Modified diphenyl oxide resin was synthesized by co-polymerization of unsaturated acid and diphenyl oxide derivants. And then modified bismaleimide resin and expoxide linear phenolic resin were added into modified dip...Modified diphenyl oxide resin was synthesized by co-polymerization of unsaturated acid and diphenyl oxide derivants. And then modified bismaleimide resin and expoxide linear phenolic resin were added into modified diphenyl oxide resin to co-polymerize and modify once more. The system was applied in composites. Their properties were investigated and found that they met the requirements as a heat-resisting adhesive.展开更多
The electrical, physical, mechanical and thermal properties of fluorine-containing alicyclic polyimides have been investigated. It was shown that the minimum value of the dielectric constant 1.91 at room temperature a...The electrical, physical, mechanical and thermal properties of fluorine-containing alicyclic polyimides have been investigated. It was shown that the minimum value of the dielectric constant 1.91 at room temperature and 1 kHz frequency was achieved for polymers containing only one fluorine atom in the structure. The dielectric loss tangent of new polymers was （I -4）~ 103. Electro-physical parameters were stable during polymer heating up to 300 ~C, and at the frequency from 1 to 20 kHz. Resistivity by heating in the air up to 320-380 ~C has been investigated depending on the polyimides structure. The coefficient of moisture absorption for the fluorine-containing polyimide based on dianhydride with 4,4＇-oxydianiline was determined at 50% humidity and 25 ℃. It was around 0.6, but after immersion in the water for 24 and 48 h was 0.8% and 1.2%, respectively. Manufactured films had tensile strength to 160-170 MPa, and elongation up to 55%.展开更多
文摘Modified diphenyl oxide resin was synthesized by co-polymerization of unsaturated acid and diphenyl oxide derivants. And then modified bismaleimide resin and expoxide linear phenolic resin were added into modified diphenyl oxide resin to co-polymerize and modify once more. The system was applied in composites. Their properties were investigated and found that they met the requirements as a heat-resisting adhesive.
文摘The electrical, physical, mechanical and thermal properties of fluorine-containing alicyclic polyimides have been investigated. It was shown that the minimum value of the dielectric constant 1.91 at room temperature and 1 kHz frequency was achieved for polymers containing only one fluorine atom in the structure. The dielectric loss tangent of new polymers was （I -4）~ 103. Electro-physical parameters were stable during polymer heating up to 300 ~C, and at the frequency from 1 to 20 kHz. Resistivity by heating in the air up to 320-380 ~C has been investigated depending on the polyimides structure. The coefficient of moisture absorption for the fluorine-containing polyimide based on dianhydride with 4,4＇-oxydianiline was determined at 50% humidity and 25 ℃. It was around 0.6, but after immersion in the water for 24 and 48 h was 0.8% and 1.2%, respectively. Manufactured films had tensile strength to 160-170 MPa, and elongation up to 55%.