The effect of current on the morphology of Al alloy T-joint in double-pulsed metal inert gas（DP-MIG） welding process was investigated by simulation and experiment.A three-dimensional finite element model and the DP-...The effect of current on the morphology of Al alloy T-joint in double-pulsed metal inert gas（DP-MIG） welding process was investigated by simulation and experiment.A three-dimensional finite element model and the DP-MIG heat source of double-ellipsoidal volumetric model were developed to simulate the temperature and stress fields under different welding conditions.The macro-morphology and microstructure of welding joints at the corresponding currents were observed in the experiment.The results show that the best condition is at an average current of 90 A and current difference of 40 A,when the maximum temperature is 200 °C higher than the fusion points,with the temperature difference of about 100 °C and stress change of 10 MPa between thermal pulse and thermal base.Under these conditions,Al alloy T-joint with proper fusion condition has smooth fish-scale welding appearance and finer microstructure.Furthermore,the thermal curves and stress distribution in the experiment are consistent with those in the simulation,verifying the precision of the welding simulation.展开更多
Direct current pulsed metal inert-gas （DC-PMIG） welding was carried out on AZ31B magnesium alloy to obtain continuous welding joints of 3 mm and 8 mm thickness with 1.6 mm diameter of filler wire. The behavior and m...Direct current pulsed metal inert-gas （DC-PMIG） welding was carried out on AZ31B magnesium alloy to obtain continuous welding joints of 3 mm and 8 mm thickness with 1.6 mm diameter of filler wire. The behavior and mechanism of metal transfer, the parameter ranges of stable welding process, the microstructure and mechanical properties of magnesium alloy were investigated. The results show that the metal transfer form of magnesium alloy using DC-PMIG welding is realized in modes of globular transfer, projected transfer and spray transfer. Welding spatter with a large size will be produced in the mode of globular transfer, and high-quality joints with few spatters can be obtained in the mode of projected transfer and spray transfer when the linear energy of filler wire is 242-27l J/cm, droplet diameter is 1.6-0.9 mm tensile strength of weld beads is 94.2% of that of base metals. and transition frequency is 30-69 Hz. The average ultimate展开更多
Four different welding sequences of double-pulse MIG welding were conducted for 6061-T6 aluminum alloy automobile bumpers by using nonlinear elastoplasticity finite element method based on ABAQUS software.The post-wel...Four different welding sequences of double-pulse MIG welding were conducted for 6061-T6 aluminum alloy automobile bumpers by using nonlinear elastoplasticity finite element method based on ABAQUS software.The post-welding residual stress and deformation were definitely different among the four welding sequences.The results showed that the highest temperature in Solution A was approximately 200℃higher than the melting point of base metal.High residual stress was resulted from this large temperature gradient and mainly concentrated on the welding vicinity between beam and crash box.The welding deformation primarily occurred in both of the contraction of two-ends of the beam and the self-contraction of crash box.Compared with other welding sequences,the residual stress in Solution A was the smallest,whereas the welding deformation was the largest.However,the optimal sequence was Solution B because of the effective reduction of residual stress and good assembly requirements.展开更多
基金Project(51475156)supported by the National Natural Science Foundation of China
文摘The effect of current on the morphology of Al alloy T-joint in double-pulsed metal inert gas（DP-MIG） welding process was investigated by simulation and experiment.A three-dimensional finite element model and the DP-MIG heat source of double-ellipsoidal volumetric model were developed to simulate the temperature and stress fields under different welding conditions.The macro-morphology and microstructure of welding joints at the corresponding currents were observed in the experiment.The results show that the best condition is at an average current of 90 A and current difference of 40 A,when the maximum temperature is 200 °C higher than the fusion points,with the temperature difference of about 100 °C and stress change of 10 MPa between thermal pulse and thermal base.Under these conditions,Al alloy T-joint with proper fusion condition has smooth fish-scale welding appearance and finer microstructure.Furthermore,the thermal curves and stress distribution in the experiment are consistent with those in the simulation,verifying the precision of the welding simulation.
基金Project (IRT1008) supported by Changjiang Scholars and Innovative Research Team in University, ChinaProject (51005035) supported by the National Natural Science Foundation of ChinaProject (51025520) supported by the National Natural Science Funds for Distinguished Young Scholar, China
文摘Direct current pulsed metal inert-gas （DC-PMIG） welding was carried out on AZ31B magnesium alloy to obtain continuous welding joints of 3 mm and 8 mm thickness with 1.6 mm diameter of filler wire. The behavior and mechanism of metal transfer, the parameter ranges of stable welding process, the microstructure and mechanical properties of magnesium alloy were investigated. The results show that the metal transfer form of magnesium alloy using DC-PMIG welding is realized in modes of globular transfer, projected transfer and spray transfer. Welding spatter with a large size will be produced in the mode of globular transfer, and high-quality joints with few spatters can be obtained in the mode of projected transfer and spray transfer when the linear energy of filler wire is 242-27l J/cm, droplet diameter is 1.6-0.9 mm tensile strength of weld beads is 94.2% of that of base metals. and transition frequency is 30-69 Hz. The average ultimate
基金Projects(31665004,31715011) supported by the Open Fund of State Key Laboratory of Advanced Design and Manufacture for Vehicle Body,Hunan University,ChinaProject(15C0450) supported by the Educational Commission of Hunan Province of China
文摘Four different welding sequences of double-pulse MIG welding were conducted for 6061-T6 aluminum alloy automobile bumpers by using nonlinear elastoplasticity finite element method based on ABAQUS software.The post-welding residual stress and deformation were definitely different among the four welding sequences.The results showed that the highest temperature in Solution A was approximately 200℃higher than the melting point of base metal.High residual stress was resulted from this large temperature gradient and mainly concentrated on the welding vicinity between beam and crash box.The welding deformation primarily occurred in both of the contraction of two-ends of the beam and the self-contraction of crash box.Compared with other welding sequences,the residual stress in Solution A was the smallest,whereas the welding deformation was the largest.However,the optimal sequence was Solution B because of the effective reduction of residual stress and good assembly requirements.