以四氯化钛、盐酸为原料,制备出花状TiO_2纳米微球,利用扫描电子显微镜(SEM)、X射线衍射(XRD)等测试方法,对样品的结构和形貌进行了表征。为了提高TiO_2微球电池的光电性能,利用TiO_2微球作为反射层构造了双层结构的薄膜电极,结果表明,...以四氯化钛、盐酸为原料,制备出花状TiO_2纳米微球,利用扫描电子显微镜(SEM)、X射线衍射(XRD)等测试方法,对样品的结构和形貌进行了表征。为了提高TiO_2微球电池的光电性能,利用TiO_2微球作为反射层构造了双层结构的薄膜电极,结果表明,双层结构染料敏化太阳能电池在100 m W·cm-2(1.5 G)光照条件下,短路光电流Jsc=17.64 m A·cm-2,开路光电压Voc=0.74 V,填充因子FF=0.63和光电转化效率η=8.33%。相比TiO_2微球制备的太阳能电池,双层结构染料敏化太阳能电池光电转化效率提高至5.3倍。最后对电极中染料的吸附量、电极的光散射性能和电池的电化学阻抗做了进一步研究和分析,研究表明,双层结构电池增强光的捕获能力,从而提高光伏性能。展开更多
Using Ti powder as reagent, TiO 2 nanoneedle/nanoribbon spheres were prepared via hydrothermal method in NaOH solution. The samples were characterized by field emission scanning electron microscopy （FESEM）, transmis...Using Ti powder as reagent, TiO 2 nanoneedle/nanoribbon spheres were prepared via hydrothermal method in NaOH solution. The samples were characterized by field emission scanning electron microscopy （FESEM）, transmission electron microscopy （TEM） with selected area electron diffraction （SAED）, X-ray diffraction （XRD）, and UV-visible light absorption spectrum. The results indicate that the growth orientations of the crystals are influenced by the hydrothermal temperature and NaOH concentration. The diameter of the nanoneedle spheres and nanoribbon spheres （40 50 μm） are almost the same as that of Ti powders. TiO 2 nanoneedle/nanoribbon sphere powders are anatase after heat treatment at 450 °C for 1 h. Furthermore, methyl orange was used as a target molecule to estimate the photocatalytic activity of the specimens. Under the same testing conditions, the photocatalytic activities of the products decrease in the following order： TiO 2 nanoneedle sphere, TiO 2 nanoribbon sphere and P25.展开更多
Urchin-like SnO2 microspheres have been grown for use as photoanodes in dye-sensitized solar cells （DSSCs）. We observed that a thin layer coating of TiO2 on urchin-like SnO2 microsphere photoanodes greatly enhanced ...Urchin-like SnO2 microspheres have been grown for use as photoanodes in dye-sensitized solar cells （DSSCs）. We observed that a thin layer coating of TiO2 on urchin-like SnO2 microsphere photoanodes greatly enhanced dye loading capability and light scattering ability, and achieved comparable solar cell per- formance even at half the thickness of a typical nanocrystalline TiO2 photoanode. In addition, this photoanode only required attaching -55% of the amount of dye for efficient light harvesting compared to one based on nanocrystalline TiO2. Longer decay of transient photovoltage and higher charge recombination resistance evidenced from electrochemical impedance spectroscopy of the devices based on TiO2 coated urchin-like SnO2 revealed slower recombination rates of electrons as a result of the thin blocking layer of TiO2 coated on urchin- like SnO2. TiO2 coated urchin-like SnO2 showed the highest value （76.1 ms） of electron lifetime （＇r） compared to 2.4 ms for bare urchin-like SnO2 and 14.9 ms for nanocrystalline TiO2. TiO2 coated SnO2 showed greatly enhanced open circuit voltage （Voc）, short-circuit current density （Jsc） and fill factor （FF） leading to a four-fold increase in efficiency increase compared to bare SnO2. Although TiO2 coated urchin-like SnO2 showed slightly lower cell efficiency than nanocrystalline TiO2, it only used a half thickness of photoanode and saved -45% of the amount of dye for efficient light harvesting compared to normal nanocrystalline TiO2.展开更多
Uniquely structured rutile TiO2 microspheres with exposed nano-acicular single crystals have been successfully synthesized via a facile hydrothermal method. After calcination at 450 ℃ for 2 h, the futile TiO2 microsp...Uniquely structured rutile TiO2 microspheres with exposed nano-acicular single crystals have been successfully synthesized via a facile hydrothermal method. After calcination at 450 ℃ for 2 h, the futile TiO2 microspheres with a high surface area of 132 m2/g have been utilized as a light harvesting enhancement material for dye-sensitized solar cells （DSSCs）. The resultant DSSCs exhibit an overall light conversion efficiency of 8.41% for TiO2 photoanodes made of futile TiO2 microspheres and anatase TiO, nanoparticles （mass ratio of 1：1）, significantly higher than that of pure anatase TiO2 nanoparticle photoanodes of similar thickness （6.74%）. Such a significant improvement in performance can be attributed to the enhanced light harvesting capability and synergetic electron transfer effect. This is because the photoanodes made of futile TiO2 microsphere possess high refractive index which improves the light utilisation efficiency, suitable microsphere core sizes （450-800 nm） to effectively scatter visible light, high surface area for dye loading, and synergetic electron transfer effects between nanoparticulate anatase and nano-acicular futile single crystals phases giving high electron collection efficiency.展开更多
文摘以四氯化钛、盐酸为原料,制备出花状TiO_2纳米微球,利用扫描电子显微镜(SEM)、X射线衍射(XRD)等测试方法,对样品的结构和形貌进行了表征。为了提高TiO_2微球电池的光电性能,利用TiO_2微球作为反射层构造了双层结构的薄膜电极,结果表明,双层结构染料敏化太阳能电池在100 m W·cm-2(1.5 G)光照条件下,短路光电流Jsc=17.64 m A·cm-2,开路光电压Voc=0.74 V,填充因子FF=0.63和光电转化效率η=8.33%。相比TiO_2微球制备的太阳能电池,双层结构染料敏化太阳能电池光电转化效率提高至5.3倍。最后对电极中染料的吸附量、电极的光散射性能和电池的电化学阻抗做了进一步研究和分析,研究表明,双层结构电池增强光的捕获能力,从而提高光伏性能。
基金Project (NS2010153) supported by Nanjing University of Aeronautics and Astronautics Research Funding, ChinaProject (BE2009130) supported by Jiangsu Key Technology R&D Program, China
文摘Using Ti powder as reagent, TiO 2 nanoneedle/nanoribbon spheres were prepared via hydrothermal method in NaOH solution. The samples were characterized by field emission scanning electron microscopy （FESEM）, transmission electron microscopy （TEM） with selected area electron diffraction （SAED）, X-ray diffraction （XRD）, and UV-visible light absorption spectrum. The results indicate that the growth orientations of the crystals are influenced by the hydrothermal temperature and NaOH concentration. The diameter of the nanoneedle spheres and nanoribbon spheres （40 50 μm） are almost the same as that of Ti powders. TiO 2 nanoneedle/nanoribbon sphere powders are anatase after heat treatment at 450 °C for 1 h. Furthermore, methyl orange was used as a target molecule to estimate the photocatalytic activity of the specimens. Under the same testing conditions, the photocatalytic activities of the products decrease in the following order： TiO 2 nanoneedle sphere, TiO 2 nanoribbon sphere and P25.
文摘Urchin-like SnO2 microspheres have been grown for use as photoanodes in dye-sensitized solar cells （DSSCs）. We observed that a thin layer coating of TiO2 on urchin-like SnO2 microsphere photoanodes greatly enhanced dye loading capability and light scattering ability, and achieved comparable solar cell per- formance even at half the thickness of a typical nanocrystalline TiO2 photoanode. In addition, this photoanode only required attaching -55% of the amount of dye for efficient light harvesting compared to one based on nanocrystalline TiO2. Longer decay of transient photovoltage and higher charge recombination resistance evidenced from electrochemical impedance spectroscopy of the devices based on TiO2 coated urchin-like SnO2 revealed slower recombination rates of electrons as a result of the thin blocking layer of TiO2 coated on urchin- like SnO2. TiO2 coated urchin-like SnO2 showed the highest value （76.1 ms） of electron lifetime （＇r） compared to 2.4 ms for bare urchin-like SnO2 and 14.9 ms for nanocrystalline TiO2. TiO2 coated SnO2 showed greatly enhanced open circuit voltage （Voc）, short-circuit current density （Jsc） and fill factor （FF） leading to a four-fold increase in efficiency increase compared to bare SnO2. Although TiO2 coated urchin-like SnO2 showed slightly lower cell efficiency than nanocrystalline TiO2, it only used a half thickness of photoanode and saved -45% of the amount of dye for efficient light harvesting compared to normal nanocrystalline TiO2.
文摘Uniquely structured rutile TiO2 microspheres with exposed nano-acicular single crystals have been successfully synthesized via a facile hydrothermal method. After calcination at 450 ℃ for 2 h, the futile TiO2 microspheres with a high surface area of 132 m2/g have been utilized as a light harvesting enhancement material for dye-sensitized solar cells （DSSCs）. The resultant DSSCs exhibit an overall light conversion efficiency of 8.41% for TiO2 photoanodes made of futile TiO2 microspheres and anatase TiO, nanoparticles （mass ratio of 1：1）, significantly higher than that of pure anatase TiO2 nanoparticle photoanodes of similar thickness （6.74%）. Such a significant improvement in performance can be attributed to the enhanced light harvesting capability and synergetic electron transfer effect. This is because the photoanodes made of futile TiO2 microsphere possess high refractive index which improves the light utilisation efficiency, suitable microsphere core sizes （450-800 nm） to effectively scatter visible light, high surface area for dye loading, and synergetic electron transfer effects between nanoparticulate anatase and nano-acicular futile single crystals phases giving high electron collection efficiency.