In order to clean production of chromium compounds, it is a critical process to remove aluminates and utilize aluminum compounds from artificial chromate alkali solutions. The effects of Na2 Cr O4 on the neutralizatio...In order to clean production of chromium compounds, it is a critical process to remove aluminates and utilize aluminum compounds from artificial chromate alkali solutions. The effects of Na2 Cr O4 on the neutralization curve, Al（OH）3 precipitation efficiency and induction period of bayerite were investigated. The results indicate that the neutralization curve of the artificial chromate alkali solutions shows three distinct regions and its induction period is longer than that of pure sodium aluminate solutions at the same aluminum concentration. And the decreased temperature and volume fraction of CO2 enhance the particle size of bayerite β-Al（OH）3. Bayerite composed of agglomerates of rods and cone frustums was obtained from alkali metal chromate solutions with 28.5% CO2（volume fraction） at temperatures ranging from 50 °C to 70 °C. Coarse bayerite with particle size（d50） from 24.2 μm to 29.3 μm extremely has few impurities, which is suitable for comprehensive utilization.展开更多
Calcium carbonate was synthesized in a CaCl2/NaCO3 mixed solution by using ethylenediaminetetraacetic acid （EDTA） as an additive. The thermodynamics and kinetics analyses indicate that although the driving force of ...Calcium carbonate was synthesized in a CaCl2/NaCO3 mixed solution by using ethylenediaminetetraacetic acid （EDTA） as an additive. The thermodynamics and kinetics analyses indicate that although the driving force of amorphous calcium carbonate （ACC） precipitation is always less than that of calcite and vaterite precipitation, the nucleation rate of ACC is greater than that of calcite and vaterite at the initial stage of the precipitation reaction. With the increasing incubation time, vaterite and calcite particles nucleate heterogeneously by using the as-formed particles as active sites. Scanning electron microscopy images indicate that the transformation mechanism of ACC and vaterite to calcite is the dissolution-recrystallisation reaction. The presence of EDTA not only improves the stabilities of ACC and vaterite, but also leads to forming enlongated, connected rhombohedral calcite crystals after incubation 7 days in solutions. The ACC and vaterite are stabler in air than in solutions at room temperature, although the dissolution-recrystallisation reaction occurs on the surface.展开更多
Structure and polarity of the Si C single crystal have been analyzed with the four- circle X- ray diffraction method by a double- crystal diffractom eter.The hexagonal{ 10 15 } pole figure shows that this Si C sam pl...Structure and polarity of the Si C single crystal have been analyzed with the four- circle X- ray diffraction method by a double- crystal diffractom eter.The hexagonal{ 10 15 } pole figure shows that this Si C sam ple has a6 H modification.The difference between the integrated intensities m easured byω scan in the triple- axis diffraction set- up finds some convincing evidence that the surface is either a Si- terminated face or C- terminated face.The experi- mental ratios of| F( 0 0 0 L) | 2 / | F( 0 0 0 L) | 2 are in good agreem entwith the calculated ones after the dispersion cor- rections to the atomic scattering factors( L=6 ,12 and18,respectively) .Thus,this m easurem ent technique is con- venient for the application of the materials with remarkable surface polarity.展开更多
The hot deformation behavior of GH3535 superalloy was investigated by hot compression tests in the temperature range of 1000-1200 °C and strain rate range of 0.01-50 s-1. The activation energy is about 356.3 k J/...The hot deformation behavior of GH3535 superalloy was investigated by hot compression tests in the temperature range of 1000-1200 °C and strain rate range of 0.01-50 s-1. The activation energy is about 356.3 k J/mol, and the flow curves and processing map were developed on the basis of experimental data. The processing map exhibits a stable domain which occurs in the strain rate range of 0.01-1 s-1 at all the temperatures and a instable domain which occurs in the strain rate range of 1-50 s-1. Microstructural observations reveal that the full dynamic recrystallization（DRX） occurs in the conditions of（1150 °C, 0.01 s-1）,（1200 °C, 0.01 s-1） and（1200 °C, 0.1 s-1） with different grain sizes and undissolved carbides. The flow localization and cracks occur in the regime of flow instability.展开更多
The Na2CO3-modified HZSM-5 zeolites were further treated by tetrapropylammonium hydroxide(TPAOH) solution. The effect of TPAOH concentration on the secondary crystallization process was investigated. The resulting sam...The Na2CO3-modified HZSM-5 zeolites were further treated by tetrapropylammonium hydroxide(TPAOH) solution. The effect of TPAOH concentration on the secondary crystallization process was investigated. The resulting samples were characterized by a complementary combination of X-ray diffraction, N2 adsorption/desorption, scanning electron microscopy, X-ray fluorescence spectroscopy, XPS, 27 Al and 29 Si magic-angle spinning nuclear magnetic resonance spectroscopy, BET and temperature-programmed desorption techniques. The results showed that the secondary crystallization of the HZSM-5 zeolite could result in migration of non-framework species from the internal channels to the zeolite surface and their transformation into framework species. The catalytic activity of these modified samples for thiophene alkylation was evaluated. Both the activity and stability of the catalysts were improved after secondary crystallization.展开更多
基金Project(51125018)supported by the National Science Found for Distinguished Young Scholars of ChinaProject(2011BAC06B07)supported by the National Key Technologies R&D Program of China+2 种基金Project(2011AA060704)supported by the National Hi-tech Research and Development Program of ChinaProjects(51204153,21106167)supported by the National Natural Science Foundation of ChinaProjects(2012M510552,2013T60175)supported by Financial Grant from the China Postdoctoral Science Foundation
文摘In order to clean production of chromium compounds, it is a critical process to remove aluminates and utilize aluminum compounds from artificial chromate alkali solutions. The effects of Na2 Cr O4 on the neutralization curve, Al（OH）3 precipitation efficiency and induction period of bayerite were investigated. The results indicate that the neutralization curve of the artificial chromate alkali solutions shows three distinct regions and its induction period is longer than that of pure sodium aluminate solutions at the same aluminum concentration. And the decreased temperature and volume fraction of CO2 enhance the particle size of bayerite β-Al（OH）3. Bayerite composed of agglomerates of rods and cone frustums was obtained from alkali metal chromate solutions with 28.5% CO2（volume fraction） at temperatures ranging from 50 °C to 70 °C. Coarse bayerite with particle size（d50） from 24.2 μm to 29.3 μm extremely has few impurities, which is suitable for comprehensive utilization.
文摘Calcium carbonate was synthesized in a CaCl2/NaCO3 mixed solution by using ethylenediaminetetraacetic acid （EDTA） as an additive. The thermodynamics and kinetics analyses indicate that although the driving force of amorphous calcium carbonate （ACC） precipitation is always less than that of calcite and vaterite precipitation, the nucleation rate of ACC is greater than that of calcite and vaterite at the initial stage of the precipitation reaction. With the increasing incubation time, vaterite and calcite particles nucleate heterogeneously by using the as-formed particles as active sites. Scanning electron microscopy images indicate that the transformation mechanism of ACC and vaterite to calcite is the dissolution-recrystallisation reaction. The presence of EDTA not only improves the stabilities of ACC and vaterite, but also leads to forming enlongated, connected rhombohedral calcite crystals after incubation 7 days in solutions. The ACC and vaterite are stabler in air than in solutions at room temperature, although the dissolution-recrystallisation reaction occurs on the surface.
文摘Structure and polarity of the Si C single crystal have been analyzed with the four- circle X- ray diffraction method by a double- crystal diffractom eter.The hexagonal{ 10 15 } pole figure shows that this Si C sam ple has a6 H modification.The difference between the integrated intensities m easured byω scan in the triple- axis diffraction set- up finds some convincing evidence that the surface is either a Si- terminated face or C- terminated face.The experi- mental ratios of| F( 0 0 0 L) | 2 / | F( 0 0 0 L) | 2 are in good agreem entwith the calculated ones after the dispersion cor- rections to the atomic scattering factors( L=6 ,12 and18,respectively) .Thus,this m easurem ent technique is con- venient for the application of the materials with remarkable surface polarity.
基金Project(XDA02040000)supported by the Strategic Priority Research Program of the Chinese Academy of Sciences
文摘The hot deformation behavior of GH3535 superalloy was investigated by hot compression tests in the temperature range of 1000-1200 °C and strain rate range of 0.01-50 s-1. The activation energy is about 356.3 k J/mol, and the flow curves and processing map were developed on the basis of experimental data. The processing map exhibits a stable domain which occurs in the strain rate range of 0.01-1 s-1 at all the temperatures and a instable domain which occurs in the strain rate range of 1-50 s-1. Microstructural observations reveal that the full dynamic recrystallization（DRX） occurs in the conditions of（1150 °C, 0.01 s-1）,（1200 °C, 0.01 s-1） and（1200 °C, 0.1 s-1） with different grain sizes and undissolved carbides. The flow localization and cracks occur in the regime of flow instability.
基金the financial support by the Natural Science Foundation of Liaoning Province of China (Grant No.201202126)the National Natural Science Foundation of China (Grant Nos. 21276253 and 21401093)
文摘The Na2CO3-modified HZSM-5 zeolites were further treated by tetrapropylammonium hydroxide(TPAOH) solution. The effect of TPAOH concentration on the secondary crystallization process was investigated. The resulting samples were characterized by a complementary combination of X-ray diffraction, N2 adsorption/desorption, scanning electron microscopy, X-ray fluorescence spectroscopy, XPS, 27 Al and 29 Si magic-angle spinning nuclear magnetic resonance spectroscopy, BET and temperature-programmed desorption techniques. The results showed that the secondary crystallization of the HZSM-5 zeolite could result in migration of non-framework species from the internal channels to the zeolite surface and their transformation into framework species. The catalytic activity of these modified samples for thiophene alkylation was evaluated. Both the activity and stability of the catalysts were improved after secondary crystallization.