与聚合物发光器相关的若干问题的研究

结合作者在聚合物发光器相关的若干问题的研究结果，评述新型可溶性导电高聚物、透明导电高聚物薄膜，多孔硅与导电高聚物异质结的研究进展。

Electron Injection Enhancement by Diamond-Like Carbon Film in Polymer Electroluminescence Devices

A diamond-like carbon （DLC） film is deposited as an electron injection layer between the polymer light-emitting layer（MEH-PPV） and aluminum （Al） cathode electrode in polymer electroluminescence devices （PLEDs） using a radio frequency plasma deposition system. The source material of the DLC is n-butylamine. The devices consist of indium tin oxide （ITO）/MEH-PPV/DLC/Al. Electron injection properties are investigated through I-V characteristics,and the mechanism of electron injection enhancement due to a thin DLC layer has been studied. It is found that： （1） a DLC layer thinner than 1.0nm leads to a higher turn-on voltage and decreased electroluminescent （EL） efficiency; （2） a 5.0nm DLC layer significantly enhances the electron injection and results in the lowest turn-on voltage and the highest EL efficiency; （3） DLC layer that exceeds 5.0nm results in poor device performance;and（4） EL emission can hardly be detected when the layer exceeds 10.0nm. The properties of ITO/MEH-PPV/DLC/Al and ITO/MEH-PPV/LiF/Al are investigated comparatively.

Optoelectronic properties of new functionalized heteroleptic iridium complex

A new functionalized heteroleptic iridium complex coordinated with 1-phenylisoquinoline （1-piq） and a functionalized fl-diketone （G1）, Ir（1-piq）2G1, was synthesized and characterized by 1H-NMR, mass spectrometry and elemental analysis. The larger conjugation of the replacement of acetylacetone （acac） by a functionalizedβ-diketonate ligand led to a significant decrease in the HOMO level toward vacuum level, while Ir（1-piq）2G1 and Ir（1-piq）2（acac） showed red phosphorescent emissions of about 620 nm in dichloromethane solution. The phosphorescent polymer light-emitting devices were achieved, with the complexes incorporated with polyfluorene （PFO） as a host polymer doped with 30% of 5-（4-biphenylyl）-2-（4-tert-butylphenyl）-1,3,4-oxadiazole （PBD） as electron transport material. The energy transfer mechanism of the devices was also discussed. The lower EL performance of Ir（1-piq）2G1 is ascribed to the inter-ligand energy transfer, indicating that it is important to control the energy level of the cyclometalated and ancillary ligands.

Highly efficient pure white polymer light-emitting devices based on poly(N-vinylcarbazole) doped with blue and red phosphorescent dyes

Efficient white-polymer-light-emitting devices (WPLEDs) have been fabricated with a single emitting layer containing a hole-transporting host polymer,poly(N-vinylcarbzole),and an electron-transporting auxiliary,1,3-bis[(4-tert-butylphenyl)-1,3,4-oxadiazolyl]-phenylene,codoped with two phosphorescent dyes:Iridium(III)bis (2-(4,6-difluorophenyl)-pyridinato-N,C2') picolinate (FIrpic) and home-made Ir-G2 for blue and red emission,respectively.With the structure of ITO/PEDOT:PSS 4083(40 nm)/emission layer(80 nm)/Ba(4 nm)/Al(120 nm),the device showed a maximal luminous efficiency (LE) of 13.5 cd A-1(corresponding to an external quantum efficiency (EQE) of 6.8%),and a peak power efficiency (PE) of 6.5 lm W-1 at 6.0 V.Meanwhile,the device exhibited pure white emission with Commission Internationale de l'Eclairage (CIE) coordinates of (0.34,0.35) at a current density of 12 mA cm-2,which is very close to the equi-energy white point with CIE coordinates of (0.33,0.33).The device performance can be further optimized when more balanced hole/electron injection is achieved by incorporating a lower conducting type anode buffer layer (PEDOT:PSS) and incorporating poly[(9,9-bis(3'-(N,N-dimethylamino)propyl)-2,7-fluorenene)-alt-2,7-(9,9-dioctyfluorene)] (PFN) as an electron injection layer at the cathode.The optimized device showed an LE of 24.6 cd A-1 (with an EQE of 14.1%),while the peak power efficiency reached 12.66 lm W-1.Moreover,the WPLEDs showed good electroluminescence (EL) stability over a wide range of operating current density and luminance.

Synthesis and optoelectronic properties of amino-functionalized carbazole-based conjugated polymers

A series of alcohol soluble amino-functionalized carbazole-based copolymers were synthesized via Suzuki coupling reaction. The pendent amino groups endow them high solubility in polar solvents, as well as efficient electron injection capability from high work-function metals. The relationships between the photophysical and electrochemical properties and the polymer backbone structure were systematically investigated. These alcohol-soluble carbazole-based copolymers were used as cathode interlayers between the high work-function metal A1 cathode and P-PPV emissive layer in polymer light-emitting diodes with device structure of ITO/PEDOT：PSS/P-PPV/interlayer/A1. The resulting devices exhibited improved performance due to the better electron injection/transporting ability of the designed copolymers from A1 cathode to the light-emitting layer.