Four different types of three-body model composed of rock and coal with different strength and stiffness were established in order to study the failure characteristics of compound model such as roof-coal-floor. Throug...Four different types of three-body model composed of rock and coal with different strength and stiffness were established in order to study the failure characteristics of compound model such as roof-coal-floor. Through stress analysis of the element with variable strength and stiffness extracted from the strong-weak interface, the tri-axial compressive strength of the weak body and strong body near the interface as well as the areas away from the contact surface was found. Then, on the basis of three-dimensional fast Lagrangian method of continua and strain softening constitutive model composed of Coulomb-Mohr shear failure with tensile cut-off, stress and strain relationship of the four three-body combined models were analyzed under different confining pressures by numerical simulation. Finally, the different features of local shear zones and plastic failure areas of the four different models and their development trend with increasing confining pressure were discussed. The results show that additional stresses are derived due to the lateral deformation constraints near the strong-weak interface area, which results in the strength increasing in weak body and strength decreasing in strong body. The weakly consolidated soft rock and coal cementation exhibit significant strain softening behavior and bear compound tension-shear failure under uni-axial compression. With the increase of confining pressure, the tensile failure disappears from the model, and the failure type of composed model changes to local shear failure with different number of shearing bands and plastic failure zones. This work shows important guiding significance for the mechanism study of seismic, rock burst, and coal bump.展开更多
The microstructure and the associated hardness, strength and electrical conductivity of a new Al-Zn-Mg-Cu alloy during one-step ageing treatment were systematically studied. The results show that the electrical conduc...The microstructure and the associated hardness, strength and electrical conductivity of a new Al-Zn-Mg-Cu alloy during one-step ageing treatment were systematically studied. The results show that the electrical conductivity of the alloy increased continuously with increasing ageing temperature and ageing time. At the early stage of ageing, the hardness and strength of the alloy increased rapidly and then reached the peak value. When aged at 120 °C, the hardness and strength maintained at high level for a long time after the peak value. The main precipitations are GPI zones, GPII zones and metastable η′ phase. GPI and GPII zones are found in the alloy after ageing for 24 h at 120 °C, which indicates that some stable GP zones can exist through the ageing process. When aged at 160 °C, the hardness and strength decreased rapidly after the peak value. The precipitation process is significantly promoted compared with that aged at 120 °C. Both GPI zones and GPII zones disappeared after ageing for 1 h at 160 °C. The main precipitates are η′ phase when aged at 160 °C for 1 h. The main precipitates are η phase when the ageing time prolongs to 24 h.展开更多
The influences of slight amount of B element on the microstructure and properties of AlCoCrFeNiBx high entropy alloys（x = 0,0.01,…,0.09 and 0.1,mole fraction） were investigated.The AlCoCrFeNi high entropy alloy exh...The influences of slight amount of B element on the microstructure and properties of AlCoCrFeNiBx high entropy alloys（x = 0,0.01,…,0.09 and 0.1,mole fraction） were investigated.The AlCoCrFeNi high entropy alloy exhibits equiaxed grain structures with obvious composition segregation.However,with the addition of B element,the alloys exhibit dendrite structures.Inside the dendrites,spinodal decomposition structure can be clearly observed.With the addition of B element,the crystal structures change from（B2 ＋ BCC） to（B2 ＋ BCC ＋ FCC） structures,and the hardness firstly increases from HV 486.7 to HV 502.4,then declines to HV 460.7（x ≥ 0.02）.The compressive fracture strength firstly shows a trend of increasing,and then declining（x ≥ 0.08）.The coercive forces and the specific saturation magnetizations of the alloys decrease as B addition contents increase,the decreasing coercive forces show a better soft magnetic behavior.展开更多
基金Project(51174128)supported by the National Natural Science Foundation of ChinaProject(20123718110007)supported by the Specialized Research Fund for the Doctoral Program of Higher Education of China
文摘Four different types of three-body model composed of rock and coal with different strength and stiffness were established in order to study the failure characteristics of compound model such as roof-coal-floor. Through stress analysis of the element with variable strength and stiffness extracted from the strong-weak interface, the tri-axial compressive strength of the weak body and strong body near the interface as well as the areas away from the contact surface was found. Then, on the basis of three-dimensional fast Lagrangian method of continua and strain softening constitutive model composed of Coulomb-Mohr shear failure with tensile cut-off, stress and strain relationship of the four three-body combined models were analyzed under different confining pressures by numerical simulation. Finally, the different features of local shear zones and plastic failure areas of the four different models and their development trend with increasing confining pressure were discussed. The results show that additional stresses are derived due to the lateral deformation constraints near the strong-weak interface area, which results in the strength increasing in weak body and strength decreasing in strong body. The weakly consolidated soft rock and coal cementation exhibit significant strain softening behavior and bear compound tension-shear failure under uni-axial compression. With the increase of confining pressure, the tensile failure disappears from the model, and the failure type of composed model changes to local shear failure with different number of shearing bands and plastic failure zones. This work shows important guiding significance for the mechanism study of seismic, rock burst, and coal bump.
文摘The microstructure and the associated hardness, strength and electrical conductivity of a new Al-Zn-Mg-Cu alloy during one-step ageing treatment were systematically studied. The results show that the electrical conductivity of the alloy increased continuously with increasing ageing temperature and ageing time. At the early stage of ageing, the hardness and strength of the alloy increased rapidly and then reached the peak value. When aged at 120 °C, the hardness and strength maintained at high level for a long time after the peak value. The main precipitations are GPI zones, GPII zones and metastable η′ phase. GPI and GPII zones are found in the alloy after ageing for 24 h at 120 °C, which indicates that some stable GP zones can exist through the ageing process. When aged at 160 °C, the hardness and strength decreased rapidly after the peak value. The precipitation process is significantly promoted compared with that aged at 120 °C. Both GPI zones and GPII zones disappeared after ageing for 1 h at 160 °C. The main precipitates are η′ phase when aged at 160 °C for 1 h. The main precipitates are η phase when the ageing time prolongs to 24 h.
基金Projects(51134013,51104029,51471044)supported by the National Natural Science Foundation of ChinaProject supported by the Fundamental Research Funds for the Central Universities,China+1 种基金Project(LZ2014007)supported by the Key Laboratory of Basic Research Projects of Liaoning Province Department of Education,ChinaProject(2014028013)supported by the Natural Science Foundation of Liaoning Province,China
文摘The influences of slight amount of B element on the microstructure and properties of AlCoCrFeNiBx high entropy alloys（x = 0,0.01,…,0.09 and 0.1,mole fraction） were investigated.The AlCoCrFeNi high entropy alloy exhibits equiaxed grain structures with obvious composition segregation.However,with the addition of B element,the alloys exhibit dendrite structures.Inside the dendrites,spinodal decomposition structure can be clearly observed.With the addition of B element,the crystal structures change from（B2 ＋ BCC） to（B2 ＋ BCC ＋ FCC） structures,and the hardness firstly increases from HV 486.7 to HV 502.4,then declines to HV 460.7（x ≥ 0.02）.The compressive fracture strength firstly shows a trend of increasing,and then declining（x ≥ 0.08）.The coercive forces and the specific saturation magnetizations of the alloys decrease as B addition contents increase,the decreasing coercive forces show a better soft magnetic behavior.