Nano/microcrystalline composite diamond films were deposited on the holes of WC-6%Co drawing dies by a two-step procedure using alternative carbon sources, i.e., methane for the microcrystalline diamond（MCD） layer a...Nano/microcrystalline composite diamond films were deposited on the holes of WC-6%Co drawing dies by a two-step procedure using alternative carbon sources, i.e., methane for the microcrystalline diamond（MCD） layer and acetone for the nanocrystalline diamond（NCD） layer. Moreover, the monolayer methane-MCD and acetone-NCD coated drawing dies were fabricated as comparisons. The adhesion and wear rates of the diamond coated drawing dies were also tested by an inner hole polishing apparatus. Compared with mono-layer diamond coated drawing die, the composite diamond coated one exhibits better comprehensive performance, including higher adhesive strength and better wear resistance than the NCD one, and smoother surface（Ra=65.3 nm） than the MCD one（Ra=95.6 nm） after polishing at the same time. Compared with the NCD coated drawing die, the working lifetime of the composite diamond coated one is increased by nearly 20 times.展开更多
Polyurethane-conjugated HgS nanocrystals with tunable sizes prepared by using biomimetic method. The obtained HgS nanoparticles with good dispersibility were characterized by Fourier transform infrared. Scanning elect...Polyurethane-conjugated HgS nanocrystals with tunable sizes prepared by using biomimetic method. The obtained HgS nanoparticles with good dispersibility were characterized by Fourier transform infrared. Scanning electron microscopy are used to envisage the binding of nanoparticles with functional groups. The polyurethane molecules can control nucleation and growth of HgS crystals by binding on the surface of nanocrystals to stabilize nanoparticles. Quantum confinement effect of polyurethane-conjugated HgS nanocrystals was confirmed by UV-Vis spectra. The nanoparticles exhibit a well-defined emission feature at about 291 nm. The fluorescence results reveal that the PU/HgS nanoparticles film is sensitive to Ba2＋, and a small amount of Ba2＋ makes the emissions increase rapidly. The emission is hardly affected by other common ions in water. The nanocomposite film is possible to become a special sensor material for Ba2＋.展开更多
As the large single-crystalline silicon wafers have revolutionized many industries including electronics and solar cells, it is envisioned that the availability of large single-crystalline perovskite crystals and wafe...As the large single-crystalline silicon wafers have revolutionized many industries including electronics and solar cells, it is envisioned that the availability of large single-crystalline perovskite crystals and wafers will revolutionize its broad applications in photovoltaics, optoelectronics, lasers, photodetectors, light emitting diodes(LEDs), etc. Here we report a method to grow large single-crystalline perovskites including single-halide crystals: CH3NH3PbX3(X=I, Br, Cl), and dual-halide ones:CH3NH3Pb(ClxBr1.x)3 and CH3NH3Pb(BrxI1.x)3, with the largest crystal being 120 mm in length. Meanwhile, we have advanced a process to slice the large perovskite crystals into thin wafers. It is found that the wafers exhibit remarkable features:(1)its trap-state density is a million times smaller than that in the microcrystalline perovskite thin films(MPTF);(2) its carrier mobility is 410 times higher than its most popular organic counterpart P3HT;(3) its optical absorption is expanded to as high as910 nm comparing to 797 nm for the MPTF;(4) while MPTF decomposes at 150 °C, the wafer is stable at high temperature up to270 °C;(5) when exposed to high humidity(75% RH), MPTF decomposes in 5 h while the wafer shows no change for overnight;(6) its photocurrent response is 250 times higher than its MPTF counterpart. A few electronic devices have been fabricated using the crystalline wafers. Among them, the Hall test gives low carrier concentration with high mobility. The trap-state density is measured much lower than common semiconductors. Moreover, the large SC-wafer is found particularly useful for mass production of integrated circuits. By adjusting the halide composition, both the optical absorption and the light emission can be fine-tuned across the entire visible spectrum from 400 nm to 800 nm. It is envisioned that a range of visible lasers and LEDs may be developed using the dual-halide perovskites. With fewer trap states, high mobility, broader absorption, and humidity resistance, it is expected that solar cells with high stable efficiency maybe attainable using the crystalline wafers.展开更多
基金Project(51275302) supported by the National Natural Science Foundation of China
文摘Nano/microcrystalline composite diamond films were deposited on the holes of WC-6%Co drawing dies by a two-step procedure using alternative carbon sources, i.e., methane for the microcrystalline diamond（MCD） layer and acetone for the nanocrystalline diamond（NCD） layer. Moreover, the monolayer methane-MCD and acetone-NCD coated drawing dies were fabricated as comparisons. The adhesion and wear rates of the diamond coated drawing dies were also tested by an inner hole polishing apparatus. Compared with mono-layer diamond coated drawing die, the composite diamond coated one exhibits better comprehensive performance, including higher adhesive strength and better wear resistance than the NCD one, and smoother surface（Ra=65.3 nm） than the MCD one（Ra=95.6 nm） after polishing at the same time. Compared with the NCD coated drawing die, the working lifetime of the composite diamond coated one is increased by nearly 20 times.
基金This work was supported by the National Natural Science Foundation of China （No.21102121）, the Shaanxi Province Council （No.2014JQ2077）, the China＇s Scholarship Council （No.2013JK0643）, and the Xianyang Normal University Council （No.13XSYK021）.
文摘Polyurethane-conjugated HgS nanocrystals with tunable sizes prepared by using biomimetic method. The obtained HgS nanoparticles with good dispersibility were characterized by Fourier transform infrared. Scanning electron microscopy are used to envisage the binding of nanoparticles with functional groups. The polyurethane molecules can control nucleation and growth of HgS crystals by binding on the surface of nanocrystals to stabilize nanoparticles. Quantum confinement effect of polyurethane-conjugated HgS nanocrystals was confirmed by UV-Vis spectra. The nanoparticles exhibit a well-defined emission feature at about 291 nm. The fluorescence results reveal that the PU/HgS nanoparticles film is sensitive to Ba2＋, and a small amount of Ba2＋ makes the emissions increase rapidly. The emission is hardly affected by other common ions in water. The nanocomposite film is possible to become a special sensor material for Ba2＋.
基金supported by the National Key Research Project MOST (2016YFA0202400)the National Natural Science Foundation of China (61604090, 61604091, 61674098)+4 种基金National University Research Fund (GK261001009, GK201603107)the Changjiang Scholar and Innovative Research Team (IRT_14R33)the 111 Project (B14041)the Chinese National 1000-talent-plan Program (1110010341)the Innovation Funds of Graduate Programs, SNNU (2015CXS047)
文摘As the large single-crystalline silicon wafers have revolutionized many industries including electronics and solar cells, it is envisioned that the availability of large single-crystalline perovskite crystals and wafers will revolutionize its broad applications in photovoltaics, optoelectronics, lasers, photodetectors, light emitting diodes(LEDs), etc. Here we report a method to grow large single-crystalline perovskites including single-halide crystals: CH3NH3PbX3(X=I, Br, Cl), and dual-halide ones:CH3NH3Pb(ClxBr1.x)3 and CH3NH3Pb(BrxI1.x)3, with the largest crystal being 120 mm in length. Meanwhile, we have advanced a process to slice the large perovskite crystals into thin wafers. It is found that the wafers exhibit remarkable features:(1)its trap-state density is a million times smaller than that in the microcrystalline perovskite thin films(MPTF);(2) its carrier mobility is 410 times higher than its most popular organic counterpart P3HT;(3) its optical absorption is expanded to as high as910 nm comparing to 797 nm for the MPTF;(4) while MPTF decomposes at 150 °C, the wafer is stable at high temperature up to270 °C;(5) when exposed to high humidity(75% RH), MPTF decomposes in 5 h while the wafer shows no change for overnight;(6) its photocurrent response is 250 times higher than its MPTF counterpart. A few electronic devices have been fabricated using the crystalline wafers. Among them, the Hall test gives low carrier concentration with high mobility. The trap-state density is measured much lower than common semiconductors. Moreover, the large SC-wafer is found particularly useful for mass production of integrated circuits. By adjusting the halide composition, both the optical absorption and the light emission can be fine-tuned across the entire visible spectrum from 400 nm to 800 nm. It is envisioned that a range of visible lasers and LEDs may be developed using the dual-halide perovskites. With fewer trap states, high mobility, broader absorption, and humidity resistance, it is expected that solar cells with high stable efficiency maybe attainable using the crystalline wafers.