用扫描电子显微镜对聚苯乙烯 b 聚丙烯酸 (PS b PAA)嵌段共聚物在水中自组装形貌进行了观察。结果表明 :外界环境和制样方法能够影响聚合物的自组装和聚集情况。 0℃时 ,PS38 b PAA2 10 胶束聚集形成纺锤状结构。而在临界条件下 ,缓慢...用扫描电子显微镜对聚苯乙烯 b 聚丙烯酸 (PS b PAA)嵌段共聚物在水中自组装形貌进行了观察。结果表明 :外界环境和制样方法能够影响聚合物的自组装和聚集情况。 0℃时 ,PS38 b PAA2 10 胶束聚集形成纺锤状结构。而在临界条件下 ,缓慢改变体系冷冻 解冻循环次数 ,则会得到这些纺锤结构的花状聚集体。展开更多
In this paper, the self-assembly of PS 43-b-PEO 45-b-PS 43 triblcok copolymer was investigated. The colloids were made by firstly dissolving the copolymer in the common solvents, including THF, 1,4-dioxane, and DMF, t...In this paper, the self-assembly of PS 43-b-PEO 45-b-PS 43 triblcok copolymer was investigated. The colloids were made by firstly dissolving the copolymer in the common solvents, including THF, 1,4-dioxane, and DMF, then droping water into the corresponding copolymer solution to induce the self-assembly. The aggregates prepared were characterized with TEM and AFM techniques. The experimental results demonstrated that the self-assembled vesicles were formed when THF and 1,4-dioxane were used as the common solvents to dissolve the copolymer, comparatively, using DMF as the common solvent resulted in the formation of spherical aggregates. The self-assembled aggregates observed, possessing hierarchical structures, could be used as either the nanostructures themselves for drug delivery systems, separations, catalysts, and so on, or templates or building blocks for more complex structures.展开更多
利用ATR单点全反射技术以及XPS(X光电子能谱 )测试方法对聚苯乙烯 聚二甲基硅氧烷嵌段 (PS b PDMS)和接枝共聚物 (PS g PDMS)进行了研究 ,发现聚合物膜表面存在着有机硅富集层 ,PS b PDMS有机硅表面富集程度要高于PS g PDMS ,而且不同...利用ATR单点全反射技术以及XPS(X光电子能谱 )测试方法对聚苯乙烯 聚二甲基硅氧烷嵌段 (PS b PDMS)和接枝共聚物 (PS g PDMS)进行了研究 ,发现聚合物膜表面存在着有机硅富集层 ,PS b PDMS有机硅表面富集程度要高于PS g PDMS ,而且不同溶解度参数的成膜溶剂和不同极性的成膜介质对有机硅富集程度有一定的影响 .展开更多
文摘In this paper, the self-assembly of PS 43-b-PEO 45-b-PS 43 triblcok copolymer was investigated. The colloids were made by firstly dissolving the copolymer in the common solvents, including THF, 1,4-dioxane, and DMF, then droping water into the corresponding copolymer solution to induce the self-assembly. The aggregates prepared were characterized with TEM and AFM techniques. The experimental results demonstrated that the self-assembled vesicles were formed when THF and 1,4-dioxane were used as the common solvents to dissolve the copolymer, comparatively, using DMF as the common solvent resulted in the formation of spherical aggregates. The self-assembled aggregates observed, possessing hierarchical structures, could be used as either the nanostructures themselves for drug delivery systems, separations, catalysts, and so on, or templates or building blocks for more complex structures.
文摘利用ATR单点全反射技术以及XPS(X光电子能谱 )测试方法对聚苯乙烯 聚二甲基硅氧烷嵌段 (PS b PDMS)和接枝共聚物 (PS g PDMS)进行了研究 ,发现聚合物膜表面存在着有机硅富集层 ,PS b PDMS有机硅表面富集程度要高于PS g PDMS ,而且不同溶解度参数的成膜溶剂和不同极性的成膜介质对有机硅富集程度有一定的影响 .