The morphology changes of both Fe-containing intermetallic compounds and the primary Si phase of Al-20Si-2Fe- 2Cu-0.4Mg-1.0Ni-0.5Mn （mass fraction, %） alloy produced by semi-solid rheo-diecasting were studied. The s...The morphology changes of both Fe-containing intermetallic compounds and the primary Si phase of Al-20Si-2Fe- 2Cu-0.4Mg-1.0Ni-0.5Mn （mass fraction, %） alloy produced by semi-solid rheo-diecasting were studied. The semi-solid slurry of high silicon aluminum alloy was prepared by direct ultrasonic vibration （DUV） which was imposed on the alloy near the liquidus temperature for about 2 rain. Then, standard test samples of 6.4 mm in diameter were formed by semi-solid rheo-diecasting. The results show that the DUV treatment suppresses the formation of needle-like ,β-Al5（Fe,Mn）Si phase, and the Fe-containing intermetallic compounds exist in the form of fine Al4（Fe, Mn）Si2 particles. Additionally, the primary Si grows up as fine and round particles with uniform distribution in α（Al） matrix of this alloy under DUV treatment. The tensile strengths of the samples at the room temperature and 573 K are 230 MPa and 145 MPa, respectively. The coefficient of thermal expansion （CTE） between 25 ℃ and 300 ℃ is 16.052 8×10^-6 ℃^-1, and the wear rate is 1.55%. The hardness of this alloy with 2% Fe reaches HB146.3. It is discovered that modified morphology and uniform distribution of the Fe-containing intermetallic compounds and the primary Si phase are the main reasons for reducing the CTE and increasing the wear resistance of this alloy.展开更多
The dynamic transformations of conformations and aromatic properties of [32]octaphyrins（1.0.1.0.1.0.1.0） through rotating the pyrrolic ring of the macrocycles are demonstrated by theoretical simulations in CH2Cl2 so...The dynamic transformations of conformations and aromatic properties of [32]octaphyrins（1.0.1.0.1.0.1.0） through rotating the pyrrolic ring of the macrocycles are demonstrated by theoretical simulations in CH2Cl2 solution. Facile multistep isomeriza- tions involving antiaromatic-Htickel and aromatic-Mobius topologies were also predicted by density functional theory （DFT）. The understanding of changes in topologies and aromaticities of free-base expanded porphrins may provide useful information to build new macrocycles with unique properties.展开更多
基金Project(2007AA03Z557) supported by the National High-tech Research and Development Program of ChinaProject(50775086) supported by the National Natural Science Foundation of China
文摘The morphology changes of both Fe-containing intermetallic compounds and the primary Si phase of Al-20Si-2Fe- 2Cu-0.4Mg-1.0Ni-0.5Mn （mass fraction, %） alloy produced by semi-solid rheo-diecasting were studied. The semi-solid slurry of high silicon aluminum alloy was prepared by direct ultrasonic vibration （DUV） which was imposed on the alloy near the liquidus temperature for about 2 rain. Then, standard test samples of 6.4 mm in diameter were formed by semi-solid rheo-diecasting. The results show that the DUV treatment suppresses the formation of needle-like ,β-Al5（Fe,Mn）Si phase, and the Fe-containing intermetallic compounds exist in the form of fine Al4（Fe, Mn）Si2 particles. Additionally, the primary Si grows up as fine and round particles with uniform distribution in α（Al） matrix of this alloy under DUV treatment. The tensile strengths of the samples at the room temperature and 573 K are 230 MPa and 145 MPa, respectively. The coefficient of thermal expansion （CTE） between 25 ℃ and 300 ℃ is 16.052 8×10^-6 ℃^-1, and the wear rate is 1.55%. The hardness of this alloy with 2% Fe reaches HB146.3. It is discovered that modified morphology and uniform distribution of the Fe-containing intermetallic compounds and the primary Si phase are the main reasons for reducing the CTE and increasing the wear resistance of this alloy.
基金supported by the National Basic Research Program of China(2011CB808600)the National Natural Science Foundation of China(21273102)
文摘The dynamic transformations of conformations and aromatic properties of [32]octaphyrins（1.0.1.0.1.0.1.0） through rotating the pyrrolic ring of the macrocycles are demonstrated by theoretical simulations in CH2Cl2 solution. Facile multistep isomeriza- tions involving antiaromatic-Htickel and aromatic-Mobius topologies were also predicted by density functional theory （DFT）. The understanding of changes in topologies and aromaticities of free-base expanded porphrins may provide useful information to build new macrocycles with unique properties.