The morphological change of St/DVB crosslinked gels during chloromethylation wasstudied by fluorescence spectroscopy using St/DVB crosslinked and hypercrosslinked gels as controlsamples. It has been found that with in...The morphological change of St/DVB crosslinked gels during chloromethylation wasstudied by fluorescence spectroscopy using St/DVB crosslinked and hypercrosslinked gels as controlsamples. It has been found that with increase of chlorine content, the excimer emission band (~325nm)approaches to vanish, while the intensity of multi-ring aggregate emission band (~420nm) quicklyreaches a maximum, and then decreases sharply accompanied by appearance ofa new broad bandcentred at ca 488nm which roughly coincides with the typical emission band of hypercrossllinkedSt/DVB gels. Mearwhile, the result of IR measurement suggests that methylene bridge between phenylrings forms and increases with chloromethylation process. These results are explained in terms ofaside reaction of post-crosslinking, which densifies the loosely crosslinked networks and undoes thedensely entangled microgel nuclei. As a result, the morphology of the crosslinked gels becom es morehomogeneous with chloromethylation.展开更多
Two kinds of St/DVB copolymer beeds containing (1 - pyrenyl) formyl and(1 -pyrenyl) methyl groups respectively have been synthesized by both functionalization and copolymerization. The fluorescence spectra of the swo...Two kinds of St/DVB copolymer beeds containing (1 - pyrenyl) formyl and(1 -pyrenyl) methyl groups respectively have been synthesized by both functionalization and copolymerization. The fluorescence spectra of the swollen polymers synthesized are similar in shape to those of the corresponding model compounds, whilethe intensity ratio of excimer to monomer shows clear dependence on the contents ofthe pyrene groups.展开更多
A series of 4,4＇-disubstituted-[2,2＇]-bipyridines, featuring electron withdrawing/donating functional groups such as amino, chloro, nitro, ethoxycarbonyl, carboxy, methyl, methoxy and hydroxymethyl, have been syn- t...A series of 4,4＇-disubstituted-[2,2＇]-bipyridines, featuring electron withdrawing/donating functional groups such as amino, chloro, nitro, ethoxycarbonyl, carboxy, methyl, methoxy and hydroxymethyl, have been syn- thesized and employed in the copolymerization of carbon monoxide （CO） and styrene. The available bipyridine and its derivatives were coordinated with palladium （ II ） acetate for catalyzing the copolymerization of CO and styrene, and the concomitant polyketone was characterized by means of t3C NMR, FTIR, differential scanning calo- rimetry （DSC） and element analysis techniques concerning its structure and thermal performance. The effect of dif- ferent electron-donating and electron-withdrawing groups on catalyst performance and molecular weight of co- polymer was studied under certain experimental condition. It has been proved that the enhancement of electron donating and conjugative effects on bipyridine ligand will not only improve the catalytic activity of the composi- tion, but also increase the molecular weight of the as-prepared polyketone. The catalytic activity is the highest in hydroxymethyl substituted 2,2＇-bipyridine ligand（l 356 gSTCO/（gPd · h））, when the molecular weight and polydispersity index of the polyketone are Mn = 8 502, Mw = 1 3440 and Mw/Mn = 1.581, respectively.展开更多
Preparation of thermoplastic elastomer of Polypropylene-SIR 10 rubber blends with addition of DCP （dicumil peroxide） as initiator and DVB （divinylbenzene） as a crosslinker has been done. Blends of Polypropylene-SI...Preparation of thermoplastic elastomer of Polypropylene-SIR 10 rubber blends with addition of DCP （dicumil peroxide） as initiator and DVB （divinylbenzene） as a crosslinker has been done. Blends of Polypropylene-SIR 10 rubber with variation of weight 60/40 （w/w）, 50/50 （w/w） and 40/60 （w/w） with variation concentration of DCP and DVB 1 phr, 2 phr and 3 phr were mixed into internal mixer at temperature 180 ℃. Then, the blends were pressed at 185 ℃ and specimen were molded according to the ASTM D638. The characterization were carried out based on tensile strength testing, crosslink percentage, morphology surface analysis with SEM and fungtional group analysis with FTIR （Fourier Transform Infra Red）. The result showed that the blends of Polypropilene-SIR 10 rubber 60/40 （w/w） with 2 phr DCP and 1 phr DVB posses a higher tensile strength with value 1.37 Kgf/mm2 and value of elongation at break 17.58%, and value of percentage crosslink 82.4%. The result of morphology test with SEM showed that the blend was well homogenous. Spectra analysis with FT-IR has shown physical interaction among components of the blends.展开更多
基金National Natural Scientific Foundation of China (Project grant No.29574165 29928003+1 种基金 29874019) National Natural Scientific Foundation of Tianjin (Project grant No.013604011)
文摘The morphological change of St/DVB crosslinked gels during chloromethylation wasstudied by fluorescence spectroscopy using St/DVB crosslinked and hypercrosslinked gels as controlsamples. It has been found that with increase of chlorine content, the excimer emission band (~325nm)approaches to vanish, while the intensity of multi-ring aggregate emission band (~420nm) quicklyreaches a maximum, and then decreases sharply accompanied by appearance ofa new broad bandcentred at ca 488nm which roughly coincides with the typical emission band of hypercrossllinkedSt/DVB gels. Mearwhile, the result of IR measurement suggests that methylene bridge between phenylrings forms and increases with chloromethylation process. These results are explained in terms ofaside reaction of post-crosslinking, which densifies the loosely crosslinked networks and undoes thedensely entangled microgel nuclei. As a result, the morphology of the crosslinked gels becom es morehomogeneous with chloromethylation.
文摘Two kinds of St/DVB copolymer beeds containing (1 - pyrenyl) formyl and(1 -pyrenyl) methyl groups respectively have been synthesized by both functionalization and copolymerization. The fluorescence spectra of the swollen polymers synthesized are similar in shape to those of the corresponding model compounds, whilethe intensity ratio of excimer to monomer shows clear dependence on the contents ofthe pyrene groups.
基金Supported by Tianjin Natural Science Foundation(No.07JCYBJC00600)
文摘A series of 4,4＇-disubstituted-[2,2＇]-bipyridines, featuring electron withdrawing/donating functional groups such as amino, chloro, nitro, ethoxycarbonyl, carboxy, methyl, methoxy and hydroxymethyl, have been syn- thesized and employed in the copolymerization of carbon monoxide （CO） and styrene. The available bipyridine and its derivatives were coordinated with palladium （ II ） acetate for catalyzing the copolymerization of CO and styrene, and the concomitant polyketone was characterized by means of t3C NMR, FTIR, differential scanning calo- rimetry （DSC） and element analysis techniques concerning its structure and thermal performance. The effect of dif- ferent electron-donating and electron-withdrawing groups on catalyst performance and molecular weight of co- polymer was studied under certain experimental condition. It has been proved that the enhancement of electron donating and conjugative effects on bipyridine ligand will not only improve the catalytic activity of the composi- tion, but also increase the molecular weight of the as-prepared polyketone. The catalytic activity is the highest in hydroxymethyl substituted 2,2＇-bipyridine ligand（l 356 gSTCO/（gPd · h））, when the molecular weight and polydispersity index of the polyketone are Mn = 8 502, Mw = 1 3440 and Mw/Mn = 1.581, respectively.
文摘Preparation of thermoplastic elastomer of Polypropylene-SIR 10 rubber blends with addition of DCP （dicumil peroxide） as initiator and DVB （divinylbenzene） as a crosslinker has been done. Blends of Polypropylene-SIR 10 rubber with variation of weight 60/40 （w/w）, 50/50 （w/w） and 40/60 （w/w） with variation concentration of DCP and DVB 1 phr, 2 phr and 3 phr were mixed into internal mixer at temperature 180 ℃. Then, the blends were pressed at 185 ℃ and specimen were molded according to the ASTM D638. The characterization were carried out based on tensile strength testing, crosslink percentage, morphology surface analysis with SEM and fungtional group analysis with FTIR （Fourier Transform Infra Red）. The result showed that the blends of Polypropilene-SIR 10 rubber 60/40 （w/w） with 2 phr DCP and 1 phr DVB posses a higher tensile strength with value 1.37 Kgf/mm2 and value of elongation at break 17.58%, and value of percentage crosslink 82.4%. The result of morphology test with SEM showed that the blend was well homogenous. Spectra analysis with FT-IR has shown physical interaction among components of the blends.