The recrystallization and softening resistance of a Cu-6.5Fe-0.3Mg(mass fraction,%)alloy prepared by Process 1(cold rolling heat treatment)and Process 2(hot/cold rolling heat treatment)were studied using Vickers hardn...The recrystallization and softening resistance of a Cu-6.5Fe-0.3Mg(mass fraction,%)alloy prepared by Process 1(cold rolling heat treatment)and Process 2(hot/cold rolling heat treatment)were studied using Vickers hardness tests,tensile tests,scanning electron microscopy and transmission electron microscopy.The softening temperature,hardness and tensile strength of the alloy prepared by Process 2 were 110°C,HV 15 and 114 MPa higher,respectively,than those of the alloy prepared by Process 1 after aging at 300°C.The recrystallization activation energy of the alloys prepared by Process 1 and Process 2 were 72.83 and 98.11 kJ/mol,respectively.The pinning effects of the precipitates of the two alloys on grain boundaries and dislocations were basically the same.The softening mechanism was mainly attributed to the loss of dislocation strengthening.The higher Fe fiber density inhibited the average free migration path of dislocations and grain boundary migration in the alloy,which was the main reason for higher softening temperature of the alloy prepared by Process 2.展开更多
In order to study the effect of dynamic recrystallization on the metal flow behavior during thermal deformation,the elevated temperature compression experiments of CuCrZr alloy and 35CrMo steel are carried out using G...In order to study the effect of dynamic recrystallization on the metal flow behavior during thermal deformation,the elevated temperature compression experiments of CuCrZr alloy and 35CrMo steel are carried out using Gleeble-3810 thermal simulator.It is proved that the samples underwent obvious dynamic recrystallization behavior during thermal deformation by microstructure observation of deformed specimens.The size of recrystallized grains increases as the temperature improved and the strain rate decreased.Meanwhile,the net softening rate caused by dynamic recrystallization is determined based on the stress-dislocation relationship.It can be found that the value of net softening rate increases quadratically as the Z parameter decreases,and the dynamic recrystallization net softening rate of CuCrZr alloy and 35CrMo steel are calculated to be 21.9%and 29.8%,respectively.Based on the dynamic recrystallization softening effect proposed,the novel elevated temperature flow constitutive models of two different alloys are proposed,and the related parameters are well defined and solved in detail.The predicted values of the obtained models are agreed well with the experimental values.展开更多
The restoration mechanisms for static recrystallization of work-hardened austenite were investigated by using double-pass compression tests performed on medium-carbon steel containing chromium and molybdenum. The soft...The restoration mechanisms for static recrystallization of work-hardened austenite were investigated by using double-pass compression tests performed on medium-carbon steel containing chromium and molybdenum. The softening fraction was defined by 2% offset method. The results show that Avrami exponent of about 0.21 is insensitive to deformation temperature, indicating that the action of steel grade should be considered. The time of 50% recrystallization (t0.5) decreases noteworthily with the increase of deformation temperature. Apparent activation energy for static recrystallization of 195 kJ/mol, which is close to that of vanadium microalloyed steel, is obtained by calculating. The increasing trend of the driving force for recrystallization is opposite to that of the deformation temperature, which is attributed to the number of operative slip system increasing as temperature increasing.展开更多
Colloidal boehmite particles have been included into a polyethylene terephthalate matrix by in situ polymerization. Boehmite nanoparticles were produced by the controlled hydrolysis of aluminium isopropylate. The nano...Colloidal boehmite particles have been included into a polyethylene terephthalate matrix by in situ polymerization. Boehmite nanoparticles were produced by the controlled hydrolysis of aluminium isopropylate. The nanoparticles were characterized using Transmitted Electronic Microscopy (TEM) and X-ray Diffraction (XRD), which revealed the particles of magnitude about 10 nm. The particles have been used without any surface modification. Characterization of the nanocomposite has been carried out using TEM and differential scanning calorimetry (DSC). TEM images indicate that the particles have been homogeneously dispersed in the polymer. DSC results show that the presence of boehmite affects the process of crystallization of polyethylene terephthalate.展开更多
Hot deformation behaviors and microstructure evolution of Ti-3Al-5Mo-4Cr-2Zr-1Fe(Ti-35421)alloy in theβsingle field are investigated by isothermal compression tests on a Gleeble-3500 simulator at temperatures of 820-...Hot deformation behaviors and microstructure evolution of Ti-3Al-5Mo-4Cr-2Zr-1Fe(Ti-35421)alloy in theβsingle field are investigated by isothermal compression tests on a Gleeble-3500 simulator at temperatures of 820-900°C and strain rates of 0.001-1 s^(-1).The research results show that discontinuous yield phenomenon and rheological softening are affected by the strain rates and deformation temperatures.The critical conditions for dynamic recrystallization and kinetic model of Ti-35421 alloy are determined,and the Arrhenius constitutive model is constructed.The rheological behaviors of Ti-35421 alloys aboveβphase transformation temperature are predicted by the constitutive model accurately.The EBSD analysis proves that the deformation softening is controlled by dynamic recovery and dynamic recrystallization.In addition,continuous dynamic recrystallization is determined during hot deformation,and the calculation model for recrystallization grain sizes is established.Good linear dependency between the experimental and simulated values of recrystallized grain sizes indicates that the present model can be used for the prediction of recrystallized grain size with high accuracy.展开更多
基金financial supports from the Department of Science and Technology and other Provincial and Ministerial Level Projects,China(No.204306800086)Science and Technology Projects of Ganzhou Science and Technology Bureau,China(No.204301000194)the Science and Technology Project of Jiangxi Provincial Department of Education,China(No.204201400853)。
文摘The recrystallization and softening resistance of a Cu-6.5Fe-0.3Mg(mass fraction,%)alloy prepared by Process 1(cold rolling heat treatment)and Process 2(hot/cold rolling heat treatment)were studied using Vickers hardness tests,tensile tests,scanning electron microscopy and transmission electron microscopy.The softening temperature,hardness and tensile strength of the alloy prepared by Process 2 were 110°C,HV 15 and 114 MPa higher,respectively,than those of the alloy prepared by Process 1 after aging at 300°C.The recrystallization activation energy of the alloys prepared by Process 1 and Process 2 were 72.83 and 98.11 kJ/mol,respectively.The pinning effects of the precipitates of the two alloys on grain boundaries and dislocations were basically the same.The softening mechanism was mainly attributed to the loss of dislocation strengthening.The higher Fe fiber density inhibited the average free migration path of dislocations and grain boundary migration in the alloy,which was the main reason for higher softening temperature of the alloy prepared by Process 2.
基金Project(2019zzts525)supported by the Fundamental Research Funds for the Central Universities,ChinaProjects(U1837207,U1637601)supported by the National Natural Science Foundation of China
文摘In order to study the effect of dynamic recrystallization on the metal flow behavior during thermal deformation,the elevated temperature compression experiments of CuCrZr alloy and 35CrMo steel are carried out using Gleeble-3810 thermal simulator.It is proved that the samples underwent obvious dynamic recrystallization behavior during thermal deformation by microstructure observation of deformed specimens.The size of recrystallized grains increases as the temperature improved and the strain rate decreased.Meanwhile,the net softening rate caused by dynamic recrystallization is determined based on the stress-dislocation relationship.It can be found that the value of net softening rate increases quadratically as the Z parameter decreases,and the dynamic recrystallization net softening rate of CuCrZr alloy and 35CrMo steel are calculated to be 21.9%and 29.8%,respectively.Based on the dynamic recrystallization softening effect proposed,the novel elevated temperature flow constitutive models of two different alloys are proposed,and the related parameters are well defined and solved in detail.The predicted values of the obtained models are agreed well with the experimental values.
文摘The restoration mechanisms for static recrystallization of work-hardened austenite were investigated by using double-pass compression tests performed on medium-carbon steel containing chromium and molybdenum. The softening fraction was defined by 2% offset method. The results show that Avrami exponent of about 0.21 is insensitive to deformation temperature, indicating that the action of steel grade should be considered. The time of 50% recrystallization (t0.5) decreases noteworthily with the increase of deformation temperature. Apparent activation energy for static recrystallization of 195 kJ/mol, which is close to that of vanadium microalloyed steel, is obtained by calculating. The increasing trend of the driving force for recrystallization is opposite to that of the deformation temperature, which is attributed to the number of operative slip system increasing as temperature increasing.
基金Supported by Ningbo Natural Science Foundation (No.2006A610067)
文摘Colloidal boehmite particles have been included into a polyethylene terephthalate matrix by in situ polymerization. Boehmite nanoparticles were produced by the controlled hydrolysis of aluminium isopropylate. The nanoparticles were characterized using Transmitted Electronic Microscopy (TEM) and X-ray Diffraction (XRD), which revealed the particles of magnitude about 10 nm. The particles have been used without any surface modification. Characterization of the nanocomposite has been carried out using TEM and differential scanning calorimetry (DSC). TEM images indicate that the particles have been homogeneously dispersed in the polymer. DSC results show that the presence of boehmite affects the process of crystallization of polyethylene terephthalate.
基金the financial supports from the National Natural Science Foundation of China (Nos. 52001163, 52075237)the Primary Research and Development Plan of Jiangsu Province, China (No. BE2019119)
文摘Hot deformation behaviors and microstructure evolution of Ti-3Al-5Mo-4Cr-2Zr-1Fe(Ti-35421)alloy in theβsingle field are investigated by isothermal compression tests on a Gleeble-3500 simulator at temperatures of 820-900°C and strain rates of 0.001-1 s^(-1).The research results show that discontinuous yield phenomenon and rheological softening are affected by the strain rates and deformation temperatures.The critical conditions for dynamic recrystallization and kinetic model of Ti-35421 alloy are determined,and the Arrhenius constitutive model is constructed.The rheological behaviors of Ti-35421 alloys aboveβphase transformation temperature are predicted by the constitutive model accurately.The EBSD analysis proves that the deformation softening is controlled by dynamic recovery and dynamic recrystallization.In addition,continuous dynamic recrystallization is determined during hot deformation,and the calculation model for recrystallization grain sizes is established.Good linear dependency between the experimental and simulated values of recrystallized grain sizes indicates that the present model can be used for the prediction of recrystallized grain size with high accuracy.