A novel polymer/SiO2 hybrid emulsion(PAES)was prepared by directly mixing colloidal silica with polyacrylate emulsion(PAE)modified by a saline coupling agent.The sol-gel-derived thin films were obtained by addition of...A novel polymer/SiO2 hybrid emulsion(PAES)was prepared by directly mixing colloidal silica with polyacrylate emulsion(PAE)modified by a saline coupling agent.The sol-gel-derived thin films were obtained by addition of co-solvents into the PAES.The effects ofγ-methacryloxypropyltrimethoxysilane(KH-570)content and co-solvent on the properties of PAES films were investigated.Dynamic laser scattering(DLS)data indicate that the average diameter of PAES(96 nm)is slightly larger than that of PAE(89 nm).Transmission electron microscopy (TEM)photo discloses that colloidal silica particles are dispersed uniformly around polyacrylate particles and some of the colloidal silica particles are adsorbed on the surface of PAE particles.The crosslinking degree data and Fourier transform infrared(FT-IR)spectra confirm that the chemical structure of the PAES is changed to form Si-O-Si-polymer crosslinking networks during the film formation.Atomic force microscope(AFM)photos show the solvent induced sol-gel process of colloidal silica and the Si-based polymer distribution on the film surface of the dried PAES.Thermogravimetric analysis(TGA)curves demonstrate that the PAES films display much better thermal stability than PAE.展开更多
Polymer nanoparticles were prepared in the methyl methacrylate (MMA)/buty lmethacrylate (BA) emulsion copolymerization process by a modified microemulsion copolymerization method. 2-Hydroxyethyl methacrylate(HEMA), ac...Polymer nanoparticles were prepared in the methyl methacrylate (MMA)/buty lmethacrylate (BA) emulsion copolymerization process by a modified microemulsion copolymerization method. 2-Hydroxyethyl methacrylate(HEMA), acrylate (AA) and methyl acrylate (MAA) were used as reactive cosurfactants. With this process high polymer: surfactant weight ratios (40:1 or greater),relatively concentrated (~30wt. %) latexes and small (~60nm) particle diameters were obtained.Properties of the latexes were characterized by TEM, DSC, dynamic light scattering, and IR spectroscopy.展开更多
基金Supported by the Program for New Century Excellent Talents in University（NCET-08-0204） National Natural Science Foundation of China（20976060） the Scientific Research Foundation for the Returned Overseas Chinese Scholars State Edu-cation Ministry （China）
文摘A novel polymer/SiO2 hybrid emulsion(PAES)was prepared by directly mixing colloidal silica with polyacrylate emulsion(PAE)modified by a saline coupling agent.The sol-gel-derived thin films were obtained by addition of co-solvents into the PAES.The effects ofγ-methacryloxypropyltrimethoxysilane(KH-570)content and co-solvent on the properties of PAES films were investigated.Dynamic laser scattering(DLS)data indicate that the average diameter of PAES(96 nm)is slightly larger than that of PAE(89 nm).Transmission electron microscopy (TEM)photo discloses that colloidal silica particles are dispersed uniformly around polyacrylate particles and some of the colloidal silica particles are adsorbed on the surface of PAE particles.The crosslinking degree data and Fourier transform infrared(FT-IR)spectra confirm that the chemical structure of the PAES is changed to form Si-O-Si-polymer crosslinking networks during the film formation.Atomic force microscope(AFM)photos show the solvent induced sol-gel process of colloidal silica and the Si-based polymer distribution on the film surface of the dried PAES.Thermogravimetric analysis(TGA)curves demonstrate that the PAES films display much better thermal stability than PAE.
基金CEM Foundation For N & T Joint Academy (Chinese Education Ministry Foundation for Nankai University and Tianjin University Joint Academy)
文摘Polymer nanoparticles were prepared in the methyl methacrylate (MMA)/buty lmethacrylate (BA) emulsion copolymerization process by a modified microemulsion copolymerization method. 2-Hydroxyethyl methacrylate(HEMA), acrylate (AA) and methyl acrylate (MAA) were used as reactive cosurfactants. With this process high polymer: surfactant weight ratios (40:1 or greater),relatively concentrated (~30wt. %) latexes and small (~60nm) particle diameters were obtained.Properties of the latexes were characterized by TEM, DSC, dynamic light scattering, and IR spectroscopy.