In order to study the influence of parameters on durability of marine concrete structures, the parameter＇s sensitivity analysis was studied in this paper. With the Fick＇s 2nd law of diffusion and the deterministic s...In order to study the influence of parameters on durability of marine concrete structures, the parameter＇s sensitivity analysis was studied in this paper. With the Fick＇s 2nd law of diffusion and the deterministic sensitivity analysis method （DSA）, the sensitivity factors of apparent surface chloride content, apparent chloride diffusion coefficient and its time dependent attenuation factor were analyzed. The results of the analysis show that the impact of design variables on concrete durability was different. The values of sensitivity factor of chloride diffusion coefficient and its time dependent attenuation factor were higher than others. Relative less error in chloride diffusion coefficient and its time dependent attenuation coefficient induces a bigger error in concrete durability design and life prediction. According to probability sensitivity analysis （PSA）, the influence of mean value and variance of concrete durability design variables on the durability failure probability was studied. The results of the study provide quantitative measures of the importance of concrete durability design and life prediction variables. It was concluded that the chloride diffusion coefficient and its time dependent attenuation factor have more influence on the reliability of marine concrete structural durability. In durability design and life prediction of marine concrete structures, it was very important to reduce the measure and statistic error of durability design variables.展开更多
To accurately evaluate the degradation process of prestressed concrete continuous bridges exposed to aggressive environments in life-cycle,a finite element-based approach with respect to the lifetime performance asses...To accurately evaluate the degradation process of prestressed concrete continuous bridges exposed to aggressive environments in life-cycle,a finite element-based approach with respect to the lifetime performance assessment of concrete bridges was proposed.The existing assessment methods were firstly introduced and compared.Some essential mechanics problems involved in the degradation process,such as the deterioration of materials properties,the reduction of sectional areas and the variation of overall structural performance caused by the first two problems,were investigated and solved.A computer program named CBDAS(Concrete Bridge Durability Analysis System) was written to perform the above-metioned approach.Finally,the degradation process of a prestressed concrete continuous bridge under chloride penetration was discussed.The results show that the concrete normal stress for serviceability limit state exceeds the threshold value after 60 a,but the various performance indicators at ultimate limit state are consistently in the allowable level during service life.Therefore,in the case of prestressed concrete bridges,the serviceability limit state is more possible to have durability problems in life-cycle;however,the performance indicators at ultimate limit state can satisfy the requirements.展开更多
Stress ribbon bridges have many advantages and became recently more popular mostly because of their versatile form, slender decks giving a light aesthetic impression and durability assured by post tensioned concrete. ...Stress ribbon bridges have many advantages and became recently more popular mostly because of their versatile form, slender decks giving a light aesthetic impression and durability assured by post tensioned concrete. The paper presents the first in Poland stress Ribbon Bridge constructed last year. A static and dynamic analyse of the model is presented as well as construction solutions which were used to achieve the highest durability. The bridge was checked during static and dynamic load test. The results of this prove test were compared with results obtained from examination and study of other different bridge structures. It confirmed that the bridge has good dynamic resistance and greater stiffness than assumed in the design.展开更多
文摘In order to study the influence of parameters on durability of marine concrete structures, the parameter＇s sensitivity analysis was studied in this paper. With the Fick＇s 2nd law of diffusion and the deterministic sensitivity analysis method （DSA）, the sensitivity factors of apparent surface chloride content, apparent chloride diffusion coefficient and its time dependent attenuation factor were analyzed. The results of the analysis show that the impact of design variables on concrete durability was different. The values of sensitivity factor of chloride diffusion coefficient and its time dependent attenuation factor were higher than others. Relative less error in chloride diffusion coefficient and its time dependent attenuation coefficient induces a bigger error in concrete durability design and life prediction. According to probability sensitivity analysis （PSA）, the influence of mean value and variance of concrete durability design variables on the durability failure probability was studied. The results of the study provide quantitative measures of the importance of concrete durability design and life prediction variables. It was concluded that the chloride diffusion coefficient and its time dependent attenuation factor have more influence on the reliability of marine concrete structural durability. In durability design and life prediction of marine concrete structures, it was very important to reduce the measure and statistic error of durability design variables.
基金Project(2006.318.223.02-01) supported by the Ministry of Transportation and Communications through the Scientific and Technological Funds of ChinaProject(2007AA11Z104) supported by the High Technology Research and Development of ChinaProject(20090072110045) supported by the Specialized Research Fund for the Doctoral Program of Higher Education of China
文摘To accurately evaluate the degradation process of prestressed concrete continuous bridges exposed to aggressive environments in life-cycle,a finite element-based approach with respect to the lifetime performance assessment of concrete bridges was proposed.The existing assessment methods were firstly introduced and compared.Some essential mechanics problems involved in the degradation process,such as the deterioration of materials properties,the reduction of sectional areas and the variation of overall structural performance caused by the first two problems,were investigated and solved.A computer program named CBDAS(Concrete Bridge Durability Analysis System) was written to perform the above-metioned approach.Finally,the degradation process of a prestressed concrete continuous bridge under chloride penetration was discussed.The results show that the concrete normal stress for serviceability limit state exceeds the threshold value after 60 a,but the various performance indicators at ultimate limit state are consistently in the allowable level during service life.Therefore,in the case of prestressed concrete bridges,the serviceability limit state is more possible to have durability problems in life-cycle;however,the performance indicators at ultimate limit state can satisfy the requirements.
文摘Stress ribbon bridges have many advantages and became recently more popular mostly because of their versatile form, slender decks giving a light aesthetic impression and durability assured by post tensioned concrete. The paper presents the first in Poland stress Ribbon Bridge constructed last year. A static and dynamic analyse of the model is presented as well as construction solutions which were used to achieve the highest durability. The bridge was checked during static and dynamic load test. The results of this prove test were compared with results obtained from examination and study of other different bridge structures. It confirmed that the bridge has good dynamic resistance and greater stiffness than assumed in the design.