Different-sized hollow SiO2 spheres of 249–1348 nm in diameter were successfully prepared by using Na2SiO3 as the precursor and using polystyrene and polystyrene-methyl acrylic acid latexes as the templates. The diam...Different-sized hollow SiO2 spheres of 249–1348 nm in diameter were successfully prepared by using Na2SiO3 as the precursor and using polystyrene and polystyrene-methyl acrylic acid latexes as the templates. The diameter and shell thickness of the hollow SiO2 spheres increase with increasing the latex template diameter at a given mass ratio of SiO2 to latex template. The diameter and shell thickness of the hollow SiO2 spheres also increase with increasing the mass ratios of SiO2 to latex template. The presence of carboxylic acid groups on the surfaces of polystyrene-methyl acrylic acid latex templates favors the formation of dense and uniform SiO2 shells. The hollow SiO2 sphere is constructed by mesoporous shell with large specific surface area. When glyphosate is used as a release model chemical, glyphosate release rate is tuned by varying the shell thickness.展开更多
Functional porous microspheres used for the slow release carrier of actives in cosmetics or pharmaceuticals were prepared by modified suspension polymerization of styrene （ST） with divinylbenzene （DVB） in the pres...Functional porous microspheres used for the slow release carrier of actives in cosmetics or pharmaceuticals were prepared by modified suspension polymerization of styrene （ST） with divinylbenzene （DVB） in the presence of toluene, cyclohexanol and heptane as porogenic diluents. The use of ultrasonic dispersion decreases the beads＇ size and improves the uniformity. The effects of the porogen mixture, DVB content and solvent extraction on the surface performance of the synthesized beads were studied. The microspheres were characterized by scanning electron microscopy （SEM） and BET surface area determination. It was found that a great proportion of the non-solvating porogen increases the pore diameter and the specific surface area. High DVB concentration also results in the great specific surface area and porosity. When the ratio of toluene/cyclohexanol is 1：2, DVB content is at the range of 40%-60% and methylene chloride was used as extractant, the beads with good spherical shape and pore size were obtained. The prepared porous microspheres were applied as active carriers and showed satisfactory slow release effect. Over 10h constantly sustained release was observed in vitro releasing test for hydroquinone-loaded microspheres. Great surface area promoted high concentration of released hydroquinone.展开更多
基金supported by the Basic and Frontier Research Project of Chongqing (cstc2013jcyjA50013)Scientific and Technological Research Program of Chongqing Municipal Education Commission (KJ131504)the Innovation Team Building at Institutions of Higher Education in Chongqing (KJTD201325)~~
基金Projects (11KJB530002, CX10B-259Z) supported by Research Funds from Jiangsu Provincial Department of Education, ChinaProject (10zxfk35) supported by Sichuan Province Nonmetallic Composites and Functional Materials Key Laboratory Project, China
文摘Different-sized hollow SiO2 spheres of 249–1348 nm in diameter were successfully prepared by using Na2SiO3 as the precursor and using polystyrene and polystyrene-methyl acrylic acid latexes as the templates. The diameter and shell thickness of the hollow SiO2 spheres increase with increasing the latex template diameter at a given mass ratio of SiO2 to latex template. The diameter and shell thickness of the hollow SiO2 spheres also increase with increasing the mass ratios of SiO2 to latex template. The presence of carboxylic acid groups on the surfaces of polystyrene-methyl acrylic acid latex templates favors the formation of dense and uniform SiO2 shells. The hollow SiO2 sphere is constructed by mesoporous shell with large specific surface area. When glyphosate is used as a release model chemical, glyphosate release rate is tuned by varying the shell thickness.
基金Natural Science Foundation of Guangdong Province （No.05006556）.
文摘Functional porous microspheres used for the slow release carrier of actives in cosmetics or pharmaceuticals were prepared by modified suspension polymerization of styrene （ST） with divinylbenzene （DVB） in the presence of toluene, cyclohexanol and heptane as porogenic diluents. The use of ultrasonic dispersion decreases the beads＇ size and improves the uniformity. The effects of the porogen mixture, DVB content and solvent extraction on the surface performance of the synthesized beads were studied. The microspheres were characterized by scanning electron microscopy （SEM） and BET surface area determination. It was found that a great proportion of the non-solvating porogen increases the pore diameter and the specific surface area. High DVB concentration also results in the great specific surface area and porosity. When the ratio of toluene/cyclohexanol is 1：2, DVB content is at the range of 40%-60% and methylene chloride was used as extractant, the beads with good spherical shape and pore size were obtained. The prepared porous microspheres were applied as active carriers and showed satisfactory slow release effect. Over 10h constantly sustained release was observed in vitro releasing test for hydroquinone-loaded microspheres. Great surface area promoted high concentration of released hydroquinone.