The fabrication technique of micro/nano-scale speckle patterns with focused ion beam (FIB) system is studied for digital image correlation (DIC) measurement under a scanning electron microscope (SEM).The speckle patte...The fabrication technique of micro/nano-scale speckle patterns with focused ion beam (FIB) system is studied for digital image correlation (DIC) measurement under a scanning electron microscope (SEM).The speckle patterns are fabricated by directly etching the counterpart of the specimen to the black part of a template.Mean intensity gradient is used to evaluate the quality of these SEM images of speckle patterns fabricated based on different templates to select an optimum template.The pattern size depending on the displacement measurement sensitivity is adjusted by altering the magnification of FIB according to the relation curve of the etching size versus magnification.The influencing factors including etching time and ion beam current are discussed.Rigid body translation tests and rotation tests are carried out under SEM to verify the reliability of the fabricated speckle patterns.The calculated values are in good agreement with the imposed ones.展开更多
To fabricate thick-walled hollow glass microspheres （HGMs） for inertial confinement fusion （ICF） targets by sol-gel technology, we investigated the effects of glass composition, blowing agent, refining temperature...To fabricate thick-walled hollow glass microspheres （HGMs） for inertial confinement fusion （ICF） targets by sol-gel technology, we investigated the effects of glass composition, blowing agent, refining temperature, pressure and composition of furnace atmosphere on the wall thickness of HGMs by numerical simulation and experiments. The results showed that the residence times of the thick-walled HGMs in the encapsulating and refining phases decreased with the increase of wall thickness of HGMs. As a response to this challenge, glass composition must be optimized with the object of high surface tension and low viscosity at refining temperature, and the blowing agents with high decomposition temperature should be used, furthermore the concentration of blowing agents in gel particles must also be precisely controlled. The higher volume fraction of argon gas in the furnace atmosphere, the thicker the wall of HGMs. Due to the limited operating range of furnace atmosphere pressure, changing furnace atmosphere pressure could not significantly increase the wall thickness of HGMs. Although increasing refin- ing temperature can improve the yield of high quality HGMs, a higher furnace atmosphere temperature may lead to a decrease in the wall thickness of HGMs. When the volume fraction of argon gas in the furnace atmosphere ranged from 80% to 95%, the furnace atmosphere pressure ranged from 1.0×l0^5 Pa to 1.25×105 Pa, and the refining temperature ranged from 1600℃ to 1800℃, we produced thick-walled （5-10 ktrn） HGMs with good sphericity, wall thickness uniformity and surface finish. However, the yield of high quality HGMs needs to be further improved. The compressive strength, tensile strength and permeation coefficient to deuterium gas of thick-walled HGMs at ambient temperature decreased with increase of the wall thickness.展开更多
基金supported by the National Basic Research Program of China (Grant Nos.2010CB631005 and 2011CB606105)the National Natural Science Foundation of China (Grant Nos.90916010 and 11172151)the Specialized Research Fund for the Doctoral Program of Higher Education (Grant No. 20090002110048)
文摘The fabrication technique of micro/nano-scale speckle patterns with focused ion beam (FIB) system is studied for digital image correlation (DIC) measurement under a scanning electron microscope (SEM).The speckle patterns are fabricated by directly etching the counterpart of the specimen to the black part of a template.Mean intensity gradient is used to evaluate the quality of these SEM images of speckle patterns fabricated based on different templates to select an optimum template.The pattern size depending on the displacement measurement sensitivity is adjusted by altering the magnification of FIB according to the relation curve of the etching size versus magnification.The influencing factors including etching time and ion beam current are discussed.Rigid body translation tests and rotation tests are carried out under SEM to verify the reliability of the fabricated speckle patterns.The calculated values are in good agreement with the imposed ones.
基金supported by the Chinese Key Laboratory of Science and Technology for Defense(Grant No.91400C680603090C68)
文摘To fabricate thick-walled hollow glass microspheres （HGMs） for inertial confinement fusion （ICF） targets by sol-gel technology, we investigated the effects of glass composition, blowing agent, refining temperature, pressure and composition of furnace atmosphere on the wall thickness of HGMs by numerical simulation and experiments. The results showed that the residence times of the thick-walled HGMs in the encapsulating and refining phases decreased with the increase of wall thickness of HGMs. As a response to this challenge, glass composition must be optimized with the object of high surface tension and low viscosity at refining temperature, and the blowing agents with high decomposition temperature should be used, furthermore the concentration of blowing agents in gel particles must also be precisely controlled. The higher volume fraction of argon gas in the furnace atmosphere, the thicker the wall of HGMs. Due to the limited operating range of furnace atmosphere pressure, changing furnace atmosphere pressure could not significantly increase the wall thickness of HGMs. Although increasing refin- ing temperature can improve the yield of high quality HGMs, a higher furnace atmosphere temperature may lead to a decrease in the wall thickness of HGMs. When the volume fraction of argon gas in the furnace atmosphere ranged from 80% to 95%, the furnace atmosphere pressure ranged from 1.0×l0^5 Pa to 1.25×105 Pa, and the refining temperature ranged from 1600℃ to 1800℃, we produced thick-walled （5-10 ktrn） HGMs with good sphericity, wall thickness uniformity and surface finish. However, the yield of high quality HGMs needs to be further improved. The compressive strength, tensile strength and permeation coefficient to deuterium gas of thick-walled HGMs at ambient temperature decreased with increase of the wall thickness.