With the aim to improve the strength of Al-Zn-Mg-Cu alloy,the alloy billet containing Mn was produced by spray forming method,and the microstructural features were investigated using X-ray diffraction（XRD）,optical m...With the aim to improve the strength of Al-Zn-Mg-Cu alloy,the alloy billet containing Mn was produced by spray forming method,and the microstructural features were investigated using X-ray diffraction（XRD）,optical microscopy（OM）,scanning electron microscopy（SEM）,transmission electron microscopy（TEM） and differential scanning calorimetry（DSC）.The results show that the billet mainly consists of fine equiaxial grains of MgZn2 and Al6Mn with size ranging from 5 μm to 25 μm.Nano-scaled MgZn2 is dispersed in the as-sprayed alloy,primary Al6Mn particles are precipitated at grain boundaries with an average size of 5 μm.A few CuAl2,Al3Zr and eutectic are also found in as-sprayed Al alloy.The volume fraction of the porosity is about 12%.DSC result indicates that most of the solutes are precipitated during spray forming process,and no obviously thermal effects occur below 450 ℃.Both matrix grains and Al6Mn particles grow monotonously with the increase of annealing temperature,but the growth rate of Al6Mn particles is markedly lower than that of Al grains,and the matrix grains grow rapidly when the annealing temperature is above 375 ℃.展开更多
The working principle of LFEC（Low frequency electromagnetic casting） process developed in Northeastern University, China was introduced and the metallurgical results of LFEC were discussed according to the casting p...The working principle of LFEC（Low frequency electromagnetic casting） process developed in Northeastern University, China was introduced and the metallurgical results of LFEC were discussed according to the casting practices. The low frequency field around the mold produces Lorenz force, which can be divided into two parts： one is the potential force which will be balanced by a pressure gradient of the liquid and results in the formation of a convex surface meniscus and improves the surface quality; the other is the rotary force which stirs the liquid in the mold to refine the microstructures and homogenize the distribution of alloying elements. LFEC can refine microstructures remarkably, improve surface quality of the ingots, depress macrosegregation and eliminate cracks. Some new technologies, such as horizontal direct chill casting under low-frequency electromagnetic field （HLEC）, DC casting of hollow billets under electromagnetic fields （HBEC）, electromagnetic modifying of hypereutectic A1-Si alloys（EMM）, air film casting under static magnetic field （AFCM）, and multi-ingots casting under low-frequency magnetic field （MLFEC） were developed based on LFEC.展开更多
The electronic structures of TiAl-2M(M=V, Nb, Ta, Cr, Mo, W,Mn) alloy have been investigated using EHT band calculation method. Their bandstructures and average prperties have been obtained. The results show that dopi...The electronic structures of TiAl-2M(M=V, Nb, Ta, Cr, Mo, W,Mn) alloy have been investigated using EHT band calculation method. Their bandstructures and average prperties have been obtained. The results show that doping thetransition metal elements can effectively change the band structure and enable the alloysystem to show the stronger metallic feature. The dopants of V, Cr and Mn increase s-orbital component of Ti and Al in bonding orbital, therefore, there is more sphericalelectronic clound and weakly directional bonds in the crystal, which improve the duictil-ity of the alloy, Nb or Ta makes stronger bonding with Ti and Al, which improvestrength and oxidation resistance of the alloy.展开更多
基金Project(2006CB605204) supported by the National Basic Research Program of China
文摘With the aim to improve the strength of Al-Zn-Mg-Cu alloy,the alloy billet containing Mn was produced by spray forming method,and the microstructural features were investigated using X-ray diffraction（XRD）,optical microscopy（OM）,scanning electron microscopy（SEM）,transmission electron microscopy（TEM） and differential scanning calorimetry（DSC）.The results show that the billet mainly consists of fine equiaxial grains of MgZn2 and Al6Mn with size ranging from 5 μm to 25 μm.Nano-scaled MgZn2 is dispersed in the as-sprayed alloy,primary Al6Mn particles are precipitated at grain boundaries with an average size of 5 μm.A few CuAl2,Al3Zr and eutectic are also found in as-sprayed Al alloy.The volume fraction of the porosity is about 12%.DSC result indicates that most of the solutes are precipitated during spray forming process,and no obviously thermal effects occur below 450 ℃.Both matrix grains and Al6Mn particles grow monotonously with the increase of annealing temperature,but the growth rate of Al6Mn particles is markedly lower than that of Al grains,and the matrix grains grow rapidly when the annealing temperature is above 375 ℃.
基金Project(2005CB623707) supported by the National Basic Research Program of China Projects(2007CB613701 and 2007CB613702) supported by the National Key Basic Research Program of China+2 种基金Projects(50974037,51004032 and 50904018) supported by the National Natural Science Foundation of ChinaProject(NCET-08-0098) supported by the New Century Excellent Talents in University,Ministry of Education,ChinaProject(20100471468) supported by China Postdoctoral Science Foundation
文摘The working principle of LFEC（Low frequency electromagnetic casting） process developed in Northeastern University, China was introduced and the metallurgical results of LFEC were discussed according to the casting practices. The low frequency field around the mold produces Lorenz force, which can be divided into two parts： one is the potential force which will be balanced by a pressure gradient of the liquid and results in the formation of a convex surface meniscus and improves the surface quality; the other is the rotary force which stirs the liquid in the mold to refine the microstructures and homogenize the distribution of alloying elements. LFEC can refine microstructures remarkably, improve surface quality of the ingots, depress macrosegregation and eliminate cracks. Some new technologies, such as horizontal direct chill casting under low-frequency electromagnetic field （HLEC）, DC casting of hollow billets under electromagnetic fields （HBEC）, electromagnetic modifying of hypereutectic A1-Si alloys（EMM）, air film casting under static magnetic field （AFCM）, and multi-ingots casting under low-frequency magnetic field （MLFEC） were developed based on LFEC.
文摘The electronic structures of TiAl-2M(M=V, Nb, Ta, Cr, Mo, W,Mn) alloy have been investigated using EHT band calculation method. Their bandstructures and average prperties have been obtained. The results show that doping thetransition metal elements can effectively change the band structure and enable the alloysystem to show the stronger metallic feature. The dopants of V, Cr and Mn increase s-orbital component of Ti and Al in bonding orbital, therefore, there is more sphericalelectronic clound and weakly directional bonds in the crystal, which improve the duictil-ity of the alloy, Nb or Ta makes stronger bonding with Ti and Al, which improvestrength and oxidation resistance of the alloy.