A modified cellular automaton(CA) program was developed to simulate the process of dynamic recrystallization(DRX) for 23Co13Ni11Cr3Mo ultrahigh strength steel.In this model,influences of deformation parameters on hard...A modified cellular automaton(CA) program was developed to simulate the process of dynamic recrystallization(DRX) for 23Co13Ni11Cr3Mo ultrahigh strength steel.In this model,influences of deformation parameters on hardening rate and solute drag effect were considered.Moreover,an inverse analysis method was proposed for parameters identification of dislocation model and solute drag effect based on the results of isothermal compression tests on Gleeble-1500.Then,simulated microstructures under different deformation conditions were compared with those of experiments.A good agreement is achieved.Furthermore,influences of deformation parameters on microstructure evolution for 23Co13Ni11Cr3Mo steel were investigated in details.High strain is an effective measure to refine grain and improve homogeneity.Meanwhile,the desired deformation parameters are temperature of 1000-1050 °C and strain rate of 0.008-0.01 s-1 for obtaining grains smaller than 22.5 μm.展开更多
The dynamic recrystallization(DRX) process of hot compressed aluminium alloy 7050 was predicted using cellular automaton(CA) combined with topology deformation. The hot deformatation characteristics of aluminium alloy...The dynamic recrystallization(DRX) process of hot compressed aluminium alloy 7050 was predicted using cellular automaton(CA) combined with topology deformation. The hot deformatation characteristics of aluminium alloy 7050 were investigated by hot uniaxial compression tests in order to obtain the material parameters used in the CA model. The influences of process parameters(strain, strain rate and temperature) on the fraction of DRX and the average recrystallization grain(R-grain) size were investigated and discussed. It is found that larger stain, higher temperature and lower strain rate(less than 0.1 s^(–1)) are beneficial to the increasing fraction of DRX. And the deformation temperature affects the mean R-grain size much more greatly than other parameters. It is also noted that there is a critical strain for the occurrence of DRX which is related to strain rate and temperature. In addition, it is shown that the CA model with topology deformation is able to simulate the microstructural evolution and the flow behavior of aluminium alloy 7050 material under various deformation conditions.展开更多
基金Project(2011CB706802)supported by the National Basic Research Program of ChinaProject(2012ZX04010-081)supported by National Science and Technology Major Program of China
文摘A modified cellular automaton(CA) program was developed to simulate the process of dynamic recrystallization(DRX) for 23Co13Ni11Cr3Mo ultrahigh strength steel.In this model,influences of deformation parameters on hardening rate and solute drag effect were considered.Moreover,an inverse analysis method was proposed for parameters identification of dislocation model and solute drag effect based on the results of isothermal compression tests on Gleeble-1500.Then,simulated microstructures under different deformation conditions were compared with those of experiments.A good agreement is achieved.Furthermore,influences of deformation parameters on microstructure evolution for 23Co13Ni11Cr3Mo steel were investigated in details.High strain is an effective measure to refine grain and improve homogeneity.Meanwhile,the desired deformation parameters are temperature of 1000-1050 °C and strain rate of 0.008-0.01 s-1 for obtaining grains smaller than 22.5 μm.
基金Project(2012ZX04010-8)supported by National Key Technology R&D Program of China
文摘The dynamic recrystallization(DRX) process of hot compressed aluminium alloy 7050 was predicted using cellular automaton(CA) combined with topology deformation. The hot deformatation characteristics of aluminium alloy 7050 were investigated by hot uniaxial compression tests in order to obtain the material parameters used in the CA model. The influences of process parameters(strain, strain rate and temperature) on the fraction of DRX and the average recrystallization grain(R-grain) size were investigated and discussed. It is found that larger stain, higher temperature and lower strain rate(less than 0.1 s^(–1)) are beneficial to the increasing fraction of DRX. And the deformation temperature affects the mean R-grain size much more greatly than other parameters. It is also noted that there is a critical strain for the occurrence of DRX which is related to strain rate and temperature. In addition, it is shown that the CA model with topology deformation is able to simulate the microstructural evolution and the flow behavior of aluminium alloy 7050 material under various deformation conditions.