The function mechanism of Sb（V） in As, Sb and Bi impurities removal from copper electrolyte was investigated by adding Sb（V） ion in a synthetic copper electrolyte containing 45 g/L Cu2＋, 185 g/L H2SO4, 10 g/L As ...The function mechanism of Sb（V） in As, Sb and Bi impurities removal from copper electrolyte was investigated by adding Sb（V） ion in a synthetic copper electrolyte containing 45 g/L Cu2＋, 185 g/L H2SO4, 10 g/L As and 0.5 g/L Bi. The electrolyte was filtered, and the precipitate structure, morphology and composition were characterized by chemical analysis, SEM, TEM, EDS, XRD and FTIR. The results show that the precipitate is in the shape of many irregular lumps with size of 50-200 μm, and it mainly consists of As, Sb, Bi and O elements. The main characteristic bands in the FTIR spectra of the precipitate are As-O-As, As-O-Sb, Sb-O-Bi, Sb-O-Sb and Bi-O-Bi. The precipitate is the mixture of microcrystalline of AsSbO4, BiSbO4 and Bi3SbO7 by XRD and electronic diffraction. The removal of As, Sb and Bi impurities by Sb（V） ion can be mainly ascribed to the formation of antimonate in copper electrolytes.展开更多
Direct phase transformation of flue gas desulfurization gypsum in hot salt solution at atmospheric pres-sure was investigated.The effects of temperature,salt species,salt concentration,solids content,pH and modifier w...Direct phase transformation of flue gas desulfurization gypsum in hot salt solution at atmospheric pres-sure was investigated.The effects of temperature,salt species,salt concentration,solids content,pH and modifier were examined.The crystals obtained under different conditions and solubility of calcium sulfate in contact with solid gypsum were also determined.α-Calcium sulfate hemihydrate crystals of stubby columnar shape and regular pentahedral sides were obtained under the following conditions：salt concentration 20%-30%,operation tempera-ture 95-100 °C,solids mass content in the slurry 10%-30% and neutral pH.Thermodynamic analysis revealed that phase transformation of calcium sulfate dihydrate to α-calcium sulfate hemihydrate occurs because of the difference in solubilities between the two solid gypsum phases in this system.展开更多
基金Project(50904023)supported by the National Natural Science Foundation of ChinaProject(2010B450001)supported by the Natural Science Fund of Department of Education of Henan Province,ChinaProject(092300410064)supported by the Basic and Frontier Technologies Research Projects of Henan Province,China
文摘The function mechanism of Sb（V） in As, Sb and Bi impurities removal from copper electrolyte was investigated by adding Sb（V） ion in a synthetic copper electrolyte containing 45 g/L Cu2＋, 185 g/L H2SO4, 10 g/L As and 0.5 g/L Bi. The electrolyte was filtered, and the precipitate structure, morphology and composition were characterized by chemical analysis, SEM, TEM, EDS, XRD and FTIR. The results show that the precipitate is in the shape of many irregular lumps with size of 50-200 μm, and it mainly consists of As, Sb, Bi and O elements. The main characteristic bands in the FTIR spectra of the precipitate are As-O-As, As-O-Sb, Sb-O-Bi, Sb-O-Sb and Bi-O-Bi. The precipitate is the mixture of microcrystalline of AsSbO4, BiSbO4 and Bi3SbO7 by XRD and electronic diffraction. The removal of As, Sb and Bi impurities by Sb（V） ion can be mainly ascribed to the formation of antimonate in copper electrolytes.
基金Supported by the National High Technology Research and Development Program of China（2006AA06Z385） the Science Foundation of Wuhan University of Science and Technology（2008RC06）
文摘Direct phase transformation of flue gas desulfurization gypsum in hot salt solution at atmospheric pres-sure was investigated.The effects of temperature,salt species,salt concentration,solids content,pH and modifier were examined.The crystals obtained under different conditions and solubility of calcium sulfate in contact with solid gypsum were also determined.α-Calcium sulfate hemihydrate crystals of stubby columnar shape and regular pentahedral sides were obtained under the following conditions：salt concentration 20%-30%,operation tempera-ture 95-100 °C,solids mass content in the slurry 10%-30% and neutral pH.Thermodynamic analysis revealed that phase transformation of calcium sulfate dihydrate to α-calcium sulfate hemihydrate occurs because of the difference in solubilities between the two solid gypsum phases in this system.