Two kinds of semi-solid samples of AZ80−0.2Y−0.15Ca(wt.%)(AZ80M)magnesium alloy were prepared by semi-solid isothermal heat treatment of materials with and without equal channel angular pressing(ECAP)process.The micro...Two kinds of semi-solid samples of AZ80−0.2Y−0.15Ca(wt.%)(AZ80M)magnesium alloy were prepared by semi-solid isothermal heat treatment of materials with and without equal channel angular pressing(ECAP)process.The microstructures of initial and semi-solid treated samples were compared and analyzed.The results showed a significant difference in the liquid phase distribution between three-pass ECAP processed(3P)and as-received samples during the isothermal heating process.The semi-solid 3P sample showed a more uniform liquid distribution due to its smaller dihedral angle.Besides,the coarsening processes of solid grains of as-received and 3P samples were dominated by the coalescence and Ostwald ripening mechanism,respectively.The difference of coarsening processes was mainly related to the proportion of the high-angle grain boundaries in materials,which further affected the evolution behavior of the liquid pools.展开更多
Nb tubes were fabricated through hydrostatic extrusion at extrusion ratios of 3.1 and 6.1 at ambient temperature,and then their microstructure,texture,and Vickers hardness were investigated based on electron back-scat...Nb tubes were fabricated through hydrostatic extrusion at extrusion ratios of 3.1 and 6.1 at ambient temperature,and then their microstructure,texture,and Vickers hardness were investigated based on electron back-scattered diffraction(EBSD)data.The fraction of low-angle boundaries(LABs)largely decreased with a sharp decrease in mean grain sizes after hydrostatic extrusion and was not proportional to extrusion ratios,assuming that mixed-asymmetrical junctions forming LABs dissociate at high extrusion ratios from the external stress(>981 MPa)with thermal activation by the generated heat.The correlation between grain size and Vickers hardness followed the Hall−Petch relationship despite the texture gradient of theá111ñcyclic fiber textural microstructure at low extrusion ratios and theá100ñtrue fiber textural microstructure at high extrusion ratios.The increase in hydrostatic pressure on the Nb tubes contributed to texture evolution in terms of extrusion ratios due to the difference between{110}<111>and{112}<111>components based on EBSD data.展开更多
基金supported by Key Development Project of Sichuan Province(Grant No.2017GZ0399)。
文摘Two kinds of semi-solid samples of AZ80−0.2Y−0.15Ca(wt.%)(AZ80M)magnesium alloy were prepared by semi-solid isothermal heat treatment of materials with and without equal channel angular pressing(ECAP)process.The microstructures of initial and semi-solid treated samples were compared and analyzed.The results showed a significant difference in the liquid phase distribution between three-pass ECAP processed(3P)and as-received samples during the isothermal heating process.The semi-solid 3P sample showed a more uniform liquid distribution due to its smaller dihedral angle.Besides,the coarsening processes of solid grains of as-received and 3P samples were dominated by the coalescence and Ostwald ripening mechanism,respectively.The difference of coarsening processes was mainly related to the proportion of the high-angle grain boundaries in materials,which further affected the evolution behavior of the liquid pools.
基金supported by a Grant from the Fundamental R&D Program(10067694)funded by the Ministry of Trade,Industry and Energy,Korea。
文摘Nb tubes were fabricated through hydrostatic extrusion at extrusion ratios of 3.1 and 6.1 at ambient temperature,and then their microstructure,texture,and Vickers hardness were investigated based on electron back-scattered diffraction(EBSD)data.The fraction of low-angle boundaries(LABs)largely decreased with a sharp decrease in mean grain sizes after hydrostatic extrusion and was not proportional to extrusion ratios,assuming that mixed-asymmetrical junctions forming LABs dissociate at high extrusion ratios from the external stress(>981 MPa)with thermal activation by the generated heat.The correlation between grain size and Vickers hardness followed the Hall−Petch relationship despite the texture gradient of theá111ñcyclic fiber textural microstructure at low extrusion ratios and theá100ñtrue fiber textural microstructure at high extrusion ratios.The increase in hydrostatic pressure on the Nb tubes contributed to texture evolution in terms of extrusion ratios due to the difference between{110}<111>and{112}<111>components based on EBSD data.
