以氯甲基杂环聚醚酮(CMPPEK)为原料,加入三乙胺进行铵化,并分别加入二乙烯三胺(DETA)和二乙胺(DEA),生成的仲胺基(或叔胺基)与邻近分子链氯甲基团进行自交联.经过制膜和离子交换反应,制备了DETA自交联杂萘联苯聚芳醚阴离子交换膜(DETA-Q...以氯甲基杂环聚醚酮(CMPPEK)为原料,加入三乙胺进行铵化,并分别加入二乙烯三胺(DETA)和二乙胺(DEA),生成的仲胺基(或叔胺基)与邻近分子链氯甲基团进行自交联.经过制膜和离子交换反应,制备了DETA自交联杂萘联苯聚芳醚阴离子交换膜(DETA-QPPEK-OH)和DEA自交联杂萘联苯聚芳醚阴离子交换膜(DEA-QPPEK-OH).采用傅里叶变换红外(FTIR)光谱对制备自交联膜的化学结构进行表征.研究了DETA-QPPEK-OH和DEA-QPPEK-OH膜的理化性质,结果表明前者具有较低吸水率和更低溶胀度.通过研究DETAQPPEK-OH和DEA-QPPEK-OH膜的离子传导率随温度的变化规律,结果表明在80°C时其离子传导率分别达到0.060和0.028 S cm-1,表明本文制备的自交联膜具有较高离子传导率.此外还通过热重分析(TGA)对两类自交联膜的热稳定性进行了研究.展开更多
In order to effectively improve the properties of anion exchange membrane(AEM)materials,a series of novel poly(aryl ether nitrile)s with flexible side-chain-type quaternary phosphonium cations(PAEN-TPP-x)were designed...In order to effectively improve the properties of anion exchange membrane(AEM)materials,a series of novel poly(aryl ether nitrile)s with flexible side-chain-type quaternary phosphonium cations(PAEN-TPP-x)were designed and prepared on the basis of considering the influences of polymer backbone,cationic group species and the connection way between the cations and polymer chains.The synthetic method,structure and ion-exchange capacity,water absorption,swelling,hydroxide conductivity and alkaline stability of the obtained AEMs were studied.A comparative study with other reported AEMs was also performed for further exploration of the relationship between the structure and properties.These AEMs with flexible side-chain-type quaternary phosphonium cations displayed good comprehensive properties.Their water uptakes and swelling ratios were in the range of 11.6%–22.7%and 4.4%–7.8%at 60℃,respectively.They had hydroxide conductivity in the range of 28.6–45.8 mS cm^-1 at 60℃.Moreover,these AEMs also exhibited improved alkaline stability,and the hydroxide conductivity for PAEN-TPP-0.35 could remain 82.1%and 80.6%of its initial value at 60 and 90℃in 2 mol L^-1 NaOH solution for480 h,respectively.展开更多
文摘以氯甲基杂环聚醚酮(CMPPEK)为原料,加入三乙胺进行铵化,并分别加入二乙烯三胺(DETA)和二乙胺(DEA),生成的仲胺基(或叔胺基)与邻近分子链氯甲基团进行自交联.经过制膜和离子交换反应,制备了DETA自交联杂萘联苯聚芳醚阴离子交换膜(DETA-QPPEK-OH)和DEA自交联杂萘联苯聚芳醚阴离子交换膜(DEA-QPPEK-OH).采用傅里叶变换红外(FTIR)光谱对制备自交联膜的化学结构进行表征.研究了DETA-QPPEK-OH和DEA-QPPEK-OH膜的理化性质,结果表明前者具有较低吸水率和更低溶胀度.通过研究DETAQPPEK-OH和DEA-QPPEK-OH膜的离子传导率随温度的变化规律,结果表明在80°C时其离子传导率分别达到0.060和0.028 S cm-1,表明本文制备的自交联膜具有较高离子传导率.此外还通过热重分析(TGA)对两类自交联膜的热稳定性进行了研究.
基金supported by the National Natural Science Foundation of China (21404016)the Key Research Program of Jiangsu Province (BE2017645)+1 种基金the Six Talent Peaks Project of Jiangsu Province (XCL-078)a project funded by the Priority Academic Program Development of Jiangsu Higher Education Institutions of China
文摘In order to effectively improve the properties of anion exchange membrane(AEM)materials,a series of novel poly(aryl ether nitrile)s with flexible side-chain-type quaternary phosphonium cations(PAEN-TPP-x)were designed and prepared on the basis of considering the influences of polymer backbone,cationic group species and the connection way between the cations and polymer chains.The synthetic method,structure and ion-exchange capacity,water absorption,swelling,hydroxide conductivity and alkaline stability of the obtained AEMs were studied.A comparative study with other reported AEMs was also performed for further exploration of the relationship between the structure and properties.These AEMs with flexible side-chain-type quaternary phosphonium cations displayed good comprehensive properties.Their water uptakes and swelling ratios were in the range of 11.6%–22.7%and 4.4%–7.8%at 60℃,respectively.They had hydroxide conductivity in the range of 28.6–45.8 mS cm^-1 at 60℃.Moreover,these AEMs also exhibited improved alkaline stability,and the hydroxide conductivity for PAEN-TPP-0.35 could remain 82.1%and 80.6%of its initial value at 60 and 90℃in 2 mol L^-1 NaOH solution for480 h,respectively.
