Using Cu-phthalocyanine(CuPc),4,4’-diaminodiphenyl ether and pyromellitic dianhydride as monomer materials, polyimide(PI) thin films doped-CuPc have been prepared onto glass substrate by vapor phase co-deposition...Using Cu-phthalocyanine(CuPc),4,4’-diaminodiphenyl ether and pyromellitic dianhydride as monomer materials, polyimide(PI) thin films doped-CuPc have been prepared onto glass substrate by vapor phase co-deposition polymerization under a vacuum of 2×10-3Pa and thermal curing of polyamic acid film in at temperature of 150-200℃ for 60min. In this process, the polymerization can be carried out through controlling the stoichiometric ratio, heating time and deposition rates of the three monomers. IR spectrum identifies the designed chemical structure of the polymer. The absorption of polyimide doped-CuPc is very intense in vis-range and near-infrared by UV-Vis spectrum. And, the PI films doped-CuPc polymerized by vapor phase deposition have uniformity, fine thermal stability and good nonlinear optical properties, and the third-order optical nonlinear susceptibility χ(3) with degenerate four-wave mixing can be 1.984×10-9ESU.展开更多
A highly porous nickel-film electrode with satisfactory mechanical strength was prepared by a facile vertical template-assisted composite electrodeposition method using polystyrene(PS) microspheres templates, with the...A highly porous nickel-film electrode with satisfactory mechanical strength was prepared by a facile vertical template-assisted composite electrodeposition method using polystyrene(PS) microspheres templates, with the aim of improving the electrocatalytic activity for the hydrogen-evolution reaction(HER). During the composite electrodeposition process, the hydrophobic PS microspheres were highly dispersed in the electrolyte with the help of a surfactant, and then co-deposited with Ni to form the film electrode. After removing the PS templates by annealing, a porous Ni film containing large amount of uniformly dispersed pores with narrow size distribution was obtained, and then applied as the electrode for the HER in an alkaline medium. As evidenced by the electrochemical analysis, the porous Ni film electrode exhibits higher catalytic activity as compared to a dense Ni film electrode and is superior to a Ni/Ru O2/Ce O2 commercial electrode. The effect of temperature on the catalytic properties of the porous Ni film electrode was also investigated; the activation energy was calculated as 17.26 k J/mol. The enhanced activity toward the HER was attributed to the improved electrochemical surface area and mass transportation facilitated by the high porosity of the synthesized Ni film electrode.展开更多
基金Natural Science Foundation of Shaanxi Province ( 2004CS110005 ) Research Foundation of Northwestern Polytechnical University
文摘Using Cu-phthalocyanine(CuPc),4,4’-diaminodiphenyl ether and pyromellitic dianhydride as monomer materials, polyimide(PI) thin films doped-CuPc have been prepared onto glass substrate by vapor phase co-deposition polymerization under a vacuum of 2×10-3Pa and thermal curing of polyamic acid film in at temperature of 150-200℃ for 60min. In this process, the polymerization can be carried out through controlling the stoichiometric ratio, heating time and deposition rates of the three monomers. IR spectrum identifies the designed chemical structure of the polymer. The absorption of polyimide doped-CuPc is very intense in vis-range and near-infrared by UV-Vis spectrum. And, the PI films doped-CuPc polymerized by vapor phase deposition have uniformity, fine thermal stability and good nonlinear optical properties, and the third-order optical nonlinear susceptibility χ(3) with degenerate four-wave mixing can be 1.984×10-9ESU.
基金supported by the National Natural Science Foundation of China(51125007)the National Key Technology R&D Program of China(2009BAE87B00)
文摘A highly porous nickel-film electrode with satisfactory mechanical strength was prepared by a facile vertical template-assisted composite electrodeposition method using polystyrene(PS) microspheres templates, with the aim of improving the electrocatalytic activity for the hydrogen-evolution reaction(HER). During the composite electrodeposition process, the hydrophobic PS microspheres were highly dispersed in the electrolyte with the help of a surfactant, and then co-deposited with Ni to form the film electrode. After removing the PS templates by annealing, a porous Ni film containing large amount of uniformly dispersed pores with narrow size distribution was obtained, and then applied as the electrode for the HER in an alkaline medium. As evidenced by the electrochemical analysis, the porous Ni film electrode exhibits higher catalytic activity as compared to a dense Ni film electrode and is superior to a Ni/Ru O2/Ce O2 commercial electrode. The effect of temperature on the catalytic properties of the porous Ni film electrode was also investigated; the activation energy was calculated as 17.26 k J/mol. The enhanced activity toward the HER was attributed to the improved electrochemical surface area and mass transportation facilitated by the high porosity of the synthesized Ni film electrode.