表面内嵌纤维筋加固混凝土T形梁的受弯性能

通过对10根不同参数设置下的混凝土T形梁进行受弯试验,研究表面内嵌纤维(fiber reinforced polymer,FRP)筋加固后混凝土T形梁的受弯性能。结果表明:FRP筋表面特征影响加固梁的破坏形态,对极限荷载和FRP筋应变影响显著;钢筋配筋率和FRP筋直径对屈服荷载及极限荷载影响显著,而混凝土强度等级对其基本没有影响;混凝土强度等级、钢筋配筋率和FRP筋直径对加固梁FRP筋应变基本没有影响。推导出表面内嵌FRP筋加固混凝土T形梁受弯承载力计算公式,并结合试验结果,利用二元线性回归法对公式中的折减系数进行了修正。

Strengthening effects of BFRP on reinforced concrete beams

Reinforced concrete （RC） beams externally bonded with basalt fiber reinforced polymer （BFRP） are experimentally investigated by using different numbers of bonding plies, transverse anchorages as well as the initial conditions of strengthened beams. The performances of the BFRP strengthening are compared with those of the carbon fiber reinforced polymer （CFRP） and the glass fiber reinforced polymer （GFRP） under the same experimental condition. Experimental results indicate that the strength and ductility of the strengthened beam with two plies of the BFRP are improved remarkably than those with one ply. The strengthening effects of the BFRP lie between those of the CFRP and the GFRP. The BFRP strengthening is little influenced by pre-cracks of concrete. Most failures are caused by interfaciai debonding induced by flexural cracks in the experiment. Clamping of Uwraps along the whole beam is less efficient than endpoint anchorage for increasing the ultimate load of the strengthened beam. Finally, the models suggested by the five guidelines for predicting the debonding strain of the CFRP are extended to the BFRP and the conservative estimates of the debonding strain of the BFRP are given as well.

Durability of concrete beams reinforced with CFRP sheet under wet-dry cycles and loading

The test results of eight concrete beams reinforced with carbon fiber reinforced polymer （CFRP） sheets subjected to an aggressive environment under a sustained load are presented. The beams are 1 700 mm long with a rectangular cross-section of 120- mm width and 200-mm depth. The beams are precracked with a four-point flexural load, bonded CFRP sheets, and placed into wet-dry saline water（ NaCl） either in an unstressed state or loaded to about 30% or 60% of the initial ultimate load. The individual and coupled effects of wet-dry saline water and sustained bending stresses on the long term behaviour of concrete beams reinforced with the CFRP are investigated. The test results show that the coupled action of wet-dry saline water and sustained bending stresses appears to significantly affect the load capacity and the failure mode of beam strengthened with CFRP, mainly due to the degradation of the bond between CFRP and concrete. However, the stiffness is not affected by the coupled action of wet-dry cycles and a sustained load.

Experimental study and calculation of flexural capacity of RC beams strengthened with GFRP sheets

Nine reinforced concrete (RC) beams strengthened by glass fiber reinforced polymer (GFRP) sheets and three control beams are tested. Four parameters are considered in this experimental program included the concrete strength, the reinforcement ratio, the number of GFRP sheets, and the shear span ratio. It is shown that the application of GFRP sheets can increase the ultimate flexural capacity. The effect of the concrete strength, the reinforcement ratio and the number of GFRP sheets on load capacity is obvious. The shear span ratio can affect the failure mode of RC beams strengthened by GFRP sheets. A theoretical model for flexural behavior of the strengthened RC beam is also developed.

Experimental study and analysis on fatigue stiffness of RC beams strengthened with CFRP and steel plate

The objective of this work is to investigate the fatigue behavior of reinforced concrete(RC) beams strengthened with externally bonded carbon fiber reinforced polymer(CFRP) and steel plate. An experimental investigation and theoretical analysis were made on the law of deflection development and stiffness degradation, as well as the influence of fatigue load ranges. Test results indicate that the law of three-stage change under fatigue loading is followed by both midspan deflection and permanent deflection, which also have positive correlation with fatigue load amplitude. Fatigue stiffness of composite strengthened beams degrades gradually with the increasing of number of cycles. Based on the experimental results, a theoretical model by effective moment of inertia method is developed for calculating the sectional stiffness of such composite strengthened beams under fatigue loading, and the calculated results are in good agreement with the experimental results.