Effects of titanium addition on structural, mechanical, tribological, and corrosion properties of Al-25Zn-3Cu and Al-25Zn-3Cu-3Si alloys

To investigate the effect of grain refinement on the material properties of recently developed Al-25 Zn-3 Cu based alloys,Al-25 Zn-3 Cu,Al-25 Zn-3 Cu-0.01 Ti,Al-25 Zn-3 Cu-3 Si and Al-25 Zn-3 Cu-3 Si-0.01 Ti alloys were produced by permanent mold casting method.Microstructures of the alloys were examined by SEM.Hardness and mechanical properties of the alloys were determined by Brinell method and tensile tests,respectively.Tribological characteristics of the alloys were investigated by a ball-on-disc type test machine.Corrosion properties of the alloys were examined by an electrochemical corrosion experimental setup.It was observed that microstructure of the ternary A1-25 Zn-3 Cu alloy consisted ofα,α+ηandθ(Al2Cu)phases.It was also observed that the addition of 3 wt.%Si to A1-25Zn-3Cu alloy resulted in the formation of silicon particles in its microstructure.The addition of 0.01 wt.%Ti to the Al-25Zn-3Cu and Al-25 Zn-3 Cu-3 Si alloys caused a decrement in grain size by approximately 20%and 39%and an increment in hardness from HRB 130 to 137 and from HRB 141 to 156,respectively.Yield strengths of these alloys increased from 278 to 297 MPa and from 320 to 336 MPa while their tensile strengths increased from 317 to 340 MPa and from 334 to 352 MPa.Wear resistance of the alloys increased,but corrosion resistance decreased with titanium addition.

Role of Ag addition on microstructure,mechanical properties,corrosion behavior and biocompatibility of porous Ti-30 at%Ta shape memory alloys

In the present study,the thermal,mechanical,and biological properties of xAg/Ti-30Ta(x=0,0.41,0.82 and 2.48 at%)shape memory alloys(SMAs)were investigated.The study was conducted using optical and scanning electron microscopy(SEM),X-ray diffractometry(XRD),compression test,and shape memory testing.The xAg/Ti-Ta was made using a powder metallurgy technique and microwave-sintering process.The results revealed that the addition of Ag has a significant effect on the pore size and shape,whereas the smallest pore size of 11μm was found with the addition of 0.41 at%along with a relative density of 72%.The fracture stress and strain increased with the addition of Ag,reaching the minimum values around 0.41 at%Ag.Therefore,this composition showed the maximum stress and strain at fracture region.Moreover,0.82 Ag/Ti-Ta shows more excellent corrosion resistance and biocompatibility than other percentages,obtaining almost the same behaviour of the pure Ti and Ti-6Al-4V alloys,which can be recommended for their promising and potential response for biomaterial applications.

我国不同区域水源水拉森指数比较分析

目前远距离调水已经成为解决区域水资源不足的一项重要措施。但在水源切换时,切换前后水源水的腐蚀性如果存在显著差异,可能会因腐蚀加剧而出现"黄水"或"红水"现象。因此,了解不同区域、不同类型水源的腐蚀性差异,对于科学合理地进行水资源调配具有重要意义。拉森指数(LR)是目前评价水质对铁质管网腐蚀程度的常用方法。本研究以14个城市的26个水源水为研究对象,对模拟常规工艺处理后的滤后水进行了水质分析,并计算出其拉森指数。结果表明,相对于湖库水和地下水,河流水的拉森指数偏高,有44%的河流水拉森指数大于1,具有较强的腐蚀倾向。按区域分华东和中南地区、按流域分黄河和珠江流域的水源水拉森指数平均值大于1,水源切换条件下应关注其腐蚀性情况。