Veratraldehyde was tested as a corrosion inhibitor for mild steel in I M HCI and 0.5 M H2SO4 separately using mass loss and electrochemical studies. The inhibition efficiencies were evaluated at different concentratio...Veratraldehyde was tested as a corrosion inhibitor for mild steel in I M HCI and 0.5 M H2SO4 separately using mass loss and electrochemical studies. The inhibition efficiencies were evaluated at different concentrations of the inhibitor at different temperatures. The inhibition efficiency increased with increase in inhibitor concentration and decreased with increase in temperature in both the acid solutions. Electrochemical studies showed that the inhibitor is of mixed type with a slight predominance of anodic character. The inhibitor was more active in HCI than in H2SO4. The maximum inhibition efficiency approached at 1000 ppm in both the acid medium. The inhibitor was found to adsorb on the mild steel surface according to the Langmuir adsorption isotherm. The surface morphology of mild steel in the presence and absence of inhibitor was studied by using scanning electron microscopic （SEM） images.展开更多
The corrosion inhibition of mild steel in 1 mol·L^(-1) hydrochloric acid by N-methyl-2-(2-nitrobenzylidene)hydrazine carbothioamide(MNBHC) was studied using weight loss and electrochemical studies.Results obtaine...The corrosion inhibition of mild steel in 1 mol·L^(-1) hydrochloric acid by N-methyl-2-(2-nitrobenzylidene)hydrazine carbothioamide(MNBHC) was studied using weight loss and electrochemical studies.Results obtained indicate that the inhibitor is effective in hydrochloric acid medium and the efficiency decreases with increase in temperature.Added halide additives improve the efficiency of the inhibitor.The AC impedance studies reveal that the process of inhibition is through charge transfer.Polarization studies indicate the mixed nature of the inhibitor.From the thermodynamic,spectral and surface analyses the nature of adsorption has been found out.The adsorption of the inhibitor on mild steel follows the Langmuir isotherm.展开更多
Corrosion is a costly and complicated problem facing mild of Vitex doniana as a corrosion inhibitor for mild steel in HCI medium steel utility. This study investigated the use of ethanol extract Experimental methods u...Corrosion is a costly and complicated problem facing mild of Vitex doniana as a corrosion inhibitor for mild steel in HCI medium steel utility. This study investigated the use of ethanol extract Experimental methods used are gravimetric and thermometric The results showed that corrosion rate decreased as the concentration of ethanol extract of Vitex doniana increased and with decrease in temperature. Vitex doniana extract obeyed Langmuir and Tempkin adsorption isotherm. Physical adsorption was proposed from △G° and Ea. Inhibition efficiency （1%） and the degree of surface coverage （0） were calculated and all indicated that Vitex doniana was a good corrosion inhibitor.展开更多
文摘Veratraldehyde was tested as a corrosion inhibitor for mild steel in I M HCI and 0.5 M H2SO4 separately using mass loss and electrochemical studies. The inhibition efficiencies were evaluated at different concentrations of the inhibitor at different temperatures. The inhibition efficiency increased with increase in inhibitor concentration and decreased with increase in temperature in both the acid solutions. Electrochemical studies showed that the inhibitor is of mixed type with a slight predominance of anodic character. The inhibitor was more active in HCI than in H2SO4. The maximum inhibition efficiency approached at 1000 ppm in both the acid medium. The inhibitor was found to adsorb on the mild steel surface according to the Langmuir adsorption isotherm. The surface morphology of mild steel in the presence and absence of inhibitor was studied by using scanning electron microscopic （SEM） images.
文摘The corrosion inhibition of mild steel in 1 mol·L^(-1) hydrochloric acid by N-methyl-2-(2-nitrobenzylidene)hydrazine carbothioamide(MNBHC) was studied using weight loss and electrochemical studies.Results obtained indicate that the inhibitor is effective in hydrochloric acid medium and the efficiency decreases with increase in temperature.Added halide additives improve the efficiency of the inhibitor.The AC impedance studies reveal that the process of inhibition is through charge transfer.Polarization studies indicate the mixed nature of the inhibitor.From the thermodynamic,spectral and surface analyses the nature of adsorption has been found out.The adsorption of the inhibitor on mild steel follows the Langmuir isotherm.
文摘Corrosion is a costly and complicated problem facing mild of Vitex doniana as a corrosion inhibitor for mild steel in HCI medium steel utility. This study investigated the use of ethanol extract Experimental methods used are gravimetric and thermometric The results showed that corrosion rate decreased as the concentration of ethanol extract of Vitex doniana increased and with decrease in temperature. Vitex doniana extract obeyed Langmuir and Tempkin adsorption isotherm. Physical adsorption was proposed from △G° and Ea. Inhibition efficiency （1%） and the degree of surface coverage （0） were calculated and all indicated that Vitex doniana was a good corrosion inhibitor.