=0.53.The dual roles of W/B ratio and superplasticizer content on flaw size distribution,cracking potential and fiber-matrix bond behavior were evaluated.Flaw size distribution modification is found beneficial in terms of ductility improvement at an optimized W/B ratio.
文摘Strengthening of RC structures with externally bonded FRP （fiber reinforced polymers） has become an important challenge in civil engineering. Epoxy is the main bonding agent used so far, but in the case of a fire, it is subjected to complete loss of his bonding capabilities. Mineral based composites strengthening systems consist of FRPs and a cementitious bonding agent which form a repair or strengthening system that is more compatible with the concrete substrata, and roved its efficiency. The current research introduces the use of a special cementitious material ＂Grancrete＂ as a bonding agent. Test results of 32 T-section RC beams strengthened with various FRG （fiber reinforced Grancrete） strengthening systems are presented. The results demonstrated that most of the specimens were likely to fail by debonding of the FRP from the concrete either at the ends or at intermediate flexural cracks. This paper presents an in-depth study aimed at the development of a better understanding of debonding failures in RC beams strengthened with externally bonded FRP systems. Different analytical models, published in the literature for plate end debonding, are reviewed and compared to test results. The results also demonstrated that when using U-wraps, the specimens were likely to fail by FRP sheet rupture.