Ultrasonic vibration was introduced into the Mg-8Li-3A1 alloy melt during its solidification process. The microstructure, corrosion resistance and mechanical properties of the Mg-8Li-3A1 alloy under ultrasonic vibrati...Ultrasonic vibration was introduced into the Mg-8Li-3A1 alloy melt during its solidification process. The microstructure, corrosion resistance and mechanical properties of the Mg-8Li-3A1 alloy under ultrasonic vibration were investigated. The experiment results show that the morphology of a phase is modified from coarse rosette-like structure to fine globular one with the application of ultrasonic vibration. The fine globular structure is obtained especially when the power is 170 W, and the refining effect also gets better with prolonging the ultrasonic treatment time. The corrosion resistance of the alloy with 170 W of ultrasonic vibration for 90 s is improved apparently compared with the alloy without ultrasonic vibration. The mechanical properties of alloys with ultrasonic vibration are also both improved apparently. The tensile strength and elongation of alloy improve by 9.5% and 45.7%, respectively, with 170 W of ultrasonic treatment for 90 s.展开更多
基金Project(2009AA03Z525)supported by the High-tech Research and Development Program of ChinaProject(NCET-08-0080)supported by the Program of New Century Excellent Talents of the Ministry of Education of China+1 种基金Project(20082172)supported by the Natural Science Fund of Liaoning Province,ChinaProject(2009J21DW003)supported by the Science and Technology Fund of Dalian City,China
文摘Ultrasonic vibration was introduced into the Mg-8Li-3A1 alloy melt during its solidification process. The microstructure, corrosion resistance and mechanical properties of the Mg-8Li-3A1 alloy under ultrasonic vibration were investigated. The experiment results show that the morphology of a phase is modified from coarse rosette-like structure to fine globular one with the application of ultrasonic vibration. The fine globular structure is obtained especially when the power is 170 W, and the refining effect also gets better with prolonging the ultrasonic treatment time. The corrosion resistance of the alloy with 170 W of ultrasonic vibration for 90 s is improved apparently compared with the alloy without ultrasonic vibration. The mechanical properties of alloys with ultrasonic vibration are also both improved apparently. The tensile strength and elongation of alloy improve by 9.5% and 45.7%, respectively, with 170 W of ultrasonic treatment for 90 s.