The preparation process of amorphous nanometer boron powders through combustion synthesis was investigated, and the effects of the reactant ratio, the heating agent and the milling rate on the activity and particle si...The preparation process of amorphous nanometer boron powders through combustion synthesis was investigated, and the effects of the reactant ratio, the heating agent and the milling rate on the activity and particle size of amorphous boron powders were studied. The results show that the boron powders exist in the form of an amorphous phase which has the crystallinity lower than 30.4%, and the panicle size of boron powder decreases with an increase of the high-energy ball milling rate. The purity of amorphous boron powder is 94.8% and panicle sizes are much smaller than 100 nm when the mass ratio of B2O3/Mg/KClO3 is 100：105：17 and the ball milling time is 20 min with the milling rate of 300 r/min. At the same time, the amorphous boron nano-fibers appear in the boron powders.展开更多
基金Project(51002025) supported by the National Natural Science Foundation of China
文摘The preparation process of amorphous nanometer boron powders through combustion synthesis was investigated, and the effects of the reactant ratio, the heating agent and the milling rate on the activity and particle size of amorphous boron powders were studied. The results show that the boron powders exist in the form of an amorphous phase which has the crystallinity lower than 30.4%, and the panicle size of boron powder decreases with an increase of the high-energy ball milling rate. The purity of amorphous boron powder is 94.8% and panicle sizes are much smaller than 100 nm when the mass ratio of B2O3/Mg/KClO3 is 100：105：17 and the ball milling time is 20 min with the milling rate of 300 r/min. At the same time, the amorphous boron nano-fibers appear in the boron powders.