Ceramic coating incorporated with nano-SiC was obtained on AZ91D magnesium alloy during MAO by adding nano-SiC into the silicate-aluminate-based composite electrolyte. The microstructure, thickness, phase analysis, el...Ceramic coating incorporated with nano-SiC was obtained on AZ91D magnesium alloy during MAO by adding nano-SiC into the silicate-aluminate-based composite electrolyte. The microstructure, thickness, phase analysis, element composition and hardness of the coatings were respectively investigated by scanning electron microscopy（SEM）, film thickness meter, X-ray diffraction （XRD）, energy disperse spectroscopy（EDS） and Vickers hardness tester. The wear resistance of Mg alloy and coatings were evaluated by friction and wear apparatus, while the corrosion resistance of Mg alloy and coatings were evaluated by potentiodynamic polarization test and electrochemical impedance spectroscopy （EIS）. The results show that after adding nano-SiC into the electrolyte, both the striking voltage and final voltage decrease, the size and number of the micropore on the surface of the coating decrease, the thickness and hardness of the coating increase, both the wear resistance and corrosion resistance of the coating raise.展开更多
Microstructure of GaAs/SiO 2 nanogranular thin films fabricated by radio frequency magnetron co sputtering technique and postannealing are investigated via atomic force microscope,X ray diffraction,and Rutherford b...Microstructure of GaAs/SiO 2 nanogranular thin films fabricated by radio frequency magnetron co sputtering technique and postannealing are investigated via atomic force microscope,X ray diffraction,and Rutherford backscattering spectroscopy.The results show that GaAs nanocrystals with average diameters from 1 5nm to 3 2nm (depending on the annealing temperature) are uniformly dispersed in the SiO 2 matrices.GaAs and SiO 2 are found in normal stoichiometry in the films.The nonlinear optical refraction and nonlinear optical absorption are studied by Z scan technique using a single Gaussian beam of pulse laser.The third order nonlinear optical refractive index and nonlinear absorption coefficient are enhanced due to the quantum confinement effects and estimated to be 4×10 -12 m 2/W and 2×10 -5 m/W respectively in nonresonant condition,while 2×10 -11 m 2/W and -1×10 -4 m/W respectively in quasi resonant condition.展开更多
The fabrication of nanocrystalline nickel coatings was conducted by pulse jet electrodeposition on the substrate of 45# carbon steel.The effects of average current density on the surface morphology,microstructure,aver...The fabrication of nanocrystalline nickel coatings was conducted by pulse jet electrodeposition on the substrate of 45# carbon steel.The effects of average current density on the surface morphology,microstructure,average grain size and microhardness of nickel coatings were investigated by scanning electron microscopy(SEM),X-ray diffractometry(XRD)and microhardness measurement.In addition,the corrosion resistances of coating and substrate were compared.It is revealed that the nickel coatings prepared by pulse jet electrodeposition exhibit a fine-grained structure with a smooth surface and a high density,although some pores and defects are still present in coatings.With the increase of average current density,the average grain size of nickel coatings is reduced at first and then increased.The coating with the optimum compactness,the smallest average grain size(13.7 nm)and the highest microhardness are obtained at current density of 39.8 A/dm2.The corrosion resistance is obviously increased for the coatings prepared by pulse jet electrodeposition;however,the corrosion rate is increased after a certain period due to the penetration of the corrosive media.展开更多
Diffusion bonding between aluminum and copper was performed by vacuum hot pressing at temperatures between 623 and 923 K through two thermal processes： hot compression under the deformation rate of 0.2 mrrdmin for 10...Diffusion bonding between aluminum and copper was performed by vacuum hot pressing at temperatures between 623 and 923 K through two thermal processes： hot compression under the deformation rate of 0.2 mrrdmin for 10 rain at pre-set temperatures, and additional pressing at 0.2 mm/min for 20 rain during furnace cooling. After analyzing interface, the feasible diffusion bonding temperature was suggested as 823 K. The three major intermetallic layers generated during diffusion bonding process were identified as AIECu, AlCu＋AlaCu4 and Al4Cu9. Furthermore, local hardness values ofAlECU, AlCu＋AlaCu4 and Al4Cu9 layers average at （4.97±0.05）, （6.33±0.00） and （6.06±0.18） GPa, respectively.展开更多
In this paper,15Cr-ODS steels containing 0,1 wt%,2 wt%and 3 wt%Al element were fabricated by combining wet-milling and spark plasma sintering(SPS)methods.The microstructure and mechanical properties of ODS steel were ...In this paper,15Cr-ODS steels containing 0,1 wt%,2 wt%and 3 wt%Al element were fabricated by combining wet-milling and spark plasma sintering(SPS)methods.The microstructure and mechanical properties of ODS steel were investigated by XRD,SEM,TEM,EBSD and tensile tests.The results demonstrate that the Al addition significantly refines the particle precipitates in the Fe-Cr matrix,leading to the obvious refinement in grain size of matrix and the improvement of mechanical properties.The dispersion particles in ODS steels with Al addition are identified as Al2O3 and Y_(2)Ti_(2)O_(7)nanoparticles,which has a heterogeneous size distribution in the range of 5 nm to 300 nm.Increasing Al addition causes an obvious increase in tensile strength and a decline in elongation.The tensile strength and elongation of 15Cr-ODS steel containing 3 wt%Al are 775.3 MPa and 15.1%,respectively.The existence of Al element improves the corrosion resistance of materials.The ODS steel containing 2 wt%Al shows corrosion potential of 0.39 V and passivation current density of 2.61×10^(−3)A/cm^(2)(1.37 V).This work shows that Al-doped ODS steels prepared by wet-milling and SPS methods have a potential application in structural parts for nuclear system.展开更多
The flow behavior of pressure-driven water infiltration through graphene-based slit nanopores has been studied by molecular simulation.The simulated flow rate is close to the experimental values,which demonstrates the...The flow behavior of pressure-driven water infiltration through graphene-based slit nanopores has been studied by molecular simulation.The simulated flow rate is close to the experimental values,which demonstrates the reasonability of simulation results.Water molecules can spontaneously infiltrate into the nanopores,but an external driving force is generally required to pass through the whole pores.The exit of nanopore has a large obstruction on the water effusion.The flow velocity within the graphene nanochannels does not display monotonous dependence upon the pore width,indicating that the flow is related to the microscopic structures of water confined in the nanopores.Extensive structures of confined water are characterized in order to understand the flow behavior.This simulation improves the understanding of graphene-based nanofluidics,which helps in developing a new type of membrane separation technique.展开更多
Electroless Ni-Fe-P alloy plating on the surface of CNTs was carded out with a bath using citrate salt and lactic acid as complex agents. We proposed a chemical reaction mechanism. The morphology, structure and chemic...Electroless Ni-Fe-P alloy plating on the surface of CNTs was carded out with a bath using citrate salt and lactic acid as complex agents. We proposed a chemical reaction mechanism. The morphology, structure and chemical composition of the Ni-Fe-P/CNTs were studied with the aid of a scanning electronic microscope （SEM）, X-ray diffraction （XRD） and an energy-dispersive X-ray spectral analysis （EDS）. The results show that through a correct pre-treatment and electroless plating, Ni-Fe-P/CNTs composite particles can be obtained. The optimum electroless plating parameters of 35-42℃ and pH of 8.5-9.7 were achieved. The as-plated Ni-Fe-P alloy is amorphous. After a heat treatment at 500℃ for 90 min in H2, the coating is transformed into crystalloid Ni3E Fe2NiP and （Fe,Ni）3R The Ni-Fe-P alloy coating on the surface of CNTs is smooth and unique. The amount of Ni on the surface （mass fraction） of the Ni-Fe-P/CNTs composite particles is 29.13%, that of Fe 3.19% and that of P 2.28%.展开更多
A1203/5%SIC nanocomposites were fabricated by pressureless sintering using MgO as a sintering aid and then post hot-isostatic pressed （HIP）, which can subsequently break through the disadvantage of hot-pressing proc...A1203/5%SIC nanocomposites were fabricated by pressureless sintering using MgO as a sintering aid and then post hot-isostatic pressed （HIP）, which can subsequently break through the disadvantage of hot-pressing process. The MgO additive was able to promote the densification of the composites, but could not induce the grain growth of A1203 matrix due to the grain growth inhibition by nano-sized SiC particles. After HIP treatment, A12OJSiC nanocomposites achieved full densification and homogeneous distribution of nano-sized SiC particles. Moreover, the fracture morphology of HIP treated specimens was identical with that of the hot-pressed A1203/SiC nanocomposites showing complete transgranular fracture. Consequently, high fracture strength of 1 GPa was achieved for the A1203/5%SIC nanocomposites by pressureless sintering and post HIP process.展开更多
基金Project(12504230006) supported by the Priority Academic Program Development of Jiangsu Higher Education Institutions,China
文摘Ceramic coating incorporated with nano-SiC was obtained on AZ91D magnesium alloy during MAO by adding nano-SiC into the silicate-aluminate-based composite electrolyte. The microstructure, thickness, phase analysis, element composition and hardness of the coatings were respectively investigated by scanning electron microscopy（SEM）, film thickness meter, X-ray diffraction （XRD）, energy disperse spectroscopy（EDS） and Vickers hardness tester. The wear resistance of Mg alloy and coatings were evaluated by friction and wear apparatus, while the corrosion resistance of Mg alloy and coatings were evaluated by potentiodynamic polarization test and electrochemical impedance spectroscopy （EIS）. The results show that after adding nano-SiC into the electrolyte, both the striking voltage and final voltage decrease, the size and number of the micropore on the surface of the coating decrease, the thickness and hardness of the coating increase, both the wear resistance and corrosion resistance of the coating raise.
文摘Microstructure of GaAs/SiO 2 nanogranular thin films fabricated by radio frequency magnetron co sputtering technique and postannealing are investigated via atomic force microscope,X ray diffraction,and Rutherford backscattering spectroscopy.The results show that GaAs nanocrystals with average diameters from 1 5nm to 3 2nm (depending on the annealing temperature) are uniformly dispersed in the SiO 2 matrices.GaAs and SiO 2 are found in normal stoichiometry in the films.The nonlinear optical refraction and nonlinear optical absorption are studied by Z scan technique using a single Gaussian beam of pulse laser.The third order nonlinear optical refractive index and nonlinear absorption coefficient are enhanced due to the quantum confinement effects and estimated to be 4×10 -12 m 2/W and 2×10 -5 m/W respectively in nonresonant condition,while 2×10 -11 m 2/W and -1×10 -4 m/W respectively in quasi resonant condition.
基金Project(50175053) supported by the National Natural Science Foundation of China
文摘The fabrication of nanocrystalline nickel coatings was conducted by pulse jet electrodeposition on the substrate of 45# carbon steel.The effects of average current density on the surface morphology,microstructure,average grain size and microhardness of nickel coatings were investigated by scanning electron microscopy(SEM),X-ray diffractometry(XRD)and microhardness measurement.In addition,the corrosion resistances of coating and substrate were compared.It is revealed that the nickel coatings prepared by pulse jet electrodeposition exhibit a fine-grained structure with a smooth surface and a high density,although some pores and defects are still present in coatings.With the increase of average current density,the average grain size of nickel coatings is reduced at first and then increased.The coating with the optimum compactness,the smallest average grain size(13.7 nm)and the highest microhardness are obtained at current density of 39.8 A/dm2.The corrosion resistance is obviously increased for the coatings prepared by pulse jet electrodeposition;however,the corrosion rate is increased after a certain period due to the penetration of the corrosive media.
基金Project (10037273) supported by the Ministry of Knowledge Economy, Korea
文摘Diffusion bonding between aluminum and copper was performed by vacuum hot pressing at temperatures between 623 and 923 K through two thermal processes： hot compression under the deformation rate of 0.2 mrrdmin for 10 rain at pre-set temperatures, and additional pressing at 0.2 mm/min for 20 rain during furnace cooling. After analyzing interface, the feasible diffusion bonding temperature was suggested as 823 K. The three major intermetallic layers generated during diffusion bonding process were identified as AIECu, AlCu＋AlaCu4 and Al4Cu9. Furthermore, local hardness values ofAlECU, AlCu＋AlaCu4 and Al4Cu9 layers average at （4.97±0.05）, （6.33±0.00） and （6.06±0.18） GPa, respectively.
基金Project(2020JJ2001)supported by Outstanding Youth Scientist Foundation of Hunan Province,ChinaProject(6142912200102)supported by Foundation for National Key Laboratory of Science and Technology on Highstrength Structural Materials,China。
文摘In this paper,15Cr-ODS steels containing 0,1 wt%,2 wt%and 3 wt%Al element were fabricated by combining wet-milling and spark plasma sintering(SPS)methods.The microstructure and mechanical properties of ODS steel were investigated by XRD,SEM,TEM,EBSD and tensile tests.The results demonstrate that the Al addition significantly refines the particle precipitates in the Fe-Cr matrix,leading to the obvious refinement in grain size of matrix and the improvement of mechanical properties.The dispersion particles in ODS steels with Al addition are identified as Al2O3 and Y_(2)Ti_(2)O_(7)nanoparticles,which has a heterogeneous size distribution in the range of 5 nm to 300 nm.Increasing Al addition causes an obvious increase in tensile strength and a decline in elongation.The tensile strength and elongation of 15Cr-ODS steel containing 3 wt%Al are 775.3 MPa and 15.1%,respectively.The existence of Al element improves the corrosion resistance of materials.The ODS steel containing 2 wt%Al shows corrosion potential of 0.39 V and passivation current density of 2.61×10^(−3)A/cm^(2)(1.37 V).This work shows that Al-doped ODS steels prepared by wet-milling and SPS methods have a potential application in structural parts for nuclear system.
基金Supported by the National Natural Science Foundation of China(21376116)A PAPD Project of Jiangsu Higher Education Institution
文摘The flow behavior of pressure-driven water infiltration through graphene-based slit nanopores has been studied by molecular simulation.The simulated flow rate is close to the experimental values,which demonstrates the reasonability of simulation results.Water molecules can spontaneously infiltrate into the nanopores,but an external driving force is generally required to pass through the whole pores.The exit of nanopore has a large obstruction on the water effusion.The flow velocity within the graphene nanochannels does not display monotonous dependence upon the pore width,indicating that the flow is related to the microscopic structures of water confined in the nanopores.Extensive structures of confined water are characterized in order to understand the flow behavior.This simulation improves the understanding of graphene-based nanofluidics,which helps in developing a new type of membrane separation technique.
基金Projects 20060359011 supported by the Doctoral Subject Foundation of the Ministry of Education of China103-037016 by the Technological Innovation Foundation of Hefei University of Technology
文摘Electroless Ni-Fe-P alloy plating on the surface of CNTs was carded out with a bath using citrate salt and lactic acid as complex agents. We proposed a chemical reaction mechanism. The morphology, structure and chemical composition of the Ni-Fe-P/CNTs were studied with the aid of a scanning electronic microscope （SEM）, X-ray diffraction （XRD） and an energy-dispersive X-ray spectral analysis （EDS）. The results show that through a correct pre-treatment and electroless plating, Ni-Fe-P/CNTs composite particles can be obtained. The optimum electroless plating parameters of 35-42℃ and pH of 8.5-9.7 were achieved. The as-plated Ni-Fe-P alloy is amorphous. After a heat treatment at 500℃ for 90 min in H2, the coating is transformed into crystalloid Ni3E Fe2NiP and （Fe,Ni）3R The Ni-Fe-P alloy coating on the surface of CNTs is smooth and unique. The amount of Ni on the surface （mass fraction） of the Ni-Fe-P/CNTs composite particles is 29.13%, that of Fe 3.19% and that of P 2.28%.
基金Project supported by Pusan National University Research GrantProject(2010-0008-276) supported by National Core Research Center Program through the National Research Foundation of Korea funded by the Ministry of Education, Science and Technology
文摘A1203/5%SIC nanocomposites were fabricated by pressureless sintering using MgO as a sintering aid and then post hot-isostatic pressed （HIP）, which can subsequently break through the disadvantage of hot-pressing process. The MgO additive was able to promote the densification of the composites, but could not induce the grain growth of A1203 matrix due to the grain growth inhibition by nano-sized SiC particles. After HIP treatment, A12OJSiC nanocomposites achieved full densification and homogeneous distribution of nano-sized SiC particles. Moreover, the fracture morphology of HIP treated specimens was identical with that of the hot-pressed A1203/SiC nanocomposites showing complete transgranular fracture. Consequently, high fracture strength of 1 GPa was achieved for the A1203/5%SIC nanocomposites by pressureless sintering and post HIP process.