Hybrid materials were prepared using a silane coupling agent, tetraethoxysilane （ TEOS ） as the precursor, dilute hydrochloric acid as the catalyst, and epoxy as the matrices. The films coated with hybrid materials ...Hybrid materials were prepared using a silane coupling agent, tetraethoxysilane （ TEOS ） as the precursor, dilute hydrochloric acid as the catalyst, and epoxy as the matrices. The films coated with hybrid materials were expected to improve abrasion resistance and mechanical properties. The morphology, mechanical properties, adhesion, and abrasion resistance of the polyethylene terephthalate （PET） films were characterized using an atomic force microscope, a tensile testing machine, a bagger knife, and a reciprocating fabric abrasion tester. The result of research indicated that the modification significantly affected the abrasion resistance and roughness. The-tensile strength and abrasion resistance of the modified PET films increased by 40% and 50% respectively at 3 % TEOS mass fraction.展开更多
基金Scientific Research Foundation for the Returned Overseas Chinese Scholars,Ministry of Education of China(No.2005-383)
文摘Hybrid materials were prepared using a silane coupling agent, tetraethoxysilane （ TEOS ） as the precursor, dilute hydrochloric acid as the catalyst, and epoxy as the matrices. The films coated with hybrid materials were expected to improve abrasion resistance and mechanical properties. The morphology, mechanical properties, adhesion, and abrasion resistance of the polyethylene terephthalate （PET） films were characterized using an atomic force microscope, a tensile testing machine, a bagger knife, and a reciprocating fabric abrasion tester. The result of research indicated that the modification significantly affected the abrasion resistance and roughness. The-tensile strength and abrasion resistance of the modified PET films increased by 40% and 50% respectively at 3 % TEOS mass fraction.