纳米碳管电极上氧的电催化还原

以聚四氟乙烯为粘结剂制成了多壁纳米碳管(MWNT)电极.采用恒电位阶跃法和循环伏安法研究了MWNT电极在碱性溶液中的电化学行为,并对碱性溶液中溶解氧在该电极上的电化学还原行为进行了研究.实验结果表明:MWNT电极具有比石墨电极更高的孔隙率和电化学表面积;MWNT电极上O2还原成HO2-的反应为准可逆过程;在5～50mV·s-1的扫描速率范围内,阴极峰电流与扫描速度成线性关系,表明MWNT电极上O2还原成HO2-的反应受吸附控制;对碱性溶液中的氧还原反应,MWNT比石墨具有更高的催化活性.

玻璃基片上纳米碳管电极的集成

利用微波等离子体化学气相沉积法在玻璃孔穴中定位生长纳米碳管电极,分析了负偏压对纳米碳管电极生长的影响.该电极对铜离子的电化学检测性能分析结果表明,所制备的纳米碳管电极具有良好的电化学检测性能,位于-0.0100V附近的铜离子的还原峰峰形良好,其电流在铜离子浓度为0.01￣0.30mmol·L-1时,与Cu2+浓度呈良好的线性关系,相关系数为0.9975,且具有较好的长期稳定性和重现性.

纳米碳管电极的制备与电化学检测性能研究

Under the assistant effect of sulfur, carbon nanotubes electrodes were prepared on the end of tungsten strings directly through microwave plasma chemical vapor deposition. And the electrochemical behavior of CuSO4 at the carbon nanotubes electrodes was investigated. Compared to the graphite electrode, carbon nanotubes elec- trodes had better electrochemical behavior for the analysis of Cu2+. Different electrodes prepared under the same condition showed good consistency of electrochemical detection property. And because carbon nanotubes were synthesized directly on the end of tungsten strings, the results of long-term stability experiments demonstrated that the carbon nanotubes electrodes had stable response to Cu2+ solution.

集成纳米碳管电极的电化学检测性能

电极的机械稳定性对电极电化学检测性能的长期稳定性非常重要。利用微波等离子体化学气相沉积法在玻璃基板上集成了纳米碳管电极,并利用该电极对溶液中的邻苯二酚进行了电化学检测。结果表明,经氧等离子体处理的纳米碳管电极具有良好的电化学检测性能,且由于该电极直接集成在玻璃基片上,良好的结构稳定性赋予该电极极为优异的重现性和长期稳定性。

集成纳米碳管电极的电化学检测性能研究

电极具有自身的机械稳定性,这些对电极电化学性能的长时间稳定性有着重要的作用,本文使用微波离子的方式和气相沉淀法逐步进行碳管电极的合成,并充分利用电极溶液之中的邻苯二酚等进行电化学检测。结果显示,经历过氧离子等处理之后的纳米碳管电极的电化学特征良好,该种电极在玻璃基片上合成效果良好,结构较为稳定,电极的优异性和稳定性被凸现出来。

等离子体改性对纳米碳管电化学检测性能的影响

利用微波等离子体化学气相沉积法制备了与电极基底结合良好的纳米碳管电极,用空气等离子体将该纳米碳管电极功能化,并以功能化的电极为工作电极,利用循环伏安法对毒性很强的酚的混合物进行检测。根据氧化还原峰电位的不同可以区分出邻苯二酚和对苯二酚,与石墨电极相比,功能化的纳米碳管电极具有更好的电催化性能。利用该电极测定酚的混合物是一种准确、快速、有效的测定方法。合成纳米碳管电极的最佳工艺条件为:功率为400 W,压强为3.0 kPa,甲烷流速为2 mL/m in,氢气流速为50 mL/m in;功能化纳米碳管的最佳工艺条件为:功率为150 W,压强为1.0 kPa,空气的流速为50 mL/m in。