This paper describes the analysis of the thermal stress concentration and the effects of geometrical shape in the interfacial edge by FEM. It is shown that the elevated stress in a dissim...This paper describes the analysis of the thermal stress concentration and the effects of geometrical shape in the interfacial edge by FEM. It is shown that the elevated stress in a dissimilar material caused by temperature is only restricted in a minor region of the interfacial edge, where the stress peak value and and the stress gradient are high. It is also found that narrowing the boundary angle can effectively reduce the peak value of stress components on the interfacial layer, especially the peeling stress σ y , which is a condition of the debonding failure in the interface.θ=60, an obvious variation, proves that selecting a reasonable edge geometrical shape helps to reduce the value of the maximum stress. At last the methods of relaxing stress concentration and effects of the geometric blunt are also discussed.展开更多
In order to analyze the origin of carbon monoxide(CO) in coal seams, stress–strain experiments under temperature of 50, 150 and 250 °C were conducted using lignite from Kailuan mining area. Fourier transform inf...In order to analyze the origin of carbon monoxide(CO) in coal seams, stress–strain experiments under temperature of 50, 150 and 250 °C were conducted using lignite from Kailuan mining area. Fourier transform infrared spectroscopy and elemental analysis were carried out before and after deformation of the samples. The results indicated that CO generated at 150 and 250 °C; the gas component was mostly oxygen(O_2), with small amount of carbon dioxide(CO_2), methane(CH_4) and hydrogen(H_2). At 50 °C, O_2 and a little CO_2 were observed and no CO was found. The carbon content of the coal samples increased slightly after deformation, and the oxygen content, H/C ratio, and O/C ratio decreased. The molecular structure of coal displayed different evolution characteristics at various temperatures. At 50 and 150 °C, the falling off of side chains, broken of ether bond and directional realignment of the aliphatic chains resulting in the formation of long chains were the main performance of coal molecular structure evolution. While at 250 °C, the side chains fell off and short chains formed. Furthermore, at both 150 and 250 °C, condensed degree of aromatic ring increased. Under the action of temperature and pressure, CO forms in two ways.The first is that ether bond breaks, oxygen and carbon atoms combine together and forms CO, or O_2 forming in the broken of ether–oxygen bond leads to the oxidation of free radicals and resulting in the formation of CO. And the second is that CO derives from falling off of C=O group.展开更多
文摘This paper describes the analysis of the thermal stress concentration and the effects of geometrical shape in the interfacial edge by FEM. It is shown that the elevated stress in a dissimilar material caused by temperature is only restricted in a minor region of the interfacial edge, where the stress peak value and and the stress gradient are high. It is also found that narrowing the boundary angle can effectively reduce the peak value of stress components on the interfacial layer, especially the peeling stress σ y , which is a condition of the debonding failure in the interface.θ=60, an obvious variation, proves that selecting a reasonable edge geometrical shape helps to reduce the value of the maximum stress. At last the methods of relaxing stress concentration and effects of the geometric blunt are also discussed.
基金financial support from the National Science foundation of China(No.41430317)the Discipline Innovative Engineering Plan sponsored by the Ministry of Education of China+1 种基金the State Administration of Foreign Experts Affairs of China(No.13023)the Priority Academic Program Development of Jiangsu Higher Education Institutions
文摘In order to analyze the origin of carbon monoxide(CO) in coal seams, stress–strain experiments under temperature of 50, 150 and 250 °C were conducted using lignite from Kailuan mining area. Fourier transform infrared spectroscopy and elemental analysis were carried out before and after deformation of the samples. The results indicated that CO generated at 150 and 250 °C; the gas component was mostly oxygen(O_2), with small amount of carbon dioxide(CO_2), methane(CH_4) and hydrogen(H_2). At 50 °C, O_2 and a little CO_2 were observed and no CO was found. The carbon content of the coal samples increased slightly after deformation, and the oxygen content, H/C ratio, and O/C ratio decreased. The molecular structure of coal displayed different evolution characteristics at various temperatures. At 50 and 150 °C, the falling off of side chains, broken of ether bond and directional realignment of the aliphatic chains resulting in the formation of long chains were the main performance of coal molecular structure evolution. While at 250 °C, the side chains fell off and short chains formed. Furthermore, at both 150 and 250 °C, condensed degree of aromatic ring increased. Under the action of temperature and pressure, CO forms in two ways.The first is that ether bond breaks, oxygen and carbon atoms combine together and forms CO, or O_2 forming in the broken of ether–oxygen bond leads to the oxidation of free radicals and resulting in the formation of CO. And the second is that CO derives from falling off of C=O group.