A two-component waterborne polyurethane(2K-WPU) was prepared by mixing water-soluble acrylic resin and hexamethylene diisocyanate biuret, and then diluted for phase inversion with water. Compared with water-soluble ac...A two-component waterborne polyurethane(2K-WPU) was prepared by mixing water-soluble acrylic resin and hexamethylene diisocyanate biuret, and then diluted for phase inversion with water. Compared with water-soluble acrylic resin, the phase inversion of 2K-WPU occurs at lower water content. It is indicated by TEM that 2K-WPU parti-cles show a core-shell structure, in which HDI biuret is encapsulated by hydrophilic acrylic resin. 2K-WPU emulsion with HDI biuret has larger particle size and narrower distribution index, while for 2K-WPU emulsion with HDI iso-cyanurate, the latex not only has large particle size, but also has two-peak distribution. FTIR shows that the reaction be-tween HDI biuret and acrylic resin can complete in 12h. In addition, studies on effect of composition of acrylic resin on performance of 2K-WPU show that narrowing the polar difference between water-soluble acrylic resin and HDI biuret and improving the miscibility of two components are the key to prepare the transparent and high gloss films with high crosslinking density.展开更多
Two kinds of water-soluble and ultraviolet (UV) curable oligomers were synthesized and characterized. The oligomers were evaluated as resins for water-based UV curable coating. The rheology of the two oligomers' a...Two kinds of water-soluble and ultraviolet (UV) curable oligomers were synthesized and characterized. The oligomers were evaluated as resins for water-based UV curable coating. The rheology of the two oligomers' aqueous so-lutions was investigated in terms of solid fraction, pH dependence, and temperature dependence. The solutions were found to be Newtonian fluid showing rather low viscosity even at high solid fraction of 0.55. The drying process of the coatings and the properties of the cured coatings were studied by comparing them with water-dispersed UV-curable polyurethane methyl acrylate. It was evident that the water-soluble coating dried more slowly; and that the overall properties were inferior to those of the water-dispersed coating.展开更多
文摘A two-component waterborne polyurethane(2K-WPU) was prepared by mixing water-soluble acrylic resin and hexamethylene diisocyanate biuret, and then diluted for phase inversion with water. Compared with water-soluble acrylic resin, the phase inversion of 2K-WPU occurs at lower water content. It is indicated by TEM that 2K-WPU parti-cles show a core-shell structure, in which HDI biuret is encapsulated by hydrophilic acrylic resin. 2K-WPU emulsion with HDI biuret has larger particle size and narrower distribution index, while for 2K-WPU emulsion with HDI iso-cyanurate, the latex not only has large particle size, but also has two-peak distribution. FTIR shows that the reaction be-tween HDI biuret and acrylic resin can complete in 12h. In addition, studies on effect of composition of acrylic resin on performance of 2K-WPU show that narrowing the polar difference between water-soluble acrylic resin and HDI biuret and improving the miscibility of two components are the key to prepare the transparent and high gloss films with high crosslinking density.
文摘Two kinds of water-soluble and ultraviolet (UV) curable oligomers were synthesized and characterized. The oligomers were evaluated as resins for water-based UV curable coating. The rheology of the two oligomers' aqueous so-lutions was investigated in terms of solid fraction, pH dependence, and temperature dependence. The solutions were found to be Newtonian fluid showing rather low viscosity even at high solid fraction of 0.55. The drying process of the coatings and the properties of the cured coatings were studied by comparing them with water-dispersed UV-curable polyurethane methyl acrylate. It was evident that the water-soluble coating dried more slowly; and that the overall properties were inferior to those of the water-dispersed coating.
