Microarc oxidation （MAO） process was conducted on AZ91D magnesium alloy in an electrolyte composed of NazSiO3, NaAlO2, NaEB4O7, NaOH, C3H803 and C6H5Na307 by AC pulse electrical source. The surface and cross-section...Microarc oxidation （MAO） process was conducted on AZ91D magnesium alloy in an electrolyte composed of NazSiO3, NaAlO2, NaEB4O7, NaOH, C3H803 and C6H5Na307 by AC pulse electrical source. The surface and cross-sectional morphologies, film thickness, chemical composition and structure of the coatings were characterized by scanning electron microscopy（SEM）, layer thickness metry, energy disperse spectroscopy（EDS） and X-ray diffraction（XRD）. The corrosiofi resistances of the coatings in a 3.5% NaC1 neutral solution were evaluated by electrochemical impedance spectroscopy （EIS） and potentiodynamic polarization test. The results showed that an optimized electrolyte with a composition of 15 g/L NazSiO3, 9 g/L NaA102, 2 g/L NazB407, 3 g/L NaOH, 5 mL/L C3H803 and 7 g/LC,HsNa307 was developed by means of orthogonal experiment. The coating obtained in the optimized electrolyte had a dense structure and revealed a lower current density, decreased by two orders of magnitude as compared with the magnesium substrate. Meanwhile, the corrosive potentials of the coated samples increased nearly by 73 inV. EIS result showed that the corrosion resistance of the coating was mainly determined by the inner dense layer. The coating primarily contained elements Mg, Al, O and Si and XRD analyses indicated that the coating was mainly composed of MgO, Mg2SiO4 and MgAl204.展开更多
基金Project (12504230006) supported by the Priority Academic Program Development of Jiangsu Higher Education Institutions, China
文摘Microarc oxidation （MAO） process was conducted on AZ91D magnesium alloy in an electrolyte composed of NazSiO3, NaAlO2, NaEB4O7, NaOH, C3H803 and C6H5Na307 by AC pulse electrical source. The surface and cross-sectional morphologies, film thickness, chemical composition and structure of the coatings were characterized by scanning electron microscopy（SEM）, layer thickness metry, energy disperse spectroscopy（EDS） and X-ray diffraction（XRD）. The corrosiofi resistances of the coatings in a 3.5% NaC1 neutral solution were evaluated by electrochemical impedance spectroscopy （EIS） and potentiodynamic polarization test. The results showed that an optimized electrolyte with a composition of 15 g/L NazSiO3, 9 g/L NaA102, 2 g/L NazB407, 3 g/L NaOH, 5 mL/L C3H803 and 7 g/LC,HsNa307 was developed by means of orthogonal experiment. The coating obtained in the optimized electrolyte had a dense structure and revealed a lower current density, decreased by two orders of magnitude as compared with the magnesium substrate. Meanwhile, the corrosive potentials of the coated samples increased nearly by 73 inV. EIS result showed that the corrosion resistance of the coating was mainly determined by the inner dense layer. The coating primarily contained elements Mg, Al, O and Si and XRD analyses indicated that the coating was mainly composed of MgO, Mg2SiO4 and MgAl204.