In order to enhance the mechanical properties of the selective laser-melted(SLM) high-Mg content AlSiMg1.4 alloy,the Zr element was introduced.The influence of Zr alloying on the processability,microstructure,and mech...In order to enhance the mechanical properties of the selective laser-melted(SLM) high-Mg content AlSiMg1.4 alloy,the Zr element was introduced.The influence of Zr alloying on the processability,microstructure,and mechanical properties of the alloy was systematically investigated through performing microstructure analysis and tensile testing.It was demonstrated that the SLM-fabricated AlSiMg1.4-Zr alloy exhibited high process stability with a relative density of over 99.5% at various process parameters.Besides,the strong grain refinement induced by the primary Al3Zr particle during the melt solidification process simultaneously enhanced both the strength and plasticity of the alloy.The values for the yield strength,ultimate tensile strength,and elongation of the SLM-fabricated AlSiMg1.4-Zr were(343±3) MPa,(485±4) MPa,and(10.2±0.2)%,respectively,demonstrating good strengthplasticity synergy in comparison to the AlSiMg1.4 and other Al-Si-based alloys fabricated by SLM.展开更多
The process of repetitive upsetting-extrusion （RUE） was used to achieve severe plastic deformation （SPD） for an as-cast AZ61 magnesium alloy in temperature range of 285-380 ℃. The microstructure and mechanical pr...The process of repetitive upsetting-extrusion （RUE） was used to achieve severe plastic deformation （SPD） for an as-cast AZ61 magnesium alloy in temperature range of 285-380 ℃. The microstructure and mechanical properties of the as-cast and RUE processed AZ61 alloys were investigated. The results indicated that homogeneous fine-grained structure with mean grain size of 3.5 μm was obtained as the accumulated true strain in the axial direction increased to 4.28 after three RUE passes at 285 ℃. The dominant reason of grain refinement was considered the dynamic recrystallization induced by strain localization. It was also found that the microstructural evolution was affected by temperature and accumulated deformation. The mechanical properties of RUE processed AZ61 alloys were significantly improved owing to grain refinement. Furthermore, the relationship between deformation parameters and mechanical properties of AZ61 alloy prepared by RUE processing was revealed by tensile tests carried out at room temperature.展开更多
The effects of Cu addition on the microstructure and mechanical properties of the as-cast magnesium alloy ZK60 were investigated with optical microscope, SEM, TEM, XRD, EPMA and tensile tester. The mechanism by which ...The effects of Cu addition on the microstructure and mechanical properties of the as-cast magnesium alloy ZK60 were investigated with optical microscope, SEM, TEM, XRD, EPMA and tensile tester. The mechanism by which the mechanical properties are affected by Cu addition was discussed. The results show that Cu can effectively eliminate the intragranular solute segregations in the alloy, and the grain size of the alloy is decreased considerably with increasing the Cu amount. A ternary eutectic phase MgZnCu with a face-centered cubic structure is identified in the Cu-bearing alloys, which predominantly distributes at the grain boundary and acts as the nucleation sites of microcracks during the plastic deformation process. It is also found that the tensile properties of the alloy firstly increase by the trace addition of 0.5%-1%Cu and then decrease by a further addition up to 2.0%.展开更多
The microstructure and mechanical properties of near-eutectic Al-12 Si alloys modified with 0-0.4% Nd（mass fraction） were investigated. The results indicate that a submicro- or nano-sized Al2 Nd phase is observed in...The microstructure and mechanical properties of near-eutectic Al-12 Si alloys modified with 0-0.4% Nd（mass fraction） were investigated. The results indicate that a submicro- or nano-sized Al2 Nd phase is observed in the modified alloy with 0.3% Nd. The morphology of the α（Al） phase is significantly refined in the Nd-modified alloys. The primary Si morphology simultaneously changes into a fine, particle-like morphology, and the morphology of eutectic Si becomes fine-fibrous instead of coarse-acicular. Relatively few growth twins are observed on the surface of the Si plate in the Al-12Si-0.3Nd alloy at the optimal modification level. The mechanical property test results confirm that the mechanical properties of the as-cast Al-12 Si alloys are enhanced after the Nd addition, with optimal ultimate tensile strength（UTS） of 252 MPa and elongation（EL） of 13% at an Nd content of 0.3%. The improved mechanical properties are attributed to the refined morphology of Si phase and the formation of the Al2 Nd phase.展开更多
Al-7.5Si-4Cu cast alloy melt modified by Al-5Ti-B, RE and Al-10Sr master alloys were poured in the chromite sand moulds, to investigate comparatively the effects of individual or combined additions of grain refiners a...Al-7.5Si-4Cu cast alloy melt modified by Al-5Ti-B, RE and Al-10Sr master alloys were poured in the chromite sand moulds, to investigate comparatively the effects of individual or combined additions of grain refiners and modifiers on the mechanical properties, microstructures, grain refining and modification, and intermetallic compounds of the alloy. The results show that the mechanical properties and the microstructures of Al-7.5Si-4Cu cast alloys are improved immensely by combining addition of 0.8%Al-5Ti-B, 0.1%RE and 0.1%Al-10Sr grain refiners and modifiers compared with the individual addition and cast conditions. For individual addition condition, addition of 0.8%Al-5Ti-B master alloy can obtain superior tensile strength, Brinell hardness and finer equiaxedα（Al） dendrites. The alloy with 0.1%RE master alloy shows the highest improvement in ductility because the rare earth can purify the molten metal and change the shape of intermetallic compounds. While the alloy with 0.1%Al-10Sr modifier shows only good improvement in yield strength, and the improvement of other performance is unsatisfactory. The Al-10Sr modifier has a significant metamorphism for the eutectic silicon, but will make the gas content in the aluminum alloy melt increase to form serious columnar grain structures. The effects of grain refining and modification on mean area and aspect ratio have the same conclusions obtained in the mechanical properties and the microstructures analyses.展开更多
The effects of current pulsing on the microstructure, hardness and tensile properties at different temperatures of gas tungsten arc （GTA） weldments of titanium matrix composites were studied. Full-penetration butt j...The effects of current pulsing on the microstructure, hardness and tensile properties at different temperatures of gas tungsten arc （GTA） weldments of titanium matrix composites were studied. Full-penetration butt joints were made with or without current pulsing. Optical microscopy, hardness test and scanning electron microscopy were employed to evaluate the metallurgical characteristics of welded joints. Tensile properties of weldments at different temperatures were studied and correlated with the microstructure. The results exhibit that current pulsing leads to the refinement of the weld microstrucmre and TiB whisker and the redistribution of reinforcements resulting in higher hardness, tensile strength and ductility of weldments in the as-welded condition.展开更多
Objective To compare the characterization and myocardial differentiation capacity of arnniotic fluid-derived mesenchymal stromal cells （AF MSCs） and umbilical cord Wharton＇s Jelly-derived mesenchymal stromal cells ...Objective To compare the characterization and myocardial differentiation capacity of arnniotic fluid-derived mesenchymal stromal cells （AF MSCs） and umbilical cord Wharton＇s Jelly-derived mesenchymal stromal cells （WJ MSCs）. Methods The human AF MSCs were cultured from amniotic fluid samples obtained by amniocentesis. The umbilical cord WJ MSCs were obtained from Wharton＇s Jelly of umbilical cords of infants delivered full-term by normal labor. The morphology, growth curves, and analyses by flow cytometry of cell surface markers were compared between the two types of cells. Myocardial genes （GATA-4, c-TnT, a-actin, and Cx43） were detected by real-time PCR and the corresponding protein expressions were detected by Western blot analysis after myocardial induced in AF MSCs and WJ MSCs. Results Our findings revealed AF MSCs and WJ MSCs shared similar morphological characteristics of the fibroblastoid shape. The AF MSCs were easily obtained than the WJ MSCs and had a shorter time to reach adherence of 2.7 ± 1.6 days to WJ MSCs of 6.5 ± 1.8 days. The growth curves by MTT cytotoxic assay showed the AF MSCs had a similar proliferative capacity at passage 5 and passage 10. However, the proliferative capacities ofWJ MSCs were decreased at 5 passage relative to 10 passage. Both AF stem cells and WJ stem cells had the characteristics of mesenchymal stromal cells with some characteristics of embryonic stem cells. They express CD29 and CD105, but not CD34. They were positive for Class I major histocompatibility （MHC I） antigens （HLA-ABC）, and were negative, or mildly positive, for MHC Class II （HLA-DR） antigen. Oct-4 was positive in all the two cells types. Both AF MSCs and WJ MSCs could differentiate along myocardium. The differentiation capacities were detected by the expression of GATA-4, c-TnT, a-actin, Cx43 after myocardial induction. Conclusions Both AF MSCs and WJ MSCs have the potential clinical application for myogenesis in cardiac regenerative therapy.展开更多
A comparative study of the structure and mechanical behavior of an Al-5 Mg-0.18 Mn-0.2 Sc-0.08 Zr-0.01 Fe-0.01 Si(wt.%)alloy ingot subjected to multidirectional isothermal forging(MIF)to a strain of 12 or equal-channe...A comparative study of the structure and mechanical behavior of an Al-5 Mg-0.18 Mn-0.2 Sc-0.08 Zr-0.01 Fe-0.01 Si(wt.%)alloy ingot subjected to multidirectional isothermal forging(MIF)to a strain of 12 or equal-channel angular pressing(ECAP)to a strain of 10 at 325℃,and subsequent warm and cold rolling(WR and CR)at 325 and 20℃,was performed.The results showed that the MIF process of ultrafine-grained structure with a(sub)grain size dUFG=2μm resulted in enhanced room-temperature ductility and superplastic elongation up to 2800%.Further grain refinement under WR as well as development of a heavily-deformed microstructure with high dislocation density by subsequent CR resulted in a yield/ultimate tensile strength increase from 235/360 MPa after MIF to 315/460 and 400/515 MPa after WR and CR,respectively.Simultaneously,WR led to improved superplastic elongation up to 4000%,while after CR the elongation remained sufficiently high(up to 1500%).Compared with MIF,ECAP resulted in more profound grain refinement(dUFG=1μm),which promoted higher strength and superplastic properties.However,this effect smoothed down upon WR,ensuring equal properties of the processed sheets.CR of the ECAPed alloy,in contrast,led to higher strengthening and slightly better superplastic behavior than those after CR following MIF.展开更多
基金supported by the National Natural Science Foundation of China (Nos.51801079, 52001140)。
文摘In order to enhance the mechanical properties of the selective laser-melted(SLM) high-Mg content AlSiMg1.4 alloy,the Zr element was introduced.The influence of Zr alloying on the processability,microstructure,and mechanical properties of the alloy was systematically investigated through performing microstructure analysis and tensile testing.It was demonstrated that the SLM-fabricated AlSiMg1.4-Zr alloy exhibited high process stability with a relative density of over 99.5% at various process parameters.Besides,the strong grain refinement induced by the primary Al3Zr particle during the melt solidification process simultaneously enhanced both the strength and plasticity of the alloy.The values for the yield strength,ultimate tensile strength,and elongation of the SLM-fabricated AlSiMg1.4-Zr were(343±3) MPa,(485±4) MPa,and(10.2±0.2)%,respectively,demonstrating good strengthplasticity synergy in comparison to the AlSiMg1.4 and other Al-Si-based alloys fabricated by SLM.
基金Project(51075098)supported by the National Natural Science Foundation of ChinaProject(HIT.NSRIF.2014006)supported by the Fundamental Research Funds for the Central Universities,China
文摘The process of repetitive upsetting-extrusion （RUE） was used to achieve severe plastic deformation （SPD） for an as-cast AZ61 magnesium alloy in temperature range of 285-380 ℃. The microstructure and mechanical properties of the as-cast and RUE processed AZ61 alloys were investigated. The results indicated that homogeneous fine-grained structure with mean grain size of 3.5 μm was obtained as the accumulated true strain in the axial direction increased to 4.28 after three RUE passes at 285 ℃. The dominant reason of grain refinement was considered the dynamic recrystallization induced by strain localization. It was also found that the microstructural evolution was affected by temperature and accumulated deformation. The mechanical properties of RUE processed AZ61 alloys were significantly improved owing to grain refinement. Furthermore, the relationship between deformation parameters and mechanical properties of AZ61 alloy prepared by RUE processing was revealed by tensile tests carried out at room temperature.
基金Project(51201088)supported by the National Natural Science Foundation of ChinaProject(12C0324)supported by the Research Foundation of Education Bureau of Hunan Province,China+1 种基金Project(2011XQD26)supported by Doctoral Scientific Research Foundation of University of South,ChinaProject([2011]76)supported by the Construct Program of the Key Discipline in Hunan Province,China
文摘The effects of Cu addition on the microstructure and mechanical properties of the as-cast magnesium alloy ZK60 were investigated with optical microscope, SEM, TEM, XRD, EPMA and tensile tester. The mechanism by which the mechanical properties are affected by Cu addition was discussed. The results show that Cu can effectively eliminate the intragranular solute segregations in the alloy, and the grain size of the alloy is decreased considerably with increasing the Cu amount. A ternary eutectic phase MgZnCu with a face-centered cubic structure is identified in the Cu-bearing alloys, which predominantly distributes at the grain boundary and acts as the nucleation sites of microcracks during the plastic deformation process. It is also found that the tensile properties of the alloy firstly increase by the trace addition of 0.5%-1%Cu and then decrease by a further addition up to 2.0%.
基金Projects(5140521651165032)supported by the National Natural Science Foundation of China+3 种基金Project(20151BAB216018)supported by the Natural Science Foundation of Jiangxi ProvinceChinaProject(GJJ14200)supported by the Education Commission Foundation of Jiangxi ProvinceChina
文摘The microstructure and mechanical properties of near-eutectic Al-12 Si alloys modified with 0-0.4% Nd（mass fraction） were investigated. The results indicate that a submicro- or nano-sized Al2 Nd phase is observed in the modified alloy with 0.3% Nd. The morphology of the α（Al） phase is significantly refined in the Nd-modified alloys. The primary Si morphology simultaneously changes into a fine, particle-like morphology, and the morphology of eutectic Si becomes fine-fibrous instead of coarse-acicular. Relatively few growth twins are observed on the surface of the Si plate in the Al-12Si-0.3Nd alloy at the optimal modification level. The mechanical property test results confirm that the mechanical properties of the as-cast Al-12 Si alloys are enhanced after the Nd addition, with optimal ultimate tensile strength（UTS） of 252 MPa and elongation（EL） of 13% at an Nd content of 0.3%. The improved mechanical properties are attributed to the refined morphology of Si phase and the formation of the Al2 Nd phase.
基金Project (09C26279200863) supported by Technology Innovation Fund Project of High-tech Small and Medium Enterprises,Ministry of Science and Technology of ChinaProject (BA2011084) supported by Special Fund Project on Science and Technology Achievement Transformation of Jiangsu Province,China
文摘Al-7.5Si-4Cu cast alloy melt modified by Al-5Ti-B, RE and Al-10Sr master alloys were poured in the chromite sand moulds, to investigate comparatively the effects of individual or combined additions of grain refiners and modifiers on the mechanical properties, microstructures, grain refining and modification, and intermetallic compounds of the alloy. The results show that the mechanical properties and the microstructures of Al-7.5Si-4Cu cast alloys are improved immensely by combining addition of 0.8%Al-5Ti-B, 0.1%RE and 0.1%Al-10Sr grain refiners and modifiers compared with the individual addition and cast conditions. For individual addition condition, addition of 0.8%Al-5Ti-B master alloy can obtain superior tensile strength, Brinell hardness and finer equiaxedα（Al） dendrites. The alloy with 0.1%RE master alloy shows the highest improvement in ductility because the rare earth can purify the molten metal and change the shape of intermetallic compounds. While the alloy with 0.1%Al-10Sr modifier shows only good improvement in yield strength, and the improvement of other performance is unsatisfactory. The Al-10Sr modifier has a significant metamorphism for the eutectic silicon, but will make the gas content in the aluminum alloy melt increase to form serious columnar grain structures. The effects of grain refining and modification on mean area and aspect ratio have the same conclusions obtained in the mechanical properties and the microstructures analyses.
基金Project(51371114)supported by the National Natural Science Foundation of ChinaProject(2012CB619600)supported by the National Basic Research Program of China+1 种基金Project(10SG15)supported by the Dawn Program of Shanghai Education Commission,ChinaProject(12XD1402800)supported by Shanghai Science and Technology Committee,China
文摘The effects of current pulsing on the microstructure, hardness and tensile properties at different temperatures of gas tungsten arc （GTA） weldments of titanium matrix composites were studied. Full-penetration butt joints were made with or without current pulsing. Optical microscopy, hardness test and scanning electron microscopy were employed to evaluate the metallurgical characteristics of welded joints. Tensile properties of weldments at different temperatures were studied and correlated with the microstructure. The results exhibit that current pulsing leads to the refinement of the weld microstrucmre and TiB whisker and the redistribution of reinforcements resulting in higher hardness, tensile strength and ductility of weldments in the as-welded condition.
文摘Objective To compare the characterization and myocardial differentiation capacity of arnniotic fluid-derived mesenchymal stromal cells （AF MSCs） and umbilical cord Wharton＇s Jelly-derived mesenchymal stromal cells （WJ MSCs）. Methods The human AF MSCs were cultured from amniotic fluid samples obtained by amniocentesis. The umbilical cord WJ MSCs were obtained from Wharton＇s Jelly of umbilical cords of infants delivered full-term by normal labor. The morphology, growth curves, and analyses by flow cytometry of cell surface markers were compared between the two types of cells. Myocardial genes （GATA-4, c-TnT, a-actin, and Cx43） were detected by real-time PCR and the corresponding protein expressions were detected by Western blot analysis after myocardial induced in AF MSCs and WJ MSCs. Results Our findings revealed AF MSCs and WJ MSCs shared similar morphological characteristics of the fibroblastoid shape. The AF MSCs were easily obtained than the WJ MSCs and had a shorter time to reach adherence of 2.7 ± 1.6 days to WJ MSCs of 6.5 ± 1.8 days. The growth curves by MTT cytotoxic assay showed the AF MSCs had a similar proliferative capacity at passage 5 and passage 10. However, the proliferative capacities ofWJ MSCs were decreased at 5 passage relative to 10 passage. Both AF stem cells and WJ stem cells had the characteristics of mesenchymal stromal cells with some characteristics of embryonic stem cells. They express CD29 and CD105, but not CD34. They were positive for Class I major histocompatibility （MHC I） antigens （HLA-ABC）, and were negative, or mildly positive, for MHC Class II （HLA-DR） antigen. Oct-4 was positive in all the two cells types. Both AF MSCs and WJ MSCs could differentiate along myocardium. The differentiation capacities were detected by the expression of GATA-4, c-TnT, a-actin, Cx43 after myocardial induction. Conclusions Both AF MSCs and WJ MSCs have the potential clinical application for myogenesis in cardiac regenerative therapy.
基金financial supports from the Russian Science Foundation under grant No.16-19-10152P(the alloy MIF processing and room-temperature mechanical testing)by the Ministry of Science and Higher Education of Russia under the state assignment of IMSP RAS(ECAP and analysis of superplasticity).
文摘A comparative study of the structure and mechanical behavior of an Al-5 Mg-0.18 Mn-0.2 Sc-0.08 Zr-0.01 Fe-0.01 Si(wt.%)alloy ingot subjected to multidirectional isothermal forging(MIF)to a strain of 12 or equal-channel angular pressing(ECAP)to a strain of 10 at 325℃,and subsequent warm and cold rolling(WR and CR)at 325 and 20℃,was performed.The results showed that the MIF process of ultrafine-grained structure with a(sub)grain size dUFG=2μm resulted in enhanced room-temperature ductility and superplastic elongation up to 2800%.Further grain refinement under WR as well as development of a heavily-deformed microstructure with high dislocation density by subsequent CR resulted in a yield/ultimate tensile strength increase from 235/360 MPa after MIF to 315/460 and 400/515 MPa after WR and CR,respectively.Simultaneously,WR led to improved superplastic elongation up to 4000%,while after CR the elongation remained sufficiently high(up to 1500%).Compared with MIF,ECAP resulted in more profound grain refinement(dUFG=1μm),which promoted higher strength and superplastic properties.However,this effect smoothed down upon WR,ensuring equal properties of the processed sheets.CR of the ECAPed alloy,in contrast,led to higher strengthening and slightly better superplastic behavior than those after CR following MIF.