Well-cubic perovskite lanthanum aluminate (LaAlO3) film on (110) silicon substrate was fabricated by sol-gel method with corresponding inorganic salts. Lanthanum acetate and aluminum acetate glacial acetic acid solut...Well-cubic perovskite lanthanum aluminate (LaAlO3) film on (110) silicon substrate was fabricated by sol-gel method with corresponding inorganic salts. Lanthanum acetate and aluminum acetate glacial acetic acid solutions were prepared via ligand exchange starting from lanthanum nitrate hexahydrate and aluminum nitrate hexahydrate after being refluxed. (CH3CO)2O removed nitrates and the crystallized H2O completely, acetylacetone (AcAc) was partially bidentated with metallic ion of the metallic acetates and formed La(OAc)3 (AcAc)x, which were hydrolyzed into La(AcAc)3 (OH)x by ?x ?x adding 10 ml 0.4% methyl cellulose (MCL) solution. The La(AcAc)3 (OH)x, polymerizing and combining with MCL, ?x formed the LaAlO3 sol precursor with heteropolymeric structure and formed film easily. The epitaxial LaAlO3 film on Si(110) substrate was crystallized after being annealed in thermal annealing furnace for 650?750 °C/30 min. The mor- phologies and microstructures were characterized. The refractive index of the LAO film was 1.942 to 2.007; the dielectric constant and the dissipation factors were estimated to be 23?26 and 2.1×10?4 ? 2.4×10?4 respectively.展开更多
This article is intended to provide an overview of recent progress in the studies of cholesterol-based low-molecular mass gelators (LMMGs) with unusual properties,in particular,gelation and selective gelation at room ...This article is intended to provide an overview of recent progress in the studies of cholesterol-based low-molecular mass gelators (LMMGs) with unusual properties,in particular,gelation and selective gelation at room temperature,gel emulsions and gel film formation,etc.Potential applications of the LMMGs in spilled oil collection and water purification are briefly presented.展开更多
文摘Well-cubic perovskite lanthanum aluminate (LaAlO3) film on (110) silicon substrate was fabricated by sol-gel method with corresponding inorganic salts. Lanthanum acetate and aluminum acetate glacial acetic acid solutions were prepared via ligand exchange starting from lanthanum nitrate hexahydrate and aluminum nitrate hexahydrate after being refluxed. (CH3CO)2O removed nitrates and the crystallized H2O completely, acetylacetone (AcAc) was partially bidentated with metallic ion of the metallic acetates and formed La(OAc)3 (AcAc)x, which were hydrolyzed into La(AcAc)3 (OH)x by ?x ?x adding 10 ml 0.4% methyl cellulose (MCL) solution. The La(AcAc)3 (OH)x, polymerizing and combining with MCL, ?x formed the LaAlO3 sol precursor with heteropolymeric structure and formed film easily. The epitaxial LaAlO3 film on Si(110) substrate was crystallized after being annealed in thermal annealing furnace for 650?750 °C/30 min. The mor- phologies and microstructures were characterized. The refractive index of the LAO film was 1.942 to 2.007; the dielectric constant and the dissipation factors were estimated to be 23?26 and 2.1×10?4 ? 2.4×10?4 respectively.
基金supported by the National High-Tech Research & Devel-opment Program of China (863 Project) (2007AA03Z349)the National Natural Science Foundation of China (20902055,20927001,91027017)the 13115 Project of Shaanxi Province (2010ZDKG-89)
文摘This article is intended to provide an overview of recent progress in the studies of cholesterol-based low-molecular mass gelators (LMMGs) with unusual properties,in particular,gelation and selective gelation at room temperature,gel emulsions and gel film formation,etc.Potential applications of the LMMGs in spilled oil collection and water purification are briefly presented.