The corrosion under insulation dominates metal loss in the case of API （American Petroleum Institute） 5L Grade B geothermal pipeline, whereas, the other possible corrosion causes, such as stress corrosion and therma...The corrosion under insulation dominates metal loss in the case of API （American Petroleum Institute） 5L Grade B geothermal pipeline, whereas, the other possible corrosion causes, such as stress corrosion and thermal cracking, did not serve a role as critical factors regarding to pipeline degradation during 26-years working operation. Actually, the header pipe diameter 32 inches and 40 inches require priority for inspection due to higher corrosion rate compared to smaller pipe diameters. By simulation method on similar heavy duty service condition in which the working pressure of 15 bars and temperature of 183 ℃, it was proved that corrosion rate will severely occur at corrosion rate more than 10 mpy in the pipe diameters of 20 inches, 32 inches and 40 inches. Further,condensation factor may contribute more significant in the case of corrosion under insulation. Practically, the metal loss at a half initial thickness requires priority for inspection, intensive maintenance or possible partial replacement.展开更多
文摘The corrosion under insulation dominates metal loss in the case of API （American Petroleum Institute） 5L Grade B geothermal pipeline, whereas, the other possible corrosion causes, such as stress corrosion and thermal cracking, did not serve a role as critical factors regarding to pipeline degradation during 26-years working operation. Actually, the header pipe diameter 32 inches and 40 inches require priority for inspection due to higher corrosion rate compared to smaller pipe diameters. By simulation method on similar heavy duty service condition in which the working pressure of 15 bars and temperature of 183 ℃, it was proved that corrosion rate will severely occur at corrosion rate more than 10 mpy in the pipe diameters of 20 inches, 32 inches and 40 inches. Further,condensation factor may contribute more significant in the case of corrosion under insulation. Practically, the metal loss at a half initial thickness requires priority for inspection, intensive maintenance or possible partial replacement.