Nanogrinding of SiC wafers with high flatness and low subsurface damage was proposed and nanogrinding experiments were carried out on an ultra precision grinding machine with fine diamond wheels. Experimental results ...Nanogrinding of SiC wafers with high flatness and low subsurface damage was proposed and nanogrinding experiments were carried out on an ultra precision grinding machine with fine diamond wheels. Experimental results show that nanogrinding can produce flatness less than 1.0μm and a surface roughness Ra of 0.42nm. It is found that nanogrinding is capable of producing much flatter SiC wafers with a lower damage than double side lapping and mechanical polishing in much less time and it can replace double side lapping and mechanical polishing and reduce the removal amount of chemical mechanical polishing.展开更多
Novel tetra-methoxy resorcinarene tetra-hydrazide（TMRTH） has been synthesized and used as a reducing agent and a capping agent for the synthesis of water-dispersible stable palladium nanoparticles（PdNPs）.The TMRTH...Novel tetra-methoxy resorcinarene tetra-hydrazide（TMRTH） has been synthesized and used as a reducing agent and a capping agent for the synthesis of water-dispersible stable palladium nanoparticles（PdNPs）.The TMRTH-PdNPs were characterized by UV-Vis spectroscopy,transmission electron microscopy,energy-dispersive X-ray spectroscopy,and powder X-ray diffraction.The synthesized nanoparticles are polydispersible with a size of 5 ± 2 nm and were found to be recyclable over five cycles maintaining a catalytic activity in the Suzuki-Miyuara cross-coupling reaction.The nanocatalyst was superior in catalytic performance to conventional palladium catalysts with respect to reaction time,catalyst loading and recyclability.TMRTH-PdNPs show promise for their use in biological applications as they exhibit good antibacterial activity against gram-positive bacteria.展开更多
基金Project (50975040) supported by the National Natural Science Foundation of China
文摘Nanogrinding of SiC wafers with high flatness and low subsurface damage was proposed and nanogrinding experiments were carried out on an ultra precision grinding machine with fine diamond wheels. Experimental results show that nanogrinding can produce flatness less than 1.0μm and a surface roughness Ra of 0.42nm. It is found that nanogrinding is capable of producing much flatter SiC wafers with a lower damage than double side lapping and mechanical polishing in much less time and it can replace double side lapping and mechanical polishing and reduce the removal amount of chemical mechanical polishing.
基金financial assistance provided by UGC(University Grant Commission)DRDO (Defence Research Development Organisation),New Delhi
文摘Novel tetra-methoxy resorcinarene tetra-hydrazide（TMRTH） has been synthesized and used as a reducing agent and a capping agent for the synthesis of water-dispersible stable palladium nanoparticles（PdNPs）.The TMRTH-PdNPs were characterized by UV-Vis spectroscopy,transmission electron microscopy,energy-dispersive X-ray spectroscopy,and powder X-ray diffraction.The synthesized nanoparticles are polydispersible with a size of 5 ± 2 nm and were found to be recyclable over five cycles maintaining a catalytic activity in the Suzuki-Miyuara cross-coupling reaction.The nanocatalyst was superior in catalytic performance to conventional palladium catalysts with respect to reaction time,catalyst loading and recyclability.TMRTH-PdNPs show promise for their use in biological applications as they exhibit good antibacterial activity against gram-positive bacteria.