Based on analysis of thermo-hydro-mechanical-chemical(THMC)coupling mechanism for brittle rock,THMC coupling indicator in terms of rock porosity was introduced to represent the influencing degree of THMC coupling fiel...Based on analysis of thermo-hydro-mechanical-chemical(THMC)coupling mechanism for brittle rock,THMC coupling indicator in terms of rock porosity was introduced to represent the influencing degree of THMC coupling field on stress field in order to establish THMC coupling fracture criterion.A novel real-time measurement method of permeability(related to porosity)was proposed to determine the THMC coupling indicator,and self-designed THMC coupling tests and scanning electron microscope tests were conducted on pre-cracked red sandstone specimens to study the macroscopic and microscopic fracture mechanism.Research results show that the higher the hydraulic pressure is,the smaller the crack initiation load is and the easier the Mode I fracture occurs.Test results are in good agreement with prediction results(crack initiation load and angle,and fracture mode),which can verify the effectiveness of the newly established THMC coupling fracture criterion.This new fracture criterion can be also further extended to predict THMC coupling fracture of multi-crack problem.展开更多
The prediction of dynamic crack propagation in brittle materials is still an important issue in many engineering fields. The remeshing technique based on scaled boundary finite element method(SBFEM) is extended to pre...The prediction of dynamic crack propagation in brittle materials is still an important issue in many engineering fields. The remeshing technique based on scaled boundary finite element method(SBFEM) is extended to predict the dynamic crack propagation in brittle materials. The structure is firstly divided into a number of superelements, only the boundaries of which need to be discretized with line elements. In the SBFEM formulation, the stiffness and mass matrices of the super-elements can be coupled seamlessly with standard finite elements, thus the advantages of versatility and flexibility of the FEM are well maintained. The transient response of the structure can be calculated directly in the time domain using a standard time-integration scheme. Then the dynamic stress intensity factor(DSIF) during crack propagation can be solved analytically due to the semi-analytical nature of SBFEM. Only the fine mesh discretization for the crack-tip super-element is needed to ensure the required accuracy for the determination of stress intensity factor(SIF). According to the predicted crack-tip position, a simple remeshing algorithm with the minimum mesh changes is suggested to simulate the dynamic crack propagation. Numerical examples indicate that the proposed method can be effectively used to deal with the dynamic crack propagation in a finite sized rectangular plate including a central crack. Comparison is made with the results available in the literature, which shows good agreement between each other.展开更多
Thermally activated dislocation emission in high-temperature ferroelectric ceramics is investigated through an assumption of thermal stability and a novel analytical method. The stress intensity factor (SIF) arising f...Thermally activated dislocation emission in high-temperature ferroelectric ceramics is investigated through an assumption of thermal stability and a novel analytical method. The stress intensity factor (SIF) arising from domain switching is evaluated by using a Green's function method, and the critical applied electric field intensity factor (CAEFIF) for brittle fracture at room temperature is obtained. Besides, the lowest temperature for single dislocation emission before brittle fracture is also obtained by constructing an energy balance. The multi-scale analysis of facture toughness of the ferroelectric ceramics at high temperature is carried out. Through the analysis, the CAEFIF for crack extension is recalculated. The results show that the competition and interaction effects between dislocation emission and brittle fracture are very obvious. Besides, the higher critical activation temperature, the more columns of obstacles will be overcome. Additionally, the shielding effect arising from thermally activated dislocations is remarkable, thus, the brittle-ductile transition can promote the fracture toughness of high-temperature ferroelectric ceramics.展开更多
基金The authors are grateful for the financial supports from the National Natural Science Foundation of China(Nos.51474251,51874351)the Excellent Postdoctoral Innovative Talents Project of Hunan Province,China(No.2020RC2001).
文摘Based on analysis of thermo-hydro-mechanical-chemical(THMC)coupling mechanism for brittle rock,THMC coupling indicator in terms of rock porosity was introduced to represent the influencing degree of THMC coupling field on stress field in order to establish THMC coupling fracture criterion.A novel real-time measurement method of permeability(related to porosity)was proposed to determine the THMC coupling indicator,and self-designed THMC coupling tests and scanning electron microscope tests were conducted on pre-cracked red sandstone specimens to study the macroscopic and microscopic fracture mechanism.Research results show that the higher the hydraulic pressure is,the smaller the crack initiation load is and the easier the Mode I fracture occurs.Test results are in good agreement with prediction results(crack initiation load and angle,and fracture mode),which can verify the effectiveness of the newly established THMC coupling fracture criterion.This new fracture criterion can be also further extended to predict THMC coupling fracture of multi-crack problem.
基金Supported by the Key Program of National Natural Science Foundation of China(No.51138001)the Science Fund for Creative Research Groups of National Natural Science Foundation of China(No.51121005)+2 种基金the Fundamental Research Funds for the Central Universities(DUT13LK16)the Young Scientists Fund of National Natural Science Foundation of China(No.51109134)China Postdoctoral Science Foundation(No.2011M500814)
文摘The prediction of dynamic crack propagation in brittle materials is still an important issue in many engineering fields. The remeshing technique based on scaled boundary finite element method(SBFEM) is extended to predict the dynamic crack propagation in brittle materials. The structure is firstly divided into a number of superelements, only the boundaries of which need to be discretized with line elements. In the SBFEM formulation, the stiffness and mass matrices of the super-elements can be coupled seamlessly with standard finite elements, thus the advantages of versatility and flexibility of the FEM are well maintained. The transient response of the structure can be calculated directly in the time domain using a standard time-integration scheme. Then the dynamic stress intensity factor(DSIF) during crack propagation can be solved analytically due to the semi-analytical nature of SBFEM. Only the fine mesh discretization for the crack-tip super-element is needed to ensure the required accuracy for the determination of stress intensity factor(SIF). According to the predicted crack-tip position, a simple remeshing algorithm with the minimum mesh changes is suggested to simulate the dynamic crack propagation. Numerical examples indicate that the proposed method can be effectively used to deal with the dynamic crack propagation in a finite sized rectangular plate including a central crack. Comparison is made with the results available in the literature, which shows good agreement between each other.
基金Supported by the Ph.D. Programs Foundation of Ministry of Education of China under Grant No. 20123305120008, the Scientific Research Project of Department of Education of Zhejiang Province under Grant No. Y201223508, a Grant from the Impact and Safety of Coastal Engineering Initiative, a COE Program of Zhejiang Provincial Government at Ningbo University under Grant Nos. zj1117, zj1203, and zj1201 and the K.C. Wong Magana Fund
文摘Thermally activated dislocation emission in high-temperature ferroelectric ceramics is investigated through an assumption of thermal stability and a novel analytical method. The stress intensity factor (SIF) arising from domain switching is evaluated by using a Green's function method, and the critical applied electric field intensity factor (CAEFIF) for brittle fracture at room temperature is obtained. Besides, the lowest temperature for single dislocation emission before brittle fracture is also obtained by constructing an energy balance. The multi-scale analysis of facture toughness of the ferroelectric ceramics at high temperature is carried out. Through the analysis, the CAEFIF for crack extension is recalculated. The results show that the competition and interaction effects between dislocation emission and brittle fracture are very obvious. Besides, the higher critical activation temperature, the more columns of obstacles will be overcome. Additionally, the shielding effect arising from thermally activated dislocations is remarkable, thus, the brittle-ductile transition can promote the fracture toughness of high-temperature ferroelectric ceramics.